Fitur ini: | Plastics |
---|---|
CAS No: | 9003-56-9 |
Rumus: | C45h51n3X2 |
EINECS: | 618-371-8 |
Material: | Acrimilitril-Butaena-Stie Copolimers/ABS |
Penggunaan: | Plastk umum, Plastik teknik, Plastik khusus |
Pemasok dengan izin usaha terverifikasi
Umum | ||
Dari Pelet resin | ||
Menggunakan Peralatan | Aplikasi Industri | |
Fisik | Nilai nominal | Metode Pengujian |
Kerapatan/Gravitasi tertentu | 1.04 g/cm³ | ASTM D792 |
Laju Aliran Massa cair, MFR(230 SBP - 3.8 kg) | 5.6 g/10 menit | ASTM D1238 |
Laju Aliran-Volume cair, MVR(220 SBP;10 kg) | 18 cm³/10 mnt | ISO 1133 |
Molding Shrkhage, Flow(3.2 mm) | 0.50 - 0.80 % | Metode Internal |
Viskositas melebur(240 SBP;1,0e+3 dtk. 1 | 225 Pa · | ASTM D3835 |
Mekanis | Nilai nominal | Metode Pengujian |
Modulus tensil(5 mm/mnt) | 2130 MPa | ASTM D638 |
Kekuatan tensil, hasil(5 mm/mnt;Tipe I) | 40.0 MPa | ASTM D638 |
Kekuatan tensil, liburan(5 mm/mnt;Tipe I) | 31.0 MPa | ASTM D638 |
Tensil untuk Naskh, hasil(5 mm/mnt;Tipe I) | 2.0 % | ASTM D638 |
Ketegangan yang lebih tinggi, Pemecahan(5 mm/mnt;Tipe I) | 20 % | ASTM D638 |
Fleksibilitas selaput tubuh (1.3 mm/mnt;50 mm;span) | 2200 MPa | ASTM D790 |
Kekuatan fleksibilitas, yield(1.3 mm/mnt;50 mm;span) | 68.0 MPa | ASTM D790 |
Pengaruh Izod Bertakik(23 SBP) | 290 J/m | ASTM D256 |
Pengaruh Dart, Total Energy(23 SBP) | 30.0 J | ASTM D3763 |
Termal | Nilai nominal | Metode Pengujian |
Suhu defleksi saat dimuat, tidak dapat disamai 0.45 MPa;3.2 mm 1.8 MPa;3.2 mm |
SBP 96.0 SBP 82.0 |
ASTM D648 |
Temperatur melemah Vicat (50 SBP/h;50 N;Rate A;Pemuatan 2) | SBP 98.0 | ASTM D1525 |
CLTE, Aliran(-40 - 40 SBP C) | 8,8E-5 cm/cm/ C | ASTM E831 |
CLTE, transversal(40 - 40 SBP C) | 8,8E-5 cm/cm/ C | ASTM E831 |
RTI Elektronik | SBP 60.0 | UL 746 |
RTI IMP | SBP 60.0 | UL 746 |
RTI Str | SBP 60.0 | UL 746 |
Peringkat api (1.5 mm) | HB | UL 94 |
Kelistrikan | Nilai nominal | Metode Pengujian |
Resistansi ARC, elektrode tungsten | PLC 6 | ASTM D495 |
Indeks Pelacak komparatif[CTI] | PLC 0 | UL 746 |
Pengapian Busur Amp Tinggi, HAI, Permukaan | PLC 0 | UL 746 |
Kecepatan Pelacakan Busur Tegangan Tinggi , | PLC 3 | UL 746 |
Pengapian kabel-panas, HWI | PLC 3 | UL 746 |
Sedang memproses | Nilai nominal | |
Temperatur pengeringan<injeksi> | SBP - 95 - 80 | |
Waktu pengeringan<injeksi> | 2.0 - 4.0 jam | |
Kelembapan Maks yang Disarankan<injeksi> | 0.10 % | |
Ukuran Bidikan yang Disarankan<injeksi> | 50 - 70 % | |
Temperatur Belakang<injeksi> | SBP - 210 - 190 | |
Suhu Tengah<injeksi> | SBP - 225 - 205 | |
Temperatur Depan<injeksi> | SBP - 240 - 215 | |
Suhu nozzle<injeksi> | SBP - 260 - 220 | |
Temperatur Pemrosesan, peleburan<injeksi> | SBP - 260 - 220 | |
Suhu mold<injeksi> | SBP - 70 - 50 | |
Tekanan Balik<injeksi> | 0.300 - 0.700 MPa | |
Kecepatan sekrup <injeksi> | 30 - 60 rpm | |
Kedalaman Ventilasi <injeksi> | 0.038 - 0.051 mm | |
Waktu pengeringan, Kumulatif<injeksi> | 8 jam |