Deskripsi Produk | |||||
Senyawa TERMOKOPEL KOMP MX89510 LNP TERMOKOPEL (PP) yang mengandung serat kaca 10%, bead kaca 10%. | |||||
Umum | |||||
Formulir | Pelet resin | ||||
Filler | 10% manik kaca | 10% Serat kaca | |||
Fitur | Warpage Rendah | Kekerasan yang baik | Struktural | ||
Penggunaan | Pelanggan | Kelistrikan | |||
Fisik | Nilai nominal | Metode Pengujian | |||
Kerapatan/Gravitasi tertentu | 1.02 1.01 g/cm³ |
ASTM D792 | |||
Penyerapan Kelembapan | |||||
SBP 23 C;50% RH/24 jam | 0.02 % | ASTM D570 | |||
23% RH;50 SBP | 0.02 % | ISO 62 | |||
Mold Shrrinkage, Flow(24 jam) | 0.8 - 2 % | ASTM D955 | |||
Mold Shrrinkage, XFlow(24 jam) | 0.9 - 3 % | ASTM D955 | |||
Mekanis | Nilai nominal | Metode Pengujian | |||
Izod Impact (dampak Izod), Unbertakik | |||||
SBP 23 | 368 J/m | ASTM D4812 | |||
80*10*4;23 SBP C | 22 kJ/m² | ISO 180/1U | |||
Izod Impact (dampak Izod) berbentuk zod, bertakik | |||||
SBP 23 | 21 J/m | ASTM D256 | |||
80*10*4;23 SBP C | 2 kJ/m² | ISO 180/1A | |||
Dampak Multi-aksial | 1 J | ISO 6603 | |||
Pengaruh Dart, Total Energy(23 SBP) | 4 J | ASTM D3763 | |||
Tekanan tensil, hasil | |||||
5 mm/mnt;Tipe I | 52 MPa | ASTM D638 | |||
5 mm/mnt | 50 MPa | ISO 527 | |||
Tekanan tensil, Pelepas | |||||
5 mm/mnt;Tipe I | 52 MPa | ASTM D638 | |||
5 mm/mnt | 48 MPa | ISO 527 | |||
Ketegangan tensil, yield | |||||
5 mm/mnt;Tipe I | 3 % | ASTM D638 | |||
5 mm/mnt | 2.9 % | ISO 527 | |||
Ketegangan tensil, Pemecahan | |||||
5 mm/mnt;Tipe I | 3.4 % | ASTM D638 | |||
5 mm/mnt | 3.4 % | ISO 527 | |||
Modulus tensil | |||||
50 mm/mnt | 3820 MPa | ASTM D638 | |||
1 mm/mnt | 3540 MPa | ISO 527 | |||
Fleksibilitas fleksibilitas, hasil (1.3 mm/mnt;50 mm;span) | 80 MPa | ASTM D790 | |||
Fleksibilitas selaput otak | |||||
1.3 mm/mnt;50 mm;span | 2800 MPa | ASTM D790 | |||
2 mm/mnt | 2950 MPa | ISO 178 | |||
Stres fleksibilitas | 76 MPa | ISO 178 | |||
Termal | Nilai nominal | Metode Pengujian | |||
Suhu Defleksi panas[HDT], tidak disGrup 0.45 MPa;3.2 mm 3.2 mm;1.82 MPa |
SBP 156 SBP 131 |
ASTM D648 | |||
CTE, Flow(-30 - 30 SBP) | 4.3E-05 1/ C | ASTM D696 | |||
CTE, XFlow(-30 - 30 SBP) | 1,2E-04 1/ C | ASTM D696 | |||
HDT/BF (0.45) | SBP 153 | ISO 75/BF | |||
HDT/AF(1.8) | SBP 119 | ISO 75/AF | |||
Sedang memproses | Nilai nominal | ||||
Temperatur pengeringan<injeksi> | SBP 80 | ||||
Waktu pengeringan<injeksi> | 4 jam | ||||
Temperatur larut<injeksi> | SBP - 250 - 225 | ||||
Temperatur Depan, Zona 3<injeksi> | SBP - 250 - 240 | ||||
Temperatur Tengah, Zona 2<injeksi> | SBP - 225 - 215 | ||||
Temperatur Belakang, Zona 1<injeksi> | SBP - 205 - 195 | ||||
Suhu mold<injeksi> | SBP - 50 - 30 | ||||
Tekanan Balik<injeksi> | 0.2 - 0.3 MPa | ||||
Kecepatan sekrup <injeksi> | 30 - 60 rpm |