Virgin Polymetil Metacryalmarhum resin transparan PMA - cm-207 Temperature

• Feature: Oxidative Degradable
• CAS No.: 9011-14-79
• Formula: [CH2c(CH3)(Cooch3)]N
• EINECS: pmma
• Material: Polymethyl Methacrylate/PMMA
• Usage: General Plastics
• Tidak. Model.: CM-207
• Plastic Properties After Heated: Thermosetting Plastic
• Plastic Forming Method: Injection
• Color: White
• nama: polymetil methyrycludeville
• nama lain: resin polymethyl methytelat/pmma
• carrier: pmma
• kelas: kelas molding injeksi/ekstrusi/blow
• gunakan: peralatan makan/pencahayaan/peralatan olahraga
• fitur: benturan/mengkilap tinggi
• fitur lainnya: transparansi tinggi/aliran tinggi
• warna: ketelekan
• formulir: granula/partikel
• tipe: virgin
• sertifikasi: iso, ce
• Paket Transportasi: Bag
• Spesifikasi: 25kg
• Merek Dagang: Chi Mei Company
• Asal: China
• Kode HS: 3906100000
• Kapasitas Produksi: 400000/Mt

Deskripsi Produk

Product Description

polymethyl methacrylate PMMA resin is a mature product. It has excellent weather-resist and heat-resist character, and excellent transparency and gloss. Besides, it has stable physical, chemical, optical, and electrical,etc., characters. It may be widely applied on electronic panel, mechanical parts, watch and clock shell, motorcycle and automobile indicator, tele communication material, insulation parts and sun glasses, etc
 

Product Parameters

 

 

Properties	ISO Test Method	Test Condition	Unit	CM-205
Melt Flow Index	1133	230ºC×3.8KG	ml/10 min	1.9
Mass Density	1183	23 ºC	g/cm3	1.19
Tensile Strength	527	5 mm/min, yield	MPa	70
		5 mm/min, break	MPa	70
Tensile Elongation	527	50 mm/min	%	12
Flexural Strength	178	2 mm/min	MPa	103
Flexural Modulus		2 mm/min	GPa	2.8
Izod Impact Strength	180/1A	23 ºC Notched	KJ/m2	2
		-30 ºC Notched	KJ/m2	-
Charpy Impact Strength	179	23 ºC Notched	KJ/m2	2
		-30 ºC Notched	KJ/m2	-
Vicat Softening Temp.	306	1 Kg,50 ºC/hr	ºC	115
		5 Kg,50 ºC/hr	ºC	107
Heat Distortion Temp.	75/A	1.8 MPa Unannealed	ºC	95
		1.8 MPa Annealed	ºC	104
Coefficient of Linear Thermal Expansion	11359	-	-	6 X 10-5
Flammability	-	UL-94	-	1.5mm HB
Mold Shrinkage	294-4	-	%	0.2~0.6
Symbol	1043	-	-	>PMMA<

Application

Molding methods include casting, injection molding, machining, thermoforming and so on. Especially injection molding, can be mass-produced, simple process, low cost. Therefore, its application is increasingly extensive, it is widely used in instrumentation parts, automotive lights, optical lenses, transparent pipes.

 

Packaging & Shipping

 

25kg/ carton or 25kg/bag, or per your requirement

25kgs net weight in PP woven or PE plastic bag about 20 tons for 20" container

 

 

Company Profile

Our company has been engaged in the production of plastic raw materials in 2010, located in Shijiazhuang, Hebei, China, covers an area of 500 mu, with more than 350 employees. The main products are carbon black, masterbatch, modifier (pvc, PP, pa6, pa66, pbt, abs), filler masterbatch, flame retardant, antioxidant, flexibility agent, plasticizer and other plastic raw materials (ldpe, hdpe, lldpe, pvc, pva, pbt, eva abs, eps, gpps, hips, pc pet, etc). After years of efforts and development, we have reached a certain scale, with a technical service team to provide users with high-quality, professional services

 

FAQ

1.We are able to provide customized service based on your requirements. 
2. Competitive prices - directly from factory to customer. 
3.Advanced equipments for testing and manufacturing. 
4.Professional and good after-sale service
5. Free sample for testing