Butiran polikarbonat dengan harga penyebar LED transparan resin PC Clear Colour - Kellet/plastik Bahan mentah

• Feature: Oxidative Degradable
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Tidak. Model.: DMX1435D
• formulir: kemungkinan kecil resin
• bahan kimia: nilon
• mode pemrosesan: molding/ekstrusi injeksi
• uv: fr. (fr)
• gunakan: peralatan listrik, suku cadang otomatis, persediaan kantor
• sertifikat: iso9001:2008.sg.rohs
• pengiriman ringan: 92%
• Paket Transportasi: Bag
• Spesifikasi: 25KG
• Merek Dagang: Forever
• Asal: China
• Kode HS: 390740000
• Kapasitas Produksi: 50000t/Year

Deskripsi Produk

Polycarbonate Granules LED Diffuser PMMA Price Transparent Clear Color PC Resin/Pellet/Plastic Raw Material

 

LNP ELCRES DMX1435D is a UV stabilized standard flow Polycarbonate (PC) copolymer resin with diffusion effect and improved scratch resistance. This grade is a good candidate for consumer electronics, mobility interiors and other adjacent applications, which need lower scratch and diffusive effects performance.

   
 

Product Description
LNP ELCRES DMX1435D is a UV stabilized standard flow Polycarbonate (PC) copolymer resin with diffusion effect and improved scratch resistance. This grade is a good candidate for consumer electronics, mobility interiors and other adjacent applications, which need lower scratch and diffusive effects performance.
General
Form	Resin Pellets
Feature                                     Diffusive                            Anti-Scratch                      Outdoor
Automotive                       Consumer   Building and Construction			Electrical
Physical		Nominal Value	Test Method
Specific Gravity		1.18	ASTM D792
Specific Volume		0.85 cm³/g	ASTM D792
Density		1.17 g/cm³ 1.18 g/cm³	ASTM D792 ISO 1183
Water Absorption 24 hrs;23 °C 23°C/Saturated 23 °C;saturated		0.08 % 0.28 % 0.27 %	ASTM D570 ASTM D570 ISO 62-1
Moisture Absorption, Equilibrium(50% RH)		0.13 %	ASTM D570
Moisture Absorption 23 °C;50% RH/24 hrs 50% RH;23 °C		0.04 % 0.13 %	ASTM D570 ISO 62
Mold Shrinkage, Flow(3.2 mm)		0.5 - 0.8 %	SABIC Method
Melt Flow Rate[MFR](300 °C;1.2 kgf)		15.4 g/10min	ASTM D1238
Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C)		14 cm³/10 min	ISO 1133
Mechanical		Nominal Value	Test Method
Izod Impact, Unnotched(23 °C)		NB J/m	ASTM D4812
Izod Impact, Notched			ASTM D256
23 °C		30 J/m
-30 °C		30 J/m
Instrumented Dart Impact, Total Energy(23 °C)		7 J	ASTM D3763

 

Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0	NB kJ/m² 40 kJ/m²	ISO 180/1U
Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0	2.2 kJ/m² 2 kJ/m²	ISO 180/1A
Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0	2.2 kJ/m² 2.5 kJ/m²	ISO 179 1eA
Charpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0	NB kJ/m² 46 KJ/m²	ISO 179 1eU
Tensile Stress, Yield 50 mm/min;Type I 50 mm/min	77 MPa 77 MPa	ASTM D638 ISO 527
Tensile Stress, Break 50 mm/min;Type I 50 mm/min	60 MPa 59 MPa	ASTM D638 ISO 527
Tensile Strain, Yield 50 mm/min;Type I 50 mm/min	7.5 % 7 %	ASTM D638 ISO 527
Tensile Strain, Break 50 mm/min;Type I 50 mm/min	20 % 20 %	ASTM D638 ISO 527
Tensile Modulus 50 mm/min 1 mm/min	2700 MPa 2400 MPa	ASTM D638 ISO 527
Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min	120 MPa 110 MPa	ASTM D790 ISO 178
Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min	2500 MPa 2600 MPa	ASTM D790 ISO 178
Hardness, Rockwell L	110	ASTM D785

 

Hardness, Rockwell M	90	ASTM D785
Pencil Hardness Test(1kgf)	H	ASTM D3363
Thermal	Nominal Value	Test Method
UL Recognized(≥ 0.6 mm)	HB	UL 94
Vicat Softening Temperature
Rate B/50	138 °C	ASTM D1525
Rate B/50	136 °C	ISO 306
Rate B/120	138 °C	ISO 306
Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa	129 °C 115 °C	ASTM D648
CTE, Flow -40°C to 95°C 23°C to 80°C	7.0E-05 1/°C 7.0E-05 1/°C	ASTM E831 ISO 11359-2
CTE, XFlow -40°C to 95°C 23°C to 80°C	7.0E-05 1/°C 7.0E-05 1/°C	ASTM E831 ISO 11359-2
HDT/Bf(0.45)	129 °C	ISO 75/Bf
HDT/Af(1.8)	115 °C	ISO 75/Af
Relative Temp Index, Elec	80 °C	UL 746B
Relative Temp Index, Mechanical with Impact	80 °C	UL 746B
Relative Temp Index, Mechanical without Impact	80 °C	UL 746B
Optical	Nominal Value	Test Method
Light Transmission At 2.0 Mm(2 mm)	85 %	ASTM D1003
Haze(2 mm)	85 %	SABIC Method

 

Processing	Nominal Value
Drying Temperature<Injection>	120 °C
Drying Time<Injection>	3 - 4 hrs
Maximum Moisture Content<Injection>	0.02 %
Melt Temperature<Injection>	295 - 315 °C
Nozzle Temperature<Injection>	290 - 310 °C
Front, Zone 3 Temperature<Injection>	295 - 315 °C
Middle, Zone 2 Temperature<Injection>	280 - 305 °C
Rear, Zone 1 Temperature<Injection>	260 - 280 °C
Hopper Temperature<Injection>	60 - 80 °C
Mold Temperature<Injection>	70 - 95 °C

 .
 .

                                                                                                                  Forever Co.,Ltd

With almost 20 years in the modified engineering plastics,Forever Plastics is a high-tech manufacture integrating R&D, production and sales of high-performance resin or polymer ,including PC,PP,PA6,PA66, PBT,PET, PC/ABS, PC/PBT, PC/PET alloy compounds,TPE,TPU, PE for rotomolding with the property of the flame retardant, glass fiber reinforced, high glossy, UV resistance.....with the annual output value of USD 65 million in 2021. 

Our customers are Osram,Cree,,Siemens,etc. for years in the electrical&electronics components, Automotive parts, House appliance,LED lights.....