| Feature: | Oxidative Degradable |
|---|---|
| Material: | Polyamide(Nylon 6.66)/PA |
| Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
| Plastic Properties After Heated: | Thermoplastic Plastics |
| Plastic Forming Method: | Injection |
| Color: | White |
Pemasok dengan izin usaha terverifikasi
Pemasok yang Diaudit | Product Description | |||||
| LEXAN LUX9132C Polycarbonate (PC) resin is a non-filled, injection moldable grade. This non-chlorinated, non- brominated flame retardant PC has an UL-94 V0 rating at 1.5 mm, high flow capability and is UV stabilized providing additional weathering capability. LEXAN LUX9132C is available in diffusion colors. | |||||
| General | |||||
| Form | Resin Pellets | ||||
Feature |
F1 Non-Chlorinated |
Excellent Processability | Non-Brominated & Non- Chlorinated Flame | ||
| Retardant Diffusive |
|||||
| UL Yellow Card E207780-101256996 | |||||
| Uses | Lighting Diffusers | Electrical | |||
| Physical | Nominal Value | Test Method | |||
| Specific Gravity | 1.19 | ASTM D792 | |||
| Mold Shrinkage, Flow(3.2 mm) | 0.55 - 0.75 % | SABIC Method | |||
| Mold Shrinkage, XFlow(3.2 mm) | 0.6 - 0.8 % | SABIC Method | |||
| Melt Flow Rate[MFR](300 °C;1.2 kgf) | 18 g/10min | ASTM D1238 | |||
| Density | 1.2 g/cm³ | ISO 1183 | |||
| Water Absorption(23 °C;saturated) | 0.13 % | ISO 62-1 | |||
| Moisture Absorption(50% RH;23 °C) | 0.11 % | ISO 62 | |||
| Melt Volume Rate, MVR(1.2 kg;MVR at 300 °C) | 17 cm³/10 min | ISO 1133 | |||
| Mechanical | Nominal Value | Test Method | |||
| Izod Impact, Unnotched 23 °C -30 °C |
NB J/m NB J/m |
ASTM D4812 | |||
| Izod Impact, Notched 23 °C -30 °C |
100 J/m 85 J/m |
ASTM D256 | |||
| Instrumented Dart Impact, Total Energy(23 °C) | 65 J | ASTM D3763 | |||
| Unnotched Izod Impact Strength unnotched;80*10*3;23 °C 0 unnotched;80*10*3;-30 °C 0 |
NB kJ/m² NB kJ/m² |
ISO 180/1U | |||
| Notched Izod Impact Strength notched;80*10*3;23 °C 0 notched;80*10*3;-30 °C 0 |
10 kJ/m² 9 kJ/m² |
ISO 180/1A |
| Charpy Impact, V-Notched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
10 kJ/m² 9 kJ/m² |
ISO 179 1eA |
| Charpy Impact, Unnotched 23 °C;Edgew;80*10*3;sp=62mm 0 -30 °C;Edgew;80*10*3;sp=62mm 0 |
NB kJ/m² NB kJ/m² |
ISO 179 1eU |
| Tensile Stress, Yield 50 mm/min;Type I 50 mm/min |
67 MPa 63 MPa |
ASTM D638 ISO 527 |
| Tensile Stress, Break 50 mm/min;Type I 50 mm/min |
54 MPa 57 MPa |
ASTM D638 ISO 527 |
| Tensile Strain, Yield 50 mm/min;Type I 50 mm/min |
6 % 6 % |
ASTM D638 ISO 527 |
| Tensile Strain, Break 50 mm/min;Type I 50 mm/min |
80 % 73 % |
ASTM D638 ISO 527 |
| Tensile Modulus 50 mm/min 1 mm/min |
2400 MPa 2300 MPa |
ASTM D638 ISO 527 |
| Flexural Stress, Yield 1.3 mm/min;50 mm;span 2 mm/min |
103 MPa 96 MPa |
ASTM D790 ISO 178 |
| Flexural Modulus 1.3 mm/min;50 mm;span 2 mm/min |
2400 MPa 2400 MPa |
ASTM D790 ISO 178 |
| Thermal | Nominal Value | Test Method |
| UL Recognized ≥ 1.5 mm ≥ 0.4 mm |
V-0 V-2 |
UL 94 |
| Glow Wire Ignition Temperature [GWIT] 3 mm 1.5 mm |
850 °C 850 °C |
IEC 60695-2-13 |
| Glow Wire Flammability Index 3 mm 1.5 mm |
960 °C 960 °C |
IEC 60695-2-12 |
| UV-light, water exposure/immersion | 1 | UL 746C |
| Vicat Softening Temperature Rate B/50 Rate B/50 Rate B/120 |
136 °C 139 °C 140 °C |
ASTM D1525 ISO 306 ISO 306 |
| Heat Deflection Temperature[HDT], Unannealed 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
130 °C 120 °C |
ASTM D648 |
| CTE, Flow -40 - 40 °C 23°C to 80°C |
6.8E-05 1/°C 7.7e-05 1/°C |
ASTM E831 ISO 11359-2 |
| CTE, XFlow -40 - 40 °C 23°C to 80°C |
7.0E-05 1/°C 8.0e-05 1/°C |
ASTM E831 ISO 11359-2 |
| Ball Pressure Test(125°C +/- 2°C) | Pass | IEC 60695-10-2 |
| HDT/Be(Edgew;120*10*4;sp=100mm; 0.45 Mpa) | 131 °C | ISO 75/Be |
| Hdt/Ae(1.8 MPa;Edgew;120*10*4;sp=100mm) | 121 °C | ISO 75/Ae |
| Relative Temp Index, Elec | 130 °C | UL 746B |
| Relative Temp Index, Mechanical with Impact | 120 °C | UL 746B |
| Relative Temp Index, Mechanical without Impact | 130 °C | UL 746B |
| Electrical | Nominal Value | Test Method |
| Comparative Tracking Index, CTI | PLC 3 | UL 746A |
| High Amp Arc Ignition, HAI(≥ 0.4 mm) | PLC 1 | UL 746A |
| Hot-wire Ignition, HWI ≥ 1.5 mm ≥ 0.4 mm |
PLC 0 PLC 3 |
UL 746A |
| Dielectric Constant, Dk(1100000000 Hz) | 2.78 | ASTM ES 7-83 |
| Dissipation Factor, Df(1100000000 Hz) | 5.6E-03 | ASTM ES 7-83 |
| Processing | Nominal Value | |
| Drying Temperature<Injection> | 120 °C | |
| Drying Time<Injection> | 3 - 4 hrs | |
| Drying Time, Cumulative<Injection> | 48 hrs | |
| Maximum Moisture Content<Injection> | 0.02 % | |
| Melt Temperature<Injection> | 280 - 305 °C | |
| Nozzle Temperature<Injection> | 275 - 300 °C | |
| Front, Zone 3 Temperature<Injection> | 280 - 305 °C | |
| Middle, Zone 2 Temperature<Injection> | 270 - 295 °C | |
| Rear, Zone 1 Temperature<Injection> | 260 - 280 °C | |
| Mold Temperature<Injection> | 70 - 95 °C | |
| Back Pressure<Injection> | 0.3 - 0.7 MPa | |
| Screw Speed<Injection> | 40 - 70 rpm | |
| Shot To Cylinder Size<Injection> | 40 - 60 % | |
| Vent Depth<Injection> | 0.025 - 0.076 mm |