Material: | Acrimilitril-Butaena-Stie Copolimers/ABS |
---|---|
Penggunaan: | Plastk umum |
Properti plastik setelah Berpemanas: | Plastik berplastik berplastik |
Metode Pembentukan plastik: | Film Pressure (Tekanan Film) |
Warna: | Putih |
kekuatan impuls-impuls izod: | 25kg.cm/cm |
Pemasok dengan izin usaha terverifikasi
Properti item | Kondisi Pengujian | Metode pengujian | Data pengujian | Unit data |
Kekuatan tensil | 1/8",50mm/mnt | ASTM D-638 | 510 | kg/cm2 |
Laju regang | 1/8",50mm/mnt | ASTM D-638 | 40 | % |
Kekuatan fleksibilitas | 1/8",1,3 mm/mnt | ASTM D-790 | 770 | kg/cm2 |
Fleksibilitas selaput otak | 1/8",1,3 mm/mnt | ASTM D-790 | 25180 | kg/cm2 |
Kekuatan impuls | 1/8",23 DERAJAT C | ASTM D-256 | 25 | kg.cm/cm |
Kekerasan Rockwell | ASTM D-785 | 112 | R Scale (Skala Kanan) | |
Suhu distorsi | 1/8",1,8 MPa | ASTM D-648 | 80 | SBP |
Titik melemah | 1kg | ASTM D-1525 | 99 | SBP |
MFR | 220 derajat C/10 kg | ASTM D-1238 | 15.5 | g/10 menit |
Kerapatan | 23 DERAJAT C | ASTM D-792 | 1.045 | g/cm3 |
Laju Contractility | ASTM D-955 | 0.5-0.8 | % |