Feature: | Natural Color |
---|---|
CAS No.: | 9003-54-7 |
Formula: | C33h33n3X2 |
Material: | Styrene-Acrylonitrile Copolymers/AS,SAV |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Pemasok dengan izin usaha terverifikasi
Deskripsi Produk | ||||||
Polypropylene copolymer UL94 V0. Emisi asap rendah, tanpa halogen dan Antimon oksida. | ||||||
Umum | ||||||
Dari Pelet resin | ||||||
Fitur |
Api Non-Brodicated & Non- Chlorinasi Retardant |
Bebas Antimon EC 1907/2006 (Jangkauan) |
Asap sedikit | |||
Kartu Kuning UL | E477602-102433013 | |||||
Menggunakan Peralatan | Kelistrikan | |||||
Fisik | Nilai nominal | Metode Pengujian | ||||
Kerapatan/Gravitasi tertentu | 1.05 g/cm³ | ASTM D792 | ||||
Laju Aliran Massa cair, MFR(230 SBP - 2.16 kg) | 15 g/10 menit | ASTM D1238 | ||||
Molding Shrincage | 1.5 % | Metode Internal | ||||
Mekanis | Nilai nominal | Metode Pengujian | ||||
Kekuatan tensil, hasil | 23.0 MPa | ASTM D638 | ||||
Sebuah yield Enonh Naskh | 3.2 % | ASTM D638 | ||||
Ketegangan yang lebih lonter, istirahat | 22 % | ASTM D638 | ||||
Fleksibilitas selaput otak | 1600 MPa | ASTM D790 | ||||
C Hup Notched Impact Strength(23 SBP) | 1.5 kJ/m² | ISO 179 1eA | ||||
C Hup kekuatan dampak tidak bertakik(23 SBP) | 20 kJ/m² | ISO 179 1eU | ||||
Pengaruh Izod Bertakik(23 SBP) | 35 J/m | ASTM D256 | ||||
Termal | Nilai nominal | Metode Pengujian | ||||
Suhu defleksi di bawah Muat, tidak dapat disamai (1.8 MPa) | SBP 60.0 | ASTM D648 | ||||
Temperatur melemah Vicat (50 SBP/h;50 N;Rate A;Pemuatan 2) | SBP 77.0 | ASTM D1525 | ||||
Uji Tekanan Bola(125 SBP) | Lulus | IEC 335 | ||||
Tetapan kebakaran 1.6 mm 3.2 mm |
V-0 V-0 |
UL 94 | ||||
Indeks Flamabilitas Kabel bersinar(3 mm) | SBP 960 | IEC 60695-2-12 | ||||
Temperatur pengapian kabel cahaya [GWIT](3 mm) | SBP 775 | IEC 60695-2-13 | ||||
Oksigen | 30 % | ASTM D2863 | ||||
Uji Flame jarum | Lulus | IEC 60695-11-5 | ||||
Kelistrikan | Nilai nominal | Metode Pengujian | ||||
Indeks Pelacakan perbandingan | 600 V. | IEC 60112 | ||||
Sedang memproses | Nilai nominal | |||||
Temperatur pengeringan<injeksi> | SBP 80 | |||||
Waktu pengeringan<injeksi> | 2.0 jam | |||||
Temperatur Belakang<injeksi> | SBP 190 | |||||
Suhu Tengah<injeksi> | SBP 210 | |||||
Temperatur Depan<injeksi> | SBP 220 | |||||
Suhu mold<injeksi> | SBP - 60 - 40 |