Fitur ini: | plastik |
---|---|
CAS No: | 25766-59-0 |
Rumus: | c6h4c(ch3)2c6h4o2-]n |
EINECS: | 618-371-8 |
Material: | Polybonates/PC |
Penggunaan: | Plastk umum, Plastik teknik, Plastik khusus |
Pemasok dengan izin usaha terverifikasi
Deskripsi Produk | ||||
XHT2141 adalah sebuah aliran yang tinggi, high-heat polikarbonat. Cahaya dapat diperoleh dalam rentang warna transparan yang buram dan terbatas . | ||||
Umum | ||||
Formulir | Pelet resin | |||
Fitur | Good Thermal | |||
Kartu Kuning UL | E207780-100127670 | |||
Menggunakan otomotif | Pelanggan | Kelistrikan | ||
Fisik | Nilai nominal | Metode Pengujian | ||
Kerapatan/Gravitasi tertentu | 1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 |
||
Mold Shrinkage, Flow(3.2 mm) | 0.6 - 0.9 % | Metode | ||
Laju Aliran cair[MFR](330 SBP;2.16 kgf) | 46 g/10 menit | ASTM D1238 | ||
Laju Penyerapan Air(23 SBP;jenuh) | 0.3 % | ISO 62-1 | ||
Laju Penyerapan Kelembapan(50% RH;23 SBP C) | 0.23 % | ISO 62 | ||
Laju cair, (2.16 kg;330 SBP) | 43 cm³/10 mnt | ISO 1133 | ||
Mekanis | Nilai nominal | Metode Pengujian | ||
Izod Impact (dampak Izod) berbentuk zod, bertakik SBP 23 C 80*10*4;23 SBP C 80*10*4;-30 SBP |
115 J/m 75 J/m 11 kJ/m² 10 kJ/m² |
ASTM D256 ASTM D256 ISO 180/1A ISO 180/1A |
||
Pengaruh Dart, Total Energy(23 SBP) | 68 J | ASTM D3763 | ||
Kekuatan benturan Izod yang tidak Bertakik Tidak terpotong;80*10*3;23 SBP C 0 Tidak terpotong;80*10*3;-30 SBP 0 |
Jml kJ/m² Jml kJ/m² |
ISO 180/1U | ||
Kekuatan benturan Izod Bertakik Terpotong;80*10*3;23 SBP C 0 Terpotong;80*10*3;-30 SBP C 0 |
10 kJ/m² 9 kJ/m² |
ISO 180/1A | ||
C dampaknya, V-bertakik SBP 23 C;Edgew;80*10*3;sp =62mm 0 C;;80*10*3;sp =62mm 0 |
12 kJ/m² 9 kJ/m² |
ISO 179 1eA | ||
Dampak C haram, tanpa hambatan SBP 23 C;Edgew;80*10*3;sp =62mm 0 C;;80*10*3;sp =62mm 0 |
Jml kJ/m² Jml kJ/m² |
ISO 179 1eU | ||
Tekanan tensil, hasil | ||||
50 mm/mnt;Tipe I | 70 MPa | ASTM D638 | ||
50 mm/mnt | 70 MPa | ISO 527 | ||
Tekanan tensil, Pelepas | ||||
50 mm/mnt;Tipe I | 60 MPa | ASTM D638 | ||
50 mm/mnt | 60 MPa | ISO 527 | ||
Ketegangan tensil, yield | ||||
50 mm/mnt;Tipe I | 6.5 % | ASTM D638 | ||
50 mm/mnt | 6.5 % | ISO 527 | ||
Ketegangan tensil, Pemecahan | ||||
50 mm/mnt;Tipe I | 90 % | ASTM D638 | ||
50 mm/mnt | 90 % | ISO 527 | ||
Modulus tensil | ||||
5 mm/mnt | 2600 MPa | ASTM D638 | ||
1 mm/mnt | 2600 MPa | ISO 527 | ||
Fleksibilitas fleksibilitas | ||||
1.3 mm/mnt;50 mm;span | 110 MPa | ASTM D790 | ||
2 mm/mnt | 100 MPa | ISO 178 | ||
Fleksibilitas selaput otak | ||||
1.3 mm/mnt;50 mm;span | 2550 MPa | ASTM D790 | ||
2 mm/mnt | 2450 MPa | ISO 178 | ||
Termal | Nilai nominal | Metode Pengujian | ||
UL dikenal(≥ 1.5 mm) | HB | UL 94 | ||
Temperatur pengapian kabel cahaya [GWIT](3 mm) | SBP 875 | IEC 60695-2-13 | ||
Indeks Flamabilitas Kabel bersinar 3 mm 2 mm 1 mm |
SBP 960 SBP 960 SBP 960 |
IEC 60695-2-12 | ||
Temperatur lunak | ||||
Laju B/50 | SBP 161 | ASTM D1525 | ||
Laju B/50 | SBP 160 | ISO 306 | ||
Laju B/120 | SBP 162 | ISO 306 | ||
Suhu Defleksi panas[HDT], tidak disGrup 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
SBP 155 SBP 145 |
ASTM D648 | ||
CTE, Flow | ||||
SBP - 40 - 40 | 6,0E-05 1/ C | ASTM E831 | ||
SBP - 40 - 40 | 6,0E-05 1/ C | ISO 11359-2 | ||
CTE, XFlow | ||||
SBP - 40 - 40 | 6,0E-05 1/ C | ASTM E831 | ||
SBP - 40 - 40 | 6,0E-05 1/ C | ISO 11359-2 | ||
Konduktivitas termal @ 25 SBP 25 (SBP) | 0.2 W/m-K | ASTM C177 | ||
Uji Tekanan Bola (125 2 C +/- C) | BERLALU | IEC 60695-10-2 | ||
HDT/BF (0.45) | SBP 155 | ISO 75/BF | ||
HDT/AF(1.8) | SBP 142 | ISO 75/AF | ||
Awalnya asap yang sempurna | SBP 155 | Metode | ||
Indeks suhu relatif, Elec | SBP 150 | UL 746B | ||
Indeks suhu relatif, Mekanis dengan dampak | SBP 130 | UL 746B | ||
Indeks suhu relatif, Mekanis tanpa dampak | SBP 150 | UL 746B | ||
Kelistrikan | Nilai nominal | Metode Pengujian | ||
Kepekaan volume | > 1,0E+17 ohm · | ASTM D257 | ||
Resistivitas permukaan | > 1.E+17 ohm | ASTM D257 | ||
Kekuatan dielektrik, dalam Oli(3.2 mm) | 22.6 kV/mm | ASTM D149 | ||
Faktor menghilangkan 100 Hz 1,0e+6 Hz |
3 3.1 |
ASTM D150 | ||
Indeks Pelacak komparatif, CTI | PLC 3 | UL 746A | ||
Pengapian kabel-panas, HWI(1.5 mm) | PLC 3 | UL 746A | ||
Pengapian Busur Amp Tinggi, HAI (1.5 mm) | PLC 0 | UL 746A | ||
Sedang memproses | Nilai nominal | |||
Temperatur pengeringan<injeksi> | SBP 125 | |||
Waktu pengeringan<injeksi> | 4 - 6 jam | |||
Kandungan Kelembapan Maksimum<injeksi> | 0.02 % | |||
Temperatur larut<injeksi> | SBP - 350 - 290 | |||
Suhu nozzle<injeksi> | SBP - 345 - 285 | |||
Temperatur Depan, Zona 3<injeksi> | SBP - 350 - 290 | |||
Temperatur Tengah, Zona 2<injeksi> | SBP - 340 - 280 | |||
Temperatur Belakang, Zona 1<injeksi> | SBP - 330 - 270 | |||
Suhu mold<injeksi> | SBP - 130 - 85 | |||
Tekanan Balik<injeksi> | 0.3 - 0.7 MPa | |||
Kecepatan sekrup <injeksi> | 40 - 90 rpm | |||
Bidik ke Ukuran Silinder<injeksi> | 40 - 60 % | |||
Kedalaman Ventilasi <injeksi> | 0.025 - 0.08 mm |