Polyurethane Prepolymer for Make Shoe Sole

• CAS No: 9009-54-5
• Rumus: c3h8n2o
• EINECS: 210-898-8
• Rantai Kepala molekuler: Polimer Rantai Karbon
• Warna: Putih
• aplikasi: untuk make shoe semata-mata
• Tidak. Model.: HD-5075-2G / HD-2122T
• Paket Transportasi: Various Package of Transport
• Spesifikasi: 220kg/235kg
• Merek Dagang: huide
• Asal: Cina
• Kode HS: 3909500000
• Kapasitas Produksi: 260000ton

Deskripsi Produk

HD-5075-2G / HD-2122T
Características: Densidad baja y dureza media-alta
Application: For slippers, beach shoes and direct injection shoes.
Typical properties of PU resin

Name of products	@40ºC Appearance	Density (g/cm^3@40^oC)	Viscosity (mPa·s @40^oC)	Package Size (kg/drum)
HD-5075-2G(POL, A)	Cream liquid	1.13~1.18	900~1200	18 / 220
HD-2122T(ISO, B)	Liquid	1.18~1.20	100~300	20 / 235

Processing
Please preheat materials at 60~70ºCfor 6~10 hours before processing. Then mix fully the whole drum of POL and other additives according to the following table. Finally, respectively transfer POL and ISO to their corresponding tanks.
Antes del moldeo, todos los componentes deben estar en estado líquido. Las materias primas deben precalentarse a bajas temperaturas en un tanque de calefacción de 60-70 °C (generalmente 6-10 horas, dependiendo de la cantidad y el tamaño del volumen de envasado. Es que el tiempo de fusión es diferente) antes de su uso. Los aditivos agregados deben mezclarse completamente con el material poliol antes de su uso y luego colocarse en el tanque de material. La cantidad de aditivos añadidos se muestra en la siguiente tabla.

HD-5075-2G (POL, A)	HD-H/g	water/g	HD-C-002/g	HD-C-009/g	Other
18 kg(one drum)	0~700	155	270	100	It depends
220 kg (one drum	0~8550	1900	3300	1200	It depends

Reactivity and product performance

Test Items	Reactivity parameters	Test Items	Product performance
Ratio of (A+C) and B material	100/109~123	Moulding density(g/cm^3)	0.28~0.32
Material temperature (^oC)	40~45/38~42	Hardness(23ºC)	60C~85C 40A~70A
Cream time (s)	3~5	Tensile strength(MPa)	≥3
End of rise time (s)	20~30	Elongation(%)	≥300
Free rise density (g/cm^3)	0.15~0.18	Tear strength(kN/m)	≥13
Metal mold temperature (^oC)	55~65	Flexing resistance(23ºC)	4  40,000 times no crack 40,000veces no grietas
Demould time(min)	2~3	DIN DIN abrasion resistance(mm3)	≤600

The ratio based on the best value varies with the type and quantity of added paint additives.
The free rise foam density varies with the seasonal variation (temperature, humidity)
Data listed above are just for reference. The detailed data are subjected to practical operation. Please contact us if other physical properties are essential.