Feature: | Oxidative Degradable |
---|---|
CAS No.: | 32131-17-2 |
Formula: | (C12h22n2o2)N |
EINECS: | 211-024-8 |
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Pemasok dengan izin usaha terverifikasi
Pelumas resin Pelet Alir 4T 30% Kaca Reinforcedmalah untuk aplikasi Elektrik
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-konduktor nilon
Deskripsi Produk | |||
Kaca 30% diperkuat, PA4T, untuk aplikasi E&E, Aliran yang baik | |||
Umum | |||
Formulir | Pelet resin | ||
Filler | 30% Serat kaca | ||
Fitur | Proses memproses yang sangat baik | ||
Kartu Kuning UL E47960-100921605 | |||
Penggunaan | Kelistrikan | ||
Fisik | Nilai nominal | Metode Pengujian | |
Kerapatan, kering | 1.43 g/cm³ | ISO 1183 | |
Kering: Molding | Shrrinkage, seberang Flow | 1.3 % | ISO 294-4 |
Kering: Molding | Shrrinkage, Flow | 0.40 % | ISO 294-4 |
Kering: Penyerapan Air, Keseimbangan (50% RH;23 SBP) | 2.1 % | ISO 62 | |
Mekanis | Nilai nominal | Metode Pengujian | |
Kering: Modulus tensil SBP 120 SBP 160 SBP 200 |
11000 MPa 8000 MPa 5000 MPa 5000 MPa |
ISO 527-2 | |
Kering: Tekanan tensil, Pelepas SBP 120 SBP 160 SBP 200 |
180 MPa 130 MPa 90.0 MPa 75.0 MPa |
ISO 527-2 | |
Kering: Ketegangan tensil, Pemecahan SBP 120 SBP 160 SBP 200 |
2.0 % 2.8 % 4.6 % 5.8 % |
ISO 527-2 | |
Kering: Fleksibilitas Modal SBP 160 SBP 200 |
10000 MPa 5000 MPa 4000 MPa |
ISO 178 | |
Kering: Fleksibilitas | 290 MPa | ISO 178 | |
Kering: Charpy Nottakic Impact Strength (23 SBP) | 10 kJ/m² | ISO 179 1eA | |
Kering: Charpy Impact Strength ( SBP 23 - 1) | 55 kJ/m² | ISO 179 1eU | |
Termal | Nilai nominal | Metode Pengujian | |
Kering: Suhu Defleksi panas, tak disnetasikan(1.8 MPa) | SBP 305 | ISO 75-2/A | |
Kering: Suhu Penpelelehan (10 SBP/mnt) | SBP 325 | ISO 11357-3 | |
Kering: CLTE, Aliran | 3,0E-5 cm/cm/C | ASTM D696 | |
Kering: CLTE, transversal | 5,0E-5 cm/cm/ C | ASTM D696 | |
Kering: Indeks Termal - 5000 jam | SBP 174 | IEC 60216 | |
Kering: Klasifikasi Flammatility 0.8 mm 1.5 mm |
HB HB |
IEC 60695-11-10, - 20 |
|
Kelistrikan | Nilai nominal | Metode Pengujian | |
Kering: Kepekaan volume | > 1,0E+15 Ohm ·cm | IEC 60093 | |
Kondisi: Resistivitas volume | > 1,0E+15 Ohm ·cm | IEC 60093 | |
Kering: Kekuatan Listrik | 33 kV/mm | IEC 60243-1 | |
Kondisi: Kekuatan Listrik | 33 kV/mm | IEC 60243-1 | |
Kering: Kepekaan relatif 100 Hz 1,0e+6 Hz 1,0e+9 Hz 1,0e+10 Hz |
5.00 4.50 3.90 3.80 |
IEC 60250 | |
Kondisi: Kerja relatif 100 Hz 1,0e+6 Hz 1,0e+9 Hz 1,0e+10 Hz |
5.00 4.50 4.00 3.90 |
IEC 60250 | |
Pengeringan : Indeks pembanding | 600 V. | IEC 60112 | |
Kondisi: Indeks komparasi | 600 V. | IEC 60112 |