Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
EINECS: | 618-371-8 |
Material: | Polycarbonates/PC |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Pemasok dengan izin usaha terverifikasi
Flame retant Black color LDS Laser Direct strukturisasi Merah Freefus Freee
https://forever-plastics.en.made-in-china.com/product-list-1.html
Deskripsi Produk | ||||
LDS ( Laser Direct struktur), penghambat api (Non br & Non P), Warna hitam saja | ||||
Umum | ||||
Formulir | Pelet resin | |||
Filler | Pengisi kepemilikan | |||
Fitur | Lemak Laser Markable |
Non-Bromnt Free Fosfor Merah | ||
Kartu Kuning UL | E340159-100746645 | |||
Menggunakan struktur langsung Laser | Kasus ponsel | |||
Fisik | Nilai nominal | Metode Pengujian | ||
Kerapatan/Gravitasi tertentu | 1.26 g/cm³ | ISO 1183 | ||
Laju Aliran Massa cair, MFR(260 SBP - 5 kg) | 8.0 g/10 menit | ISO 1133 | ||
Laju Aliran-Volume cair, MVR(260 SBP;5 kg) | 8.00 cm³/10 mnt | ISO 1133 | ||
Molding Shrkhage, di seluruh Flow | 0.40 - 0.60 % | Metode Internal | ||
Molding Shrkhage, Flow | 0.40 - 0.60 % | Metode Internal | ||
Laju Penyerapan Air, Saturasi(23 SBP) | 0.35 % | ISO 62 | ||
Mekanis | Nilai nominal | Metode Pengujian | ||
Modulus tensil | 2200 MPa | ISO 527-2/1 | ||
Tekanan tensil, hasil | 52.0 MPa | ISO 527-2/50 | ||
Ketegangan tensil, yield | 5.0 % | ISO 527-2/50 | ||
Ketegangan tensil, Pemecahan | > 50 % | ISO 527-2/50 | ||
Fleksibilitas selaput tubuh (2 mm/mnt) | 2300 MPa | ISO 178 | ||
Stres fleksibilitas fleksibilitas fleksibilitas (2 mm/mnt) | 80.0 MPa | ISO 178 | ||
C memiliki kekuatan benturan bertakik C SBP 23 |
30 kJ/m² 55 kJ/m² |
ISO 179 | ||
Kekuatan dampak tidak bertakik C SBP 23 |
Tanpa Pemisah Tanpa Pemisah |
ISO 179 | ||
Kekuatan benturan Izod Bertakik -20 C SBP 23 |
40 kJ/m² 60 kJ/m² |
ISO 180/4A | ||
SBP - instrumented instrumented Energy (SBP 23) | 35.0 J | ISO 6603-2 | ||
Termal | Nilai nominal | Metode Pengujian | ||
Suhu Defleksi panas, tak disnetasikan(1.8 MPa) | SBP 122 | ISO 75-2/A | ||
Temperatur lunak | SBP 144 | ISO 306 | ||
CLTE, Aliran | 6,0E-5 cm/cm/ C | ISO 11359-2 | ||
CLTE, transversal | 6,5E-5 cm/cm/ C | ISO 11359-2 | ||
Tetapan kebakaran 0.5 mm 1.5 mm 3 mm |
HB V-0 5VB |
UL 94 | ||
Kelistrikan | Nilai nominal | Metode Pengujian | ||
Resistivitas permukaan | > 1,0E+15 Ohm | IEC 60093 | ||
Kepekaan volume | > 1,0E+15 Ohm ·cm | IEC 60093 | ||
Konstanta dielektrik(1,0e+6 Hz) | 3.00 | IEC 60250 | ||
Faktor disipasi(1,0e+6 Hz) | 05.0E-3 | IEC 60250 | ||
Sedang memproses | Nilai nominal | |||
Temperatur pengeringan - pengering Udara panas<injeksi> | SBP - 120 - 100 | |||
Waktu pengeringan - pengering Udara panas<injeksi> | 4.0 - 6.0 jam | |||
Temperatur Belakang<injeksi> | SBP - 300 - 270 | |||
Suhu Tengah<injeksi> | SBP - 300 - 270 | |||
Temperatur Depan<injeksi> | SBP - 300 - 270 | |||
Suhu nozzle<injeksi> | SBP - 300 - 270 | |||
Suhu mold<injeksi> | SBP - 120 - 80 |
Forever Co.,Ltd