Fitur ini: | Plastics |
---|---|
CAS No: | 25766-59-0 |
Rumus: | C6h4c(CH3)2c6h4oco2-]N |
EINECS: | 618-371-8 |
Material: | Polybonates/PC |
Penggunaan: | Plastk umum, Plastik teknik, Plastik khusus |
Pemasok dengan izin usaha terverifikasi
Deskripsi Produk | ||||
XHT3143T adalah aliran tinggi, UV distabilkan, polikarbonat panas tinggi. Fitur ini hanya tersedia dalam warna transparan yang terbatas | ||||
Umum | ||||
Dari Pelet resin | ||||
Memiliki fitur Thermal outdoor yang bagus | ||||
Menggunakan Kelistrikan otomotif | ||||
Metode Uji nilai Nominal Fisik | ||||
Kerapatan/Gravitasi tertentu 1.21 ASTM D792 1.2 g/cm³ ISO 1183 |
||||
Mold Shrrinkage, Flow(3.2 mm) 0.6 - 0.9 % Method | ||||
Laju Aliran cair[MFR](330 SBP;2.16 kgf) 33 g/10 mnt ASTM D1238 | ||||
Laju Penyerapan Air(23 SBP;jenuh) 0.3% ISO 62-1 | ||||
Laju Penyerapan Kelembapan(50% RH;23 SBP C) 0.3 % ISO 62 | ||||
Laju cair, (2.16 kg;330 SBP) 30 cm³/10 mnt 1133 | ||||
Metode Uji nilai Nominal Mekanis | ||||
Dampak Izod, ASTM D256 dengan takik | ||||
SBP 23 C 97 J/m | ||||
C 55 J/m | ||||
Pengaruh Dart, Total Energy(23 SBP) 68 J ASTM D3763 | ||||
Kekuatan dampak Izod tidak BERALUR ISO 180/1U | ||||
Tidak bertakik;80*10*3;23 SBP 0 NB kJ/m² | ||||
Tidak terpotong;80*10*3;-30 SBP /m² 0 NB | ||||
Kekuatan benturan Izod bertakik ISO 180/1A | ||||
Terpotong;80*10*3;23 SBP C 0 9 kJ/m² | ||||
Terpotong;80*10*3;-30 SBP /m² 0 9 kJ/ | ||||
Dampak C Humpy, ISO 179 1eA terpotong | ||||
SBP 23 C;Edgew;80*10*3;sp =62mm 0 11 kJ/m² | ||||
C;;80*10*3;sp =62mm 0 9 kJ/m² | ||||
Dampak C Humpy, tanpa takik ISO 179 1eU | ||||
SBP 23 C;Edgew;80*10*3;sp =62mm 0 NB kJ/m² | ||||
C;;80*10*3;sp =62mm 0 NB kJ/m² | ||||
Tekanan tensil, hasil | ||||
50 mm/mnt;Tipe I | 70 MPa | ASTM D638 | ||
50 mm/mnt | 70 MPa | ISO 527 | ||
Tekanan tensil, Pelepas | ||||
50 mm/mnt;Tipe I | 55 MPa | ASTM D638 | ||
50 mm/mnt | 60 MPa | ISO 527 | ||
Ketegangan tensil, yield | ||||
50 mm/mnt;Tipe I | 6 % | ASTM D638 | ||
50 mm/mnt | 6 % | ISO 527 | ||
Ketegangan tensil, Pemecahan | ||||
50 mm/mnt;Tipe I | 70 % | ASTM D638 | ||
50 mm/mnt | 70 % | ISO 527 | ||
Modulus tensil | ||||
5 mm/mnt | 2700 MPa | ASTM D638 | ||
1 mm/mnt | 2500 MPa | ISO 527 | ||
Fleksibilitas fleksibilitas | ||||
1.3 mm/mnt;50 mm;span | 120 MPa | ASTM D790 | ||
2 mm/mnt | 80 MPa | ISO 178 | ||
Fleksibilitas selaput otak | ||||
1.3 mm/mnt;50 mm;span | 2600 MPa | ASTM D790 | ||
2 mm/mnt | 2500 MPa | ISO 178 | ||
Termal | Nilai nominal | Metode Pengujian | ||
Temperatur lunak | ||||
Laju B/50 | SBP 170 | ASTM D1525 | ||
Laju B/50 | SBP 168 | ISO 306 | ||
Laju B/120 | SBP 170 | ISO 306 | ||
Suhu Defleksi panas[HDT], tidak disGrup 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
SBP 166 SBP 156 |
ASTM D648 | ||
CTE, Flow | ||||
SBP - 40 - 40 | 6,0E-05 1/ C | ASTM E831 | ||
SBP - 40 - 40 | 6,0E-05 1/ C | ISO 11359-2 | ||
CTE, XFlow | ||||
SBP - 40 - 40 | 6,0E-05 1/ C | ASTM E831 | ||
SBP - 40 - 40 | 6,0E-05 1/ C | ISO 11359-2 | ||
HDT/AF(1.8) | SBP 152 | ISO 75/AF | ||
Sedang memproses | Nilai nominal | |||
Temperatur pengeringan<injeksi> | SBP 135 | |||
Waktu pengeringan<injeksi> | 4 - 6 jam | |||
Kandungan Kelembapan Maksimum<injeksi> | 0.02 % | |||
Temperatur larut<injeksi> | SBP - 325 - 290 | |||
Suhu nozzle<injeksi> | SBP - 320 - 285 | |||
Temperatur Depan, Zona 3<injeksi> | SBP - 325 - 290 | |||
Temperatur Tengah, Zona 2<injeksi> | SBP - 310 - 280 | |||
Temperatur Belakang, Zona 1<injeksi> | SBP - 300 - 270 | |||
Suhu mold<injeksi> | SBP - 130 - 95 | |||
Tekanan Balik<injeksi> | 0.3 - 0.7 MPa | |||
Kecepatan sekrup <injeksi> | 40 - 90 rpm | |||
Bidik ke Ukuran Silinder<injeksi> | 40 - 60 % | |||
Kedalaman Ventilasi <injeksi> | 0.025 - 0.08 mm |