Feature: | Plastics |
---|---|
CAS No.: | 63440-93-7 |
Formula: | C24h24o8 |
EINECS: | 618-371-8 |
Material: | Polybutylene Terephthalate/PBT |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Pemasok dengan izin usaha terverifikasi
Umum | |||
Formulir | Pelet resin | ||
Fitur |
Bahan kimia tahan luar ruangan | Proses memproses dengan sangat baik api Non-Bromencated & Non- Klorida Retardant |
Resistansi Hidolisis Tidak Dilaminasi |
Penggunaan | Consumer Healthcare Electrical (Kelistrikan Konsumen) Membangun dan Konstruksi Hidrologis dan Energi |
||
Fisik | Nilai nominal | Metode Pengujian | |
Kerapatan/Gravitasi tertentu | 1.19 1.2 g/cm³ |
ASTM D792 ISO 1183 |
|
Laju Aliran cair[MFR](260 SBP;2.16 kgf) | 16 g/10 menit | ASTM D1238 | |
Laju Penyerapan Air(23 SBP;jenuh) | 0.2 % | ISO 62-1 | |
Laju Penyerapan Kelembapan(50% RH;23 SBP C) | 0.1 % | ISO 62 | |
Laju cair, (2.16 kg; pada 260 SBP) | 15 cm³/10 mnt | ISO 1133 |
Mekanis | Nilai nominal | Metode Pengujian |
Izod Impact (dampak Izod) berbentuk zod, bertakik SBP 23 C |
500 J/m 100 J/m |
ASTM D256 |
Pengaruh Dart, Total Energy(23 SBP) | 65 J | ASTM D3763 |
Kekuatan benturan Izod Bertakik Terpotong;80*10*3;23 SBP C 0 Terpotong;80*10*3;-30 SBP C 0 |
20 kJ/m² 10 kJ/m² |
ISO 180/1A |
C dampaknya, V-bertakik SBP 23 C;Edgew;80*10*3;sp =62mm 0 C;;80*10*3;sp =62mm 0 |
20 kJ/m² 10 kJ/m² |
ISO 179 1eA |
Tekanan tensil, hasil | ||
50 mm/mnt;Tipe I | 65 MPa | ASTM D638 |
50 mm/mnt | 65 MPa | ISO 527 |
Tekanan tensil, Pelepas | ||
50 mm/mnt;Tipe I | 58 MPa | ASTM D638 |
50 mm/mnt | 50 MPa | ISO 527 |
Ketegangan tensil, yield | ||
50 mm/mnt;Tipe I | 4.1 % | ASTM D638 |
50 mm/mnt | 4 % | ISO 527 |
Ketegangan tensil, Pemecahan | ||
50 mm/mnt;Tipe I | 100 % | ASTM D638 |
50 mm/mnt | 90 % | ISO 527 |
Modulus tensil | ||
50 mm/mnt | 2950 MPa | ASTM D638 |
1 mm/mnt | 2530 MPa | ISO 527 |
Fleksibilitas fleksibilitas | ||
1.3 mm/mnt;50 mm;span | 104 MPa | ASTM D790 |
2 mm/mnt | 96 MPa | ISO 178 |
Fleksibilitas selaput otak | ||
1.3 mm/mnt;50 mm;span | 2750 MPa | ASTM D790 |
2 mm/mnt | 2500 MPa | ISO 178 |
Termal | Nilai nominal | Metode Pengujian |
Temperatur Pengapian Kabel Pijar [GWIT] 3 mm 2 mm 1.5 mm 0.75 mm |
SBP 800 SBP 800 SBP 800 SBP 800 |
IEC 60695-2-13 |
Indeks Flamabilitas Kabel bersinar 3 mm 2 mm 1.5 mm 0.75 mm |
SBP 960 SBP 960 SBP 960 SBP 960 |
IEC 60695-2-12 |
Temperatur lunak Laju B/50 Laju B/50 Laju B/120 |
SBP 106 SBP 110 SBP 113 |
ASTM D1525 ISO 306 ISO 306 |
Suhu Defleksi panas[HDT], tidak disGrup 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa 1.82 MPa;6.4 mm |
SBP 100 SBP 89 SBP 99 |
ASTM D648 |
CTE, Flow SBP - 40 - 40 SBP - 40 - 40 |
5,3E-05 1/ C 5,4E-05 1/ C |
ASTM E831 ISO 11359-2 |
CTE, XFlow SBP - 40 - 40 SBP - 40 - 40 |
6,3e-05 1/ C 6.2e-05 1/ C |
ASTM E831 ISO 11359-2 |
Uji Tekanan Bola (75 2 C +/- C) | Lulus | IEC 60695-10-2 |
HDT/AF(1.8) | SBP 93 | ISO 75/AF |
Indeks suhu relatif, Elec | SBP 90 | UL 746B |
Indeks suhu relatif, Mekanis dengan dampak | SBP 90 | UL 746B |
Indeks suhu relatif, Mekanis tanpa dampak | SBP 90 | UL 746B |
Kelistrikan | Nilai nominal | Metode Pengujian |
Indeks Pelacak komparatif, CTI | PLC 3 | UL 746A |
Pengapian kabel-panas, HWI(0.75 mm) | PLC 3 | UL 746A |
Pengapian Busur Amp Tinggi, HAI (0.75 mm) | PLC 0 | UL 746A |
Sedang memproses | Nilai nominal | |
Temperatur pengeringan<injeksi> | SBP 90 | |
Waktu pengeringan<injeksi> | 4 jam | |
Kandungan Kelembapan Maksimum<injeksi> | 0.04 % | |
Temperatur larut<injeksi> | SBP - 300 - 270 | |
Suhu nozzle<injeksi> | SBP - 300 - 265 | |
Temperatur Depan, Zona 3<injeksi> | SBP - 300 - 265 | |
Temperatur Tengah, Zona 2<injeksi> | SBP - 300 - 260 | |
Temperatur Belakang, Zona 1<injeksi> | SBP - 300 - 260 | |
Temperatur Hopper<injeksi> | SBP - 80 - 60 | |
Suhu mold<injeksi> | SBP - 90 - 60 | |
Tekanan Balik<injeksi> | 0.3 - 0.7 MPa | |
Kecepatan sekrup <injeksi> | 40 - 70 rpm | |
Bidik ke Ukuran Silinder<injeksi> | 40 - 80 % | |
Kedalaman Ventilasi <injeksi> | 0.038 - 0.076 mm |