Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
EINECS: | 618-371-8 |
Material: | Polycarbonates/PC |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Pemasok dengan izin usaha terverifikasi
Penggunaan | Listrik otomotif | Industrialisasi pelanggan Hidrokarbon dan Energi |
||
Fisik | Nilai nominal | Metode Pengujian | ||
Kerapatan/Gravitasi tertentu | 1.16 g/cm³ 1.16 |
ISO 1183 ASTM D792 |
||
Penyerapan Kelembapan | ISO 62-4 | |||
SBP 23 C;50% RH/24 jam | 0.15 % | |||
SBP 23 C;50% RH/Keseimbangan | 0.3 % | |||
Penyerapan air | ||||
SBP 24 jam;23 jam | 0.7 % | ISO 62-1 | ||
23 SBP;jenuh | 3.5 % | ISO 62-1 | ||
SBP 24 jam;23 jam | 0.7 % | ASTM D570 | ||
23 o C/jenuh | 3.5 % | ASTM D570 | ||
Laju Volume cair , MVR | ISO 1133 | |||
2.16 kg;MVR pada 250 SBP | 5 cm³/10 mnt | |||
5 kg;MVR pada 250 SBP | 15 cm³/10 mnt | |||
5 kg;MVR pada 260 SBP | 23 cm³/10 mnt | |||
Laju Aliran cair[MFR](250 SBP;5 kgf) | 15 g/10 menit | ASTM D1238 | ||
Mold Shrinkage, Flow | 0.5 - 0.7 % | Metode | ||
Mold Shrinkage, XFlow | 0.6 - 0.8 % | Metode | ||
Mekanis | Nilai nominal | Metode Pengujian | ||
Izod Impact (dampak Izod) berbentuk zod, bertakik 80*10*4;23 SBP C 80*10*4;-30 SBP SBP 23 C |
60 kJ/m² 60 kJ/m² 850 J/m 750 J/m |
ISO 180/1A ISO 180/1A ASTM D256 ASTM D256 |
||
Kekuatan benturan Izod Bertakik Terpotong;80*10*3;23 SBP C 0 Terpotong;80*10*3;-30 SBP C 0 |
65 kJ/m² 65 kJ/m² |
ISO 180/1A | ||
Kekuatan benturan Izod yang tidak Bertakik Tidak terpotong;80*10*3;23 SBP C 0 Tidak terpotong;80*10*3;-30 SBP 0 |
Jml kJ/m² Jml kJ/m² |
ISO 180/1U | ||
Izod Impact (dampak Izod), Unbertakik 80*10*4;23 SBP C 80*10*4;-30 SBP SBP 23 C |
Jml kJ/m² Jml kJ/m² Jml J/m Jml J/m |
ISO 180/1U ISO 180/1U ASTM D4812 ASTM D4812 |
||
C dampaknya, V-bertakik 23 SBP C;Edgew;80*10*4;sp =62 mm 0 SBP - 30 C;Edgew;80*10*4;sp =62 mm 0 |
60 kJ/m² 60 kJ/m² |
ISO 179 1eA | ||
Dampak C haram, tanpa hambatan 23 SBP C;Edgew;80*10*4;sp =62 mm 0 SBP - 30 C;Edgew;80*10*4;sp =62 mm 0 |
Jml kJ/m² Jml kJ/m² |
ISO 179 1eU | ||
Dampak instrumented multi-Aksial, Total Energy SBP 23 C |
65 J 65 J |
ISO 6603-2 | ||
Dampak instrumented multi-Aksial, Peak Energy SBP 23 C |
55 J 55 J |
ISO 6603-2 | ||
Dampak Dart terinstrumentasi, Total Energy SBP 23 C |
40 J 40 J |
ASTM D3763 | ||
Dampak Dart terinstrumentasi, Energi di Puncak SBP 23 C |
35 J 35 J |
ASTM D3763 | ||
Dampak Dart terinstrumentasi, gaya Puncak SBP 23 C |
4000 N. 4800 N. |
ASTM D3763 | ||
Modulus tensil | ||||
1 mm/mnt | 1750 MPa | ISO 527 | ||
50 mm/mnt | 1750 MPa | ASTM D638 | ||
Tekanan tensil, hasil | ||||
50 mm/mnt | 45 MPa | ISO 527 | ||
50 mm/mnt;Tipe I | 45 MPa | ASTM D638 | ||
Ketegangan tensil, yield | ||||
50 mm/mnt | 5.5 % | ISO 527 | ||
50 mm/mnt;Tipe I | 5.5 % | ASTM D638 | ||
Ketegangan tensil, Pemecahan | ||||
50 mm/mnt | > 60 % | ISO 527 | ||
50 mm/mnt;Tipe I | > 60 % | ASTM D638 | ||
Tegangan Nominal tensil, Break | ||||
50 mm/mnt | > 60 % | ISO 527 | ||
50 mm/mnt;Tipe I | > 60 % | ASTM D638 | ||
Fleksibilitas selaput otak | ||||
2 mm/mnt | 1825 MPa | ISO 178 | ||
1.3 mm/mnt;50 mm;span | 1900 MPa | ASTM D790 | ||
Kekuatan fleksibilitas | ||||
2 mm/mnt | 70 MPa | ISO 178 | ||
1.3 mm/mnt;50 mm;span | 70 MPa | ASTM D790 | ||
Kekerasan Indentasi Bola(H358/30) | 78 MPa | ISO 2039-1 | ||
Termal | Nilai nominal | Metode Pengujian | ||
HDT/AF(1.8) | SBP 105 | ISO 75/AF | ||
HDT/BF (0.45) | SBP 123 | ISO 75/BF | ||
Temperatur lunak | ||||
Laju B/50 | SBP 123 | ISO 306 | ||
Laju B/120 | SBP 123 | ISO 306 | ||
Tarif A/50 | SBP 137 | ISO 306 | ||
Tarif A/120 | SBP 138 | ISO 306 | ||
Laju B/50 | SBP 123 | ASTM D1525 | ||
Laju B/120 | SBP 123 | ASTM D1525 | ||
CTE, Flow | ||||
23 o C hingga 50 C | 8,5E-05 1/ C | ISO 11359-2 | ||
23 o C hingga 50 C | 8,5E-05 1/ C | ASTM E831 | ||
CTE, XFlow | ||||
23 o C hingga 50 C | 1.1E-04 1/ C | ISO 11359-2 | ||
23 o C hingga 50 C | 1.1E-04 1/ C | ASTM E831 | ||
Suhu Defleksi panas[HDT], tidak disGrup 3.2 mm;1.82 MPa 0.45 MPa;3.2 mm |
SBP 105 SBP 123 |
ASTM D648 | ||
Uji Tekanan Bola (125 2 C +/- C) | Lulus | IEC 60695-10-2 | ||
Kelistrikan | Nilai nominal | Metode Pengujian | ||
Indeks Pelacakan perbandingan | 175 V. | IEC 60112 | ||
Resistivitas permukaan, ROA | 1,0E+09 - 1,0E +11 ohm | IEC 60093 | ||
Peluruhan statis(5000 V hingga <50V) | < 0.01 detik | FTMS101B | ||
Konstanta dielektrik(6,0e+10 - 9,0e+10 Hz) | 2.73 | |||
Faktor menghilangkan(6,0e+10 - 9,0e+10 Hz) | 0.022 | |||
Resistivitas permukaan | 1,0E+09 - 1,0E +11 ohm | ASTM D257 |