| Fitur ini: | Oksidatif Dedapat dimutakhirkan |
|---|---|
| Material: | Poliamida(Nilon 6.66)/PA |
| Penggunaan: | Plastk umum, Plastik teknik, Plastik khusus |
| Warna: | Putih |
| rantai utama molekuler: | polimer rantai karbon |
| bahan kimia: | polikarbonat |
Pemasok dengan izin usaha terverifikasi
Pemasok yang Diaudit Factory direct sale pa6 gf30 Polyamide Virgin Resin PA6 Engineering plastics PA6 gf30 / raw material nylon granules gf35/gf25
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html
Ultramid KB30564 is an impact-modified, pigmented black, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity. Applications Typical applications include automotive airbag housings and half-shells for suitcases
| Product Description | ||||
| Ultramid KB30564 is an impact-modified, pigmented black, 30% glass fiber reinforced injection molding PA6 grade for industrial items having very high impact strength and rigidity. Applications Typical applications include automotive airbag housings and half-shells for suitcases. | ||||
| General | ||||
| Form | Resin Pellets | |||
| Filler | 30 % Glass Fiber | |||
| Feature | High Mechanical Strength High Impact Fuel Resistant And Rigidity Ec (Reach) |
|||
| UL Yellow Card | ||||
| Industrial Applications Housing |
Luggage | Automotive | ||
| Physical | Nominal Value | Test Method | ||
| Density | 1.33 g/cm³ | ISO 1183 | ||
| Melt Volume-Flow Rate, MVR(275 °C;5 kg) | 25 cm³/10 min | ISO 1133 | ||
| Water Absorption, Saturation(23 °C) | 6.2 % | ISO 62 | ||
| Water Absorption, Equilibrium(50% RH;23 °C) | 2.0 % | ISO 62 | ||
| Mechanical | Nominal Value | Test Method | ||
| Tensile Modulus(23 °C) | 8800 MPa | ISO 527-2 | ||
| Tensile Stress, Break(23 °C) | 150 MPa | ISO 527-2 | ||
| Tensile Strain, Break(23 °C) | 3.2 % | ISO 527-2 | ||
| Flexural Modulus(23 °C) | 7900 MPa | ISO 178 | ||
| Charpy Notched Impact Strength -30 °C 23 °C |
8.0 kJ/m² 15 kJ/m² |
ISO 179 | ||
| Notched Izod Impact Strength -30 °C 23 °C |
8.0 kJ/m² 16 kJ/m² |
ISO 180 | ||
| Thermal | Nominal Value | Test Method | ||
| Heat Deflection Temperature, Unannealed(1.8 MPa) | 205 °C | ISO 75-2/A | ||
| Melting Temperature, DSC | 220 °C | ISO 3146 | ||
| Processing | Nominal Value |
| Drying Temperature<Injection> | 80 °C |
| Drying Time<Injection> | 2.0 - 4.0 hr |
| Suggested Max Moisture<Injection> | 0.080 % |
| Rear Temperature<Injection> | 245 - 275 °C |
| Middle Temperature<injection> | 260 - 285 °C |
| Front Temperature<Injection> | 270 - 295 °C |
| Nozzle Temperature<Injection> | 270 - 295 °C |
| Processing Temp, Melt<Injection> | 270 - 295 °C |
| Mold Temperature<Injection> | 80 - 95 °C |
| Injection Pressure<Injection> | 3.50 - 12.5 MPa |
| Injection Rate<Injection> | Fast |
Forever Co.,Ltd