Feature: | Oxidative Degradable |
---|---|
CAS No.: | 32131-17-2 |
Formula: | (C12h22n2o2)N |
EINECS: | 211-024-8 |
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Pemasok dengan izin usaha terverifikasi
Poliamida 6, pengisi mineral 30%, penghambat api , halogen dan bebas fosfor merah
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-konduktor nilon
Deskripsi Produk | ||||
( 6M30V0EF) poliamida 6, pengisi mineral 30%, penghambat api, halogen dan bebas fosfor merah , untuk molding injeksi. | ||||
Umum | ||||
Dari Pelet resin | ||||
Pengisian 30 % Mineral | ||||
Tidak terBromina & Non- | ||||
Fitur | Api klorinasi | |||
Retardant | ||||
Fisik | Nilai nominal | Metode Pengujian | ||
Kerapatan/Gravitasi tertentu | 1.42 g/cm³ | ISO 1183 | ||
Srinkage molding , melalui Flow(50% RH;23 SBP;72 jam) | 0.60 - 0.80 % | ISO 2577 | ||
Srinkage molding , Flow(50% RH;23 SBP;72 jam) | 0.50 - 0.70 % | ISO 2577 | ||
Mekanis | Nilai nominal | Metode Pengujian | ||
Modulus tensil | 5800 MPa | ISO 527-2/1 | ||
Tekanan tensil, Pelepas | 70.0 MPa | ISO 527-2/5 | ||
Ketegangan tensil, Pemecahan | 2.0 % | ISO 527-2/5 | ||
Fleksibilitas selaput tubuh (2 mm/mnt) | 5500 MPa | ISO 178 | ||
Stres fleksibilitas fleksibilitas fleksibilitas (2 mm/mnt) | 110 MPa | ISO 178 | ||
C Hup Notched Impact Strength(23 SBP) | 3.0 kJ/m² | ISO 179 1eA | ||
C Hup kekuatan dampak tidak bertakik(23 SBP) | 30 kJ/m² | ISO 179 1eU | ||
Kekuatan dampak Izod Bertakik(23 SBP) | 3.5 kJ/m² | ISO 180/1A | ||
Kekuatan dampak takuk Izod(23 SBP) | 25 kJ/m² | ISO 180/1U | ||
Termal | Nilai nominal | Metode Pengujian | ||
Suhu Defleksi panas, tak disamai | ||||
0.45 MPa | SBP 200 | ISO 75-2/B | ||
1.8 MPa | SBP 115 | ISO 75-2/A | ||
Temperatur lunak | SBP 200 | ISO 306/B50 | ||
Titik Lekapan | SBP 221 | ISO 11357-3 | ||
Rasio pembakaran | < 100 mm/mnt | FMVSS 302 | ||
Peringkat api (1.5 mm) | V-0 | UL 94 | ||
Indeks Flamabilitas Kabel bersinar(1 - 3 mm) | SBP 960 | IEC 60695-2-12 | ||
Temperatur pengapian kabel cahaya [GWIT](1 - 3 mm) | SBP 750 | IEC 60695-2-13 | ||
Kelistrikan | Nilai nominal | Metode Pengujian | ||
Resistivitas permukaan | 1,0E+13 ohm | IEC 60093 | ||
Kepekaan volume | 1,0e+15 ohm ·cm | IEC 60093 | ||
Indeks Pelacakan perbandingan, Solusi A | 600 V. | IEC 60112 | ||
Sedang memproses | Nilai nominal | |||
Temperatur pengeringan<injeksi> | SBP - 85 - 75 | |||
Waktu pengeringan<injeksi> | 2.0 - 4.0 jam | |||
Temperatur Pemrosesan, peleburan<injeksi> | SBP - 270 - 240 | |||
Suhu mold<injeksi> | SBP - 100 - 80 |
Forever Co.,Ltd