CAS No.: | 9003-07-0 |
---|---|
Formula: | C3h6 |
EINECS: | Nonh for All Modes of Transport |
Color: | Black |
formulir: | kemungkinan kecil resin |
bahan kimia: | polipropilena |
Pemasok dengan izin usaha terverifikasi
Deskripsi Produk | |||
Kaca 20% diperkuat secara kimia ; nilainya didasarkan pada material yang alami atau hitam kecuali dinyatakan lain. | |||
Umum | |||
Formulir | Pelet resin | ||
Filler | 20% Serat kaca | ||
Fisik | Nilai nominal | Metode Pengujian | |
Gravitasi spesifik | 1.04 g/cm³ | ASTM D792 | |
Konten Filler | 20.0 % | ASTM D2584 | |
Mold Linier Shrrinkage | 0.1 - 0.4 % | ASTM D955 | |
Mold Linier Shrrinkage, transversal | 0.4 - 0.8 % | ASTM D955 | |
Aliran meleleh | 10.0 g/10 menit | ASTM D1238 | |
Mekanis | Nilai nominal | Metode Pengujian | |
Kekuatan tensil, hasil | 52.0 MPa | ASTM D638 | |
Naskh dalam Pronh | 4.00 % | ASTM D638 | |
Kekuatan fleksibilitas | 86.0 MPa | ASTM D790 | |
Fleksibilitas selaput otak | 3450 MPa | ASTM D790 | |
Dampak Izod, bertakik (Ketebalan bertakik; 3.17 mm) | 133 J/m | ASTM D256 | |
Termal | Nilai nominal | Metode Pengujian | |
Suhu defleksi | ASTM D648 | ||
Ketebalan; 3.17 mm;Tekanan; 0.46 MPa | SBP 146 | ||
Ketebalan; 3.17 mm;Tekanan; 1.8 MPa | SBP 132 | ||
Flammaility, UL94 Ketebalan; 3 mm; semua Ketebalan Pengakuan Warna; 1.5 mm; semua Pengenalan Warna |
HB HB |
||
Sedang memproses | Nilai nominal | ||
Temperatur barel Belakang | SBP - 249 - 204 | ||
Suhu barrel Tengah | SBP - 260 - 216 | ||
Temperatur barel Depan | SBP - 260 - 216 | ||
Suhu nozzle | SBP - 260 - 216 | ||
Temperatur Rombak | SBP - 260 - 216 | ||
Suhu mold | SBP - 60.0 - 26.7 | ||
Tekanan Balik | 0.345 - 0.689 MPa |