Feature: | Oxidative Degradable |
---|---|
Material: | Polyamide(Nylon 6.66)/PA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Injection |
Color: | White |
Pemasok dengan izin usaha terverifikasi
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html30% Glass Reinforced, Heat Stabilized, Flame Retardant, High Flow
General | |||
Form | Resin Pellets | ||
Filler | 30 % Glass Fiber | ||
Feature | Flame Retardant | ||
Uses Automotive Engineered Electron & electric parts | |||
Physical | Nominal Value | Test Method | |
Specific Gravity | 1.41 g/cm³ | ISO 1183 | |
Mold Shrinkage, MD | 0.3 % | ISO 294-4 | |
Mold Shrinkage, TD | 0.7 % | ISO 294-4 | |
Mechanical | Nominal Value | Test Method | |
Tensile Strength(20 mm/min) | 135 MPa | ISO 527-2 | |
Elongation at Break(20 mm/min) | 2.6 % | ISO 527-2 | |
Flexural Strength(2 mm/min) | 185 MPa | ISO 178 | |
Flexural Modulus(2 mm/min) | 7800 MPa | ISO 178 | |
Notched Izod Impact Strength | 10 kJ/m² | ISO 180 | |
Thermal | Nominal Value | Test Method | |
Heat Deflection Temperature | ISO 75 | ||
0.45 MPa | 210 °C | ||
1.82 MPa | 200 °C | ||
Flammability(1.6 mm) | V-0 | UL94 | |
Processing | Nominal Value | ||
Drying Temperature | 95 - 110 °C | ||
Drying Time | 2 - 4 h | ||
Mold Temperature | 65 - 100 °C | ||
Melt Temperature | 230 - 265 °C |