CAS No.: | 9002-88-4 |
---|---|
Material: | Polyethylene/PE |
Usage: | General Plastics |
Plastic Properties After Heated: | Thermosetting Plastic |
Plastic Forming Method: | Film Pressure |
Color: | White |
Pemasok dengan izin usaha terverifikasi
Properti Fisik |
Nilai umum | Komentar |
Kerapatan | 0,92g/cc | ISO 1183 |
Aliran meleleh (190C/2.16kg) | 0,90g/10 menit | ISO 1183 |
Sifat Mekanis | Nilai umum | Komentar |
Modulus elastisitas | 0,190Pa | MD,ISO 527 |
0,200GPa | TD,ISO 527 | |
Koefisien gesekan | 0.50 | ASTM D1894 |
Elorf merobek Strength MD | 145g | ASTM D1922 |
Elorf merobek kekuatan TD | 370g | ASTM D1922 |
Uji penurunan Dart | 150 g | ASTM D1709 |
Properti Optik | Nilai umum | Komentar |
Kabut asap | 12% | ASTM D1003 |
Mengkilap | 50% | ASTM D523 |
Memproses Properti | Nilai umum | |
Temperatur Rombak | 127C | |
180-225C |
Properti Fisik |
Nilai umum | Komentar |
Kerapatan | 0,92g/cc | ISO 1183 |
Aliran meleleh (190C/2.16kg) | 0,90g/10 menit | ISO 1183 |
Sifat Mekanis | Nilai umum | Komentar |
Modulus elastisitas | 0,190Pa | MD,ISO 527 |
0,200GPa | TD,ISO 527 | |
Koefisien gesekan | 0.50 | ASTM D1894 |
Elorf merobek Strength MD | 145g | ASTM D1922 |
Elorf merobek kekuatan TD | 370g | ASTM D1922 |
Uji penurunan Dart | 150 g | ASTM D1709 |
Properti Optik | Nilai umum | Komentar |
Kabut asap | 12% | ASTM D1003 |
Mengkilap | 50% | ASTM D523 |
Memproses Properti | Nilai umum | |
Temperatur Rombak | 127C | |
180-225C |
Pemasok dengan izin usaha terverifikasi