Product Description | ||||
PBT 5515F-104 is a 15% glass fiber reinforced and flame retardant injection molding grade. (Halogen and Antimony Free) | ||||
General | ||||
Form | Resin Pellets | |||
Filler | 15 % Glass Fiber | |||
Feature | Non-Brominated & Non- Antimony Free Chlorinated Flame | High Impact | ||
Retardant | ||||
Physical | Nominal Value | Test Method | ||
Density | 1.40 g/cm³ | ISO 1183 | ||
Molding Shrinkage, Across Flow | 0.90 - 1.2 % | ISO 294-4 | ||
Molding Shrinkage, Flow | 0.30 - 0.60 % | ISO 294-4 | ||
Water Absorption, Equilibrium(50% RH;23 °C) | 0.20 % | ISO 62 | ||
Mechanical | Nominal Value | Test Method | ||
Tensile Stress, Break | 75.0 MPa | ISO 527-2 | ||
Tensile Strain, Break | 2.5 % | ISO 527-2 | ||
Flexural Modulus | 5200 MPa | ISO 178 | ||
Flexural Stress | 115 MPa | ISO 178 | ||
Charpy Notched Impact Strength(23 °C) | 6.7 kJ/m² | ISO 179/1eA | ||
Thermal | Nominal Value | Test Method | ||
Deflection Temperature Under Load, Unannealed 0.45 MPa 1.8 MPa |
205 °C 190 °C |
ISO 75-2/B ISO 75-2/A |
||
Melting Temperature(10 °C/min) | 225 °C | ISO 11357-3 | ||
Flame Rating(0.8 mm) | V-0 | UL 94 | ||
Electrical | Nominal Value | Test Method | ||
Surface Resistivity | 1.0E+13 ohms | IEC 60093 | ||
Volume Resistivity | > 1.0E+15 Ohms·cm | IEC 60093 | ||
Electric Strength(2 mm) | 23 kV/mm | IEC 60243-1 | ||
Comparative Tracking Index | 450 V | IEC 60112 |
Processing | Nominal Value |
Drying Temperature<Injection> | 120 - 140 °C |
Drying Time<Injection> | 3.0 - 4.0 hr |
Suggested Max Moisture<Injection> | 0.040 % |
Processing Temp, Melt<Injection> | 240 - 270 °C |
Mold Temperature<Injection> | 40 - 80 °C |