Material: | Low Density Polyethylene/LDPE |
---|---|
Usage: | General Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Extrusion |
Color: | White |
mfr: | 1,9 g/10 menit |
Pemasok dengan izin usaha terverifikasi
Item properti | Kondisi Pengujian | Metode pengujian | Data pengujian | Unit data |
MFR | 190 derajat C/2.16kg | ISO 1133 | 1.9 | g/10 menit |
Kerapatan | ISO 1183 | 921 | kg/m3 | |
Kekuatan impulse | ASTM D-4272 | 20 | KJ/m | |
Mencabut kekuatan(MD) | ISO 6383-2 | 70 | KN/m | |
Mencabut kekuatan(TD) | ISO 6383-2 | 25 | KN/m | |
Menghasilkan stres (MD) | ISO 527-3 | 11 | MPa | |
Menghasilkan stres (TD) | ISO 527-3 | 11 | MPa | |
Stres fraktur | ISO 527-3 | 30 | MPa | |
Fraktur tegangan fraktur (TD) | ISO 527-3 | 17 | MPa | |
Naskh (penghapusan) dalam waktu dekat (MD) | ISO 527-3 | >100 | % | |
Naskh (penghapusan waktu) (TD) | ISO 527-3 | >500 | % | |
Modulus(MD) | ISO 527-3 | 190 | MPa | |
Modulus(TD) | ISO 527-3 | 190 | MPa | |
Faktor gesek | ASTM D-1894 | >1 | ||
gluttujuan | Metode SAB IC | 20 | g | |
Glutback | Metode SABIC | 50 | g | |
Mengkilap | 45 | ASTM D-2457 | 53 | |
Kabut asap | ASTM D-1003A | 10 | % | |
Transparansi | Metode SABIC | 26 | MV |