CAS No.: | 9002-86-2 |
---|---|
Formula: | C2h3cl |
Material: | Polyvinyl Chloride/PVC |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Extrusion |
Pemasok dengan izin usaha terverifikasi
Tidak. | Item inspeksi | Permintaan standar | Metode pengujian | Nilai umum | |
Technical | |||||
1 | Kerapatan g/cm3 | / | GB 1033 | 1.45 | |
2 | MPa kekuatan tensil | ≥16.0 | GB 1040 | 18 | |
3 | Naskh dalam waktu istirahat % | ≥150 | GB 1040 | 230 | |
4 | Penukar bentuk panas (penukar ASCII ASCII)% | ≤40 | GB8815 | 20 | |
5 | Temperatur rendah Uji suhu 25 derajat |
Gagal No.≤15/30 | GB5470 | Lulus | |
6 | 200 menit stabilitas termal statis | ≥60 | GB8815 | 70 | |
7 | Resistivitas volume di 20Ω .m | ≥1 dan 4 poin 1012 | GB/T 1410 | 3.2 x 1012 | |
8 | Kekuatan dielektrik MV/m. | ≥20 | GB/T1408. 1 | 23 | |
9 |
Properti termal tua | 100±2 , 168h | |||
MPa kekuatan tensil | ≥16.0 | GB1040 |
Lulus | ||
Variasi Maks pada kekuatan tensil % | ±20 | ||||
Naskh dalam waktu rehat % | ≥150 | ||||
Variasi Maks dalam lonutan % demi istirahat | ±20 | ||||
10 | Thermal sudah berkurang kualitasnya | 100±2 | GB/T2951 | ||
h | 168 |
Kehilangan kualitas g/m2 | ≤20 | 15 | |||
Kualitas penampilan | |||||
1 | Tampilan | Garis-garis ekstrusi halus |
Survei mata | ||
2 |
Warna | Nuansa warna konsisten | Survei mata | ||
Simpangan baku ≤1.5 | Colorimeter | ||||
*Catatan: 1 saluran ekstrusi mulus, dan tidak lebih dari 3 titik mengambang dengan diameter ≥1,1.0mm diperbolehkan dalam jarak 1 meter.tidak ada partikel ≥ 3,0mm. 2 semua produk akan menjalani pemeriksaan awal ketika startup, termasuk tampilan, warna, densitas, dll. 3 Jika sampel pertama gagal, tes ulang diperlukan, dan hasil tes kedua adalah standar penilaian. |
Zona | Zona 1 | Zona 2 | Zona 3 | Zona 4 | Zona 5 | Kepala | Mati |
Suhu tubuh | 120 | 130 | 135 | 145 | 155 | 160 | 160 |