Feature: | Plastics |
---|---|
CAS No.: | 32131-17-2 |
Formula: | C36h66n6o6 |
EINECS: | 618-371-8 |
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Pemasok dengan izin usaha terverifikasi
Deskripsi Produk | |||
Kaca 30 % diperkuat, Aliran Tinggi, bebas Halogen dan bebas fosfor merah | |||
Umum | |||
Formulir | Pelet resin | ||
Filler | 30% Serat kaca | ||
Fosfor Merah bebas Fitur |
Proses Prosesor Non-Bromnt & Non-Excellent memproses api Klorinasi | ||
Fisik | Nilai nominal | Metode Pengujian | |
Kerapatan /Gravitasi tertentu | 1.43 g/cm³ | ISO 1183 | |
Aliran spiral, Tekanan injeksi 1 mm;800 bar 1 mm;1,0e+3 bilah 1 mm;1,2e+3 bar |
8.70 cm 10.4 cm 12.1 cm |
||
Molding Shrkhage, di seluruh Flow | 1.3 % | ISO 294-4 | |
Molding Shrkhage, Flow | 0.28 % | ISO 294-4 | |
Penyerapan Air (24 jam;23 SBP) | 1.0 % | ISO 62 | |
Laju Penyerapan Air, Saturasi (23 SBP) | 4.9 % | ISO 62 | |
Penyerapan air, Keseimbangan (50% RH;23 SBP) 1.6% ISO 62 |
Mekanis | Nilai nominal | Metode Pengujian |
Modulus tensil SBP - 1 SBP 100 SBP 120 SBP 140 SBP 160 |
11000 MPa 11000 MPa 1130 MPa 5800 MPa 5300 MPa 4800 MPa 4600 MPa |
ISO 527-2 |
Tekanan tensil, Pelepas SBP - 1 SBP 100 SBP 120 SBP 140 SBP 160 |
150 MPa 140 MPa 200 MPa 87.0 MPa 79.0 MPa 72.0 MPa 66.0 MPa |
ISO 527-2 |
Ketegangan tensil, Pemecahan SBP - 1 SBP 120 SBP 140 SBP 160 |
2.8 % 2.6 % 3.0 % 5.4 % 5.7 % 6.0 % |
ISO 527-2 |
Fleksibilitas selaput otak | 9450 MPa | ISO 178 |
Stres fleksibilitas | 225 MPa | ISO 178 |
Daya tahan bertakik (23 SBP C) | 10 kJ/m² | ISO 179 1eA |
Charpy tak Berdampak taktaktakis (23 SBP) | 68 kJ/m² | ISO 179 1eU |
Termal | Nilai nominal | Metode Pengujian |
Suhu Defleksi panas, tak disnetasikan(1.8 MPa) | SBP 247 | ISO 75-2/A |
Suhu Transisi Kaca(10 SBP/mnt) | SBP 60.0 | ISO 11357-2 |
Uji Tekanan Bola(255 SBP) | Lulus | IEC 60695-10-2 |
CLTE, Aliran | 2.1E-5 cm/cm/ C | ISO 11359-2 |
CLTE, transversal(0.75 mm) | 6,7E-5 cm/cm/ C | ISO 11359-2 |
Klasifikasi keterbacaan Flammungkin 3 mm |
V-0 V-0 |
IEC 60695-11-10, - 20 |
Indeks Flamabilitas Kabel bersinar 0.4 mm 3 mm |
SBP 960 SBP 960 |
IEC 60695-2-12 |
Temperatur Pengapian Kabel Pijar [GWIT] 0.4 mm 3 mm |
SBP 800 SBP 825 |
IEC 60695-2-13 |
Kelistrikan | Nilai nominal | Metode Pengujian |
Resistivitas permukaan | > 1,0E+15 Ohm | IEC 60093 |
Kepekaan volume | > 1,0E+15 Ohm· cm | IEC 60093 |
Kekuatan listrik | 41 kV/mm | IEC 60243-1 |
Aktivitas relatif 100 Hz 1,0e+6 Hz 1,0e+9 Hz |
4.24 3.87 3.60 |
IEC 60250 |
Faktor menghilangkan 100 Hz 1,0e+6 Hz 1,0e+9 Hz |
0.011 0.015 0.010 |
IEC 60250 |
Indeks Pelacakan perbandingan | 600 V. | IEC 60112 |
Sedang memproses | Nilai nominal | |
Penunu Point (10 SBP/mnt) | SBP 260 |