Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
EINECS: | 618-371-8 |
Material: | Polycarbonates/PC |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Pemasok dengan izin usaha terverifikasi
Deskripsi Produk | ||||
Buram EXL, kemampuan UV-distabilkan & pelindung cahaya ( Ketebalan dinding >0,8mm), untuk aplikasi tutup perangkat elektronik portabel. Hanya tersedia dalam warna putih, abu-abu, dan pastel terbatas. Lihat CIC atau PM untuk warna ketersediaan & batasan. |
||||
Umum | ||||
Formulir | Pelet resin | |||
Fitur | Dampak Temperatur Rendah dampak terhadap ht shi ldi luar ruangan | Benturan keras | ||
Kartu Kuning UL E207780-642296 | ||||
Menggunakan otomotif | Industria | Kelistrikan | ||
Fisik | Nilai nominal | Metode Pengujian | ||
Kerapatan/Gravitasi tertentu | 1.28 1.28 g/cm³ |
ASTM D792 ISO 1183 |
||
Mold Shrinkage, Flow(3.2 mm) | 0.4 - 0.8 % | Metode | ||
Laju Aliran cair[MFR](300 SBP;1.2 kgf) | 11 g/10 menit | ASTM D1238 | ||
Laju Penyerapan Air(23 SBP;jenuh) | 0.17 % | ISO 62-1 | ||
Laju Penyerapan Kelembapan(50% RH;23 SBP C) | 0.07 % | ISO 62 | ||
Laju cair, (1.2 kg; pada 300 SBP) | 10 cm³/10 mnt | ISO 1133 | ||
Mekanis | Nilai nominal | Metode Pengujian | ||
Izod Impact (dampak Izod) berbentuk zod, bertakik | ||||
SBP 23 | 766 J/m | ASTM D256 | ||
C | 640 J/m | ASTM D256 | ||
80*10*4;23 SBP C | 56 kJ/m² | ISO 180/1A | ||
80*10*4;-30 SBP | 46 KJ/m² | ISO 180/1A | ||
Pengaruh Dart, Total Energy(23 SBP) | 68 J | ASTM D3763 | ||
Pengaruh besar C Humph, V-bertakik(23 SBP C;Edgew;80*10*4;sp =62 mm 0) | 55 kJ/m² | ISO 179 1eA | ||
Tekanan tensil, hasil | ||||
50 mm/mnt;Tipe I | 52 MPa | ASTM D638 | ||
50 mm/mnt | 52 MPa | ISO 527 | ||
Tekanan tensil, Pelepas | ||||
50 mm/mnt;Tipe I | 54 MPa | ASTM D638 | ||
50 mm/mnt | 47 MPa | ISO 527 | ||
Ketegangan tensil, yield | ||||
50 mm/mnt;Tipe I | 5 % | ASTM D638 | ||
50 mm/mnt | 5 % | ISO 527 | ||
Ketegangan tensil, Pemecahan | ||||
50 mm/mnt;Tipe I | 84 % | ASTM D638 | ||
50 mm/mnt | 75 % | ISO 527 | ||
Modulus tensil | ||||
50 mm/mnt | 2030 MPa | ASTM D638 | ||
1 mm/mnt | 2000 MPa | ISO 527 | ||
Fleksibilitas fleksibilitas | ||||
1.3 mm/mnt;50 mm;span | 86 MPa | ASTM D790 | ||
2 mm/mnt | 83 MPa | ISO 178 | ||
Fleksibilitas selaput otak | ||||
1.3 mm/mnt;50 mm;span | 2050 MPa | ASTM D790 | ||
2 mm/mnt | 2110 MPa | ISO 178 | ||
Termal | Nilai nominal | Metode Pengujian | ||
UL dikenal (0.4 mm) | HB | UL 94 | ||
Temperatur lunak | ||||
Laju B/50 | SBP 138 | ASTM D1525 | ||
Laju B/50 | SBP 138 | ISO 306 | ||
Laju B/120 | SBP 146 | ISO 306 | ||
Suhu Defleksi panas[HDT], tidak disGrup(3.2 mm;1.82 MPa) | SBP 121 | ASTM D648 | ||
CTE, Flow | ||||
SBP - 40 - 40 | 7,0E-05 1/ C | ASTM E831 | ||
SBP - 40 - 40 | 7,0E-05 1/ C | ISO 11359-2 | ||
CTE, XFlow | ||||
SBP - 40 - 40 | 6.7e-05 1/ C | ASTM E831 | ||
SBP - 40 - 40 | 8,2E-05 1/ C | ISO 11359-2 | ||
HDT/AF(1.8) | SBP 118 | ISO 75/AF | ||
Indeks suhu relatif, Elec | SBP 80 | UL 746B | ||
Indeks suhu relatif, Mekanis dengan dampak | SBP 80 | UL 746B | ||
Indeks suhu relatif, Mekanis tanpa dampak | SBP 80 | UL 746B | ||
Sedang memproses | Nilai nominal | |||
Temperatur pengeringan<injeksi> | SBP 120 | |||
Waktu pengeringan<injeksi> | 3 - 4 jam | |||
Kandungan Kelembapan Maksimum<injeksi> | 0.02 % | |||
Temperatur larut<injeksi> | SBP - 315 - 295 | |||
Suhu nozzle<injeksi> | SBP - 310 - 290 | |||
Temperatur Depan, Zona 3<injeksi> | SBP - 315 - 295 | |||
Temperatur Tengah, Zona 2<injeksi> | SBP - 305 - 280 | |||
Temperatur Belakang, Zona 1<injeksi> | SBP - 280 - 260 | |||
Temperatur Hopper<injeksi> | SBP - 80 - 60 | |||
Suhu mold<injeksi> | SBP - 95 - 70 |