Rantai Kepala molekuler: | Urethane Based Polymer |
---|---|
Warna: | Putih |
formulir: | partikel oval |
kekerasan,pantai a: | 72-95 |
kerapatan,g/cm3: | 1.19-1.20 |
100% modulus,mpa: | 3-11 |
Pemasok dengan izin usaha terverifikasi
Properti | Standar | Satuan | P72 | P82 | P86 | P92 | P95 | |
Kerapatan | ASTM D792 | g/cm3 | 1.19 | 1.19 | 1.19 | 1.19 | 1.20 | |
Kekerasan | ASTM D2240 | A/D Shore | 72/- | 82/- | 86/- | 92/- | 95/- | |
Kekuatan tensil | ASTM D412 | MPa | / | / | / | / | / | |
100% Modulus | ASTM D412 | MPa | / | / | / | / | / | |
300% Modulus | ASTM D412 | MPa | / | / | / | / | / | |
Naskh dalam Pronh | ASTM D412 | % | / | / | / | / | / | |
Kekuatan robek | ASTM D624 | KN/m | / | / | / | / | / | |
Kehilangan Abrasi DIN | DIN 53516 | mm3 | / | / | / | / | / | |
TG | DSC | / | / | / | / | / | ||
Kompresi Setel | 22 jam@70 | ASTM D395 | % | / | / | / | / | / |
24 jam@100 | ASTM D395 | % | / | / | / | / | / |