CAS No.: | 9011-14-7 |
---|---|
Material: | Polymethyl Methacrylate/PMMA |
Usage: | General Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Film Pressure |
Color: | White |
Pemasok dengan izin usaha terverifikasi
Spesifikasi
Item |
Metode Pengujian |
Kondisi Pengujian |
Satuan |
|
|
|
|
Fisik Properti |
Spesifik |
ISO 1183 |
23 DERAJAT C |
g/cm3 |
1.16 |
1.16 |
1.14 |
Transmisi ringan |
ISO 13468 |
3 mm |
% |
92 |
92 |
92 |
|
Kabut asap |
ISO 14782 |
3 mm |
% |
0.5 |
0.6 |
0.6 |
|
Indeks bias |
ASTM D452 |
nd |
- |
1.49 |
1.49 |
1.49 |
|
Penyerapan air |
ISO 62 |
24 jam |
% |
0.3 |
0.3 |
0.3 |
|
Termal Properti |
Panas Khusus |
JIS K7123 |
|
J/ (contoh: C) |
1.5 |
1.5 |
1.5 |
Koefisien Ekspansi Linear |
ASTM D696 |
|
1 DERAJAT C |
6 Tambah bintik pada 10-5 |
10 Tambah bintik pada 10-5 |
12 Tambah bintik pada 10-5 |
|
Laju Transfer panas |
ASTM C177 |
|
W/ (m.) |
0.2 |
0.2 |
0.2 |
|
Suhu distorsi panas. |
ISO 75 |
1,82MPa |
SBP |
82 |
92 |
81 |
|
Vicat Soft Temp. |
ISO 306 |
50N |
SBP |
85 |
93 |
78 |
|
Cair tidak lancar |
ISO 1133 |
230 DERAJAT C, 37,3 N |
g/10 menit |
6 |
1.1 |
1.3 |
|
Aliran spiral (Ketebalan 2 mm) |
MRC |
230 DERAJAT C |
mm |
ND |
170 |
200 |
|
250 DERAJAT C |
mm |
ND |
260 |
290 |
|||
Mekanis Properti |
Kekuatan tensil |
ISO 527 |
1A/5 |
MPa |
52 |
52 |
37 |
Ketegangan itu semakin lonter |
ISO 527 |
1A/5 |
% |
40 |
15 |
50 |
|
Modulus tensil |
ISO 527 |
1a/1 |
IPK |
1.8 |
1.9 |
1.4 |
|
Kekuatan fleksibilitas |
ISO 178 |
|
MPa |
76 |
76 |
52 |
|
Fleksibilitas selaput otak |
ISO 178 |
|
IPK |
1.9 |
1.9 |
1.5 |
|
Kekuatan dampak Izod |
ISO 180 |
1A |
KJ/m2 |
3.7 |
4.3 |
9.8 |
|
Dampak Charpy |
ISO 179 |
Tidak terpotong |
KJ/m2 |
49 |
62 |
110 |
|
Terpotong |
KJ/m2 |
2.8 |
2.7 |
6.6 |
|||
Kekerasan Rockwell |
ISO 2039 |
Skala m. |
- |
68 |
55 |
33 |
|
Properti Elektrial |
Resistivitas permukaan |
JIS K6911 |
|
Ω |
>1016 |
>1016 |
>1016 |
Kepekaan volume |
JIS K6911 |
|
Ωm |
>1013 |
>1013 |
>1013 |
|
Melalui kekuatan isolasi |
JIS K6911 |
4KV/det |
MV/m |
20 |
20 |
20 |
|
Kepekaan |
JIS K6911 |
60 Hz |
- |
3.7 |
3.7 |
3.7 |
|
Faktor atenuasi media |
JIS K6911 |
60 Hz |
- |
0.05 |
0.05 |
0.05 |
|
Resistansi ARC |
JIS K6911 |
|
- |
Tidak ada jejak |
Tidak ada jejak |
Tidak ada jejak |
Pemasok dengan izin usaha terverifikasi