Usage: | General Plastics |
---|---|
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Injection |
ratio: | 120-200% |
panggil aman: | mengkilap |
aplikasi: | Widely Used to Produce Slippers, Shoes |
Pemasok dengan izin usaha terverifikasi
EVA16%
|
|||
PROPERTI
|
METODE PENGUJIAN
|
SATUAN
|
Data
|
Konten VA
|
|
%
|
16
|
Kerapatan
|
ASTM D1505
|
g/cm3
|
0.937
|
Cairkan Indeks
|
ASTM D1238
|
g/10 menit
|
1.5
|
Kekuatan tensil (Pemecahan)
|
ASTM D638
|
Kg/cm2
|
170
|
Naskh dalam waktu rehat
|
ASTM D638
|
%
|
700
|
Titik lebur
|
ASTM D-3418
|
89
|
|
Kekerasan
|
ASTM D2240
|
Pantai D
|
37
|
EVA 18%
|
|
||
Properti
|
Metode pengujian
|
Nilai
|
|
Konten VA(%)
|
USI
|
18
|
|
Kerapatan(g/cm3)
|
ASTM D792
|
0.939
|
|
Cairkan Indeks (g/10 menit)
|
ASTM D1238
|
2.5
|
|
Kekuatan tensil(Molded)(Break)(kg/cm2)
|
ASTM D638
|
180
|
|
Ongasi akhir (Molded)(%)
|
ASTM D638
|
750
|
|
Brittlewatan suhu Rendah(celcius/F50)
|
ASTM D746
|
<-76
|
|
Vicat lembek(celcius)
|
ASTM D1525
|
64
|
|
Titik leleh (celcius)
|
ASTM D3418
|
86
|
|
Kekerasan(Shore D)
|
ASTM D2240
|
36
|
|
EVA28%
|
|
||
PROPERTI
|
METODE PENGUJIAN
|
SATUAN
|
Data
|
Konten VA
|
|
%
|
28
|
Kerapatan
|
ASTM D1505
|
g/cm3
|
0.954
|
Cairkan Indeks
|
ASTM D1238
|
g/10 menit
|
15
|
Kekuatan tensil (Pemecahan)
|
ASTM D638
|
Kg/cm2
|
80
|
Naskh dalam waktu rehat
|
ASTM D638
|
%
|
>800
|
Titik lebur
|
ASTM D-3418
|
69
|
|
Kekerasan
|
ASTM D2240
|
Pantai D
|
20
|
Keuntungan:
1. Barang kami memiliki kualitas yang sangat baik dan harga yang kompetitif.
2.Ekspor komapny bahan EVA selama lebih dari 18 tahun.
Konten VA
|
Rentang Aplikasi
|
<5%
|
Film, kabel dan kabel, pengubah LDPE, adhesif, dan lain-lain
|
5%. 10%
|
Film elastis, molding injeksi dan pembuatan busa, dll.
|
28% - 20%
|
Utamanya digunakan untuk bahan perekat peleburan dan produk pelapis
|
28% - 33%.
|
Material Photovoltaic, perekat sel surya, dll
|
38% - 40%
|
Perekat
|
Pemasok dengan izin usaha terverifikasi