Feature: | Plastics |
---|---|
CAS No.: | 25766-59-0 |
Formula: | C6h4c(CH3)2c6h4oco2-]N |
EINECS: | 618-371-8 |
Material: | Polycarbonates/PC |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Pemasok dengan izin usaha terverifikasi
Deskripsi Produk | |||
4795R adalah poly(ester) injeksi injeksi karbonat tahan panas tinggi . Api dapat dipendekkan. | |||
Umum | |||
Dari Pelet resin | |||
Memiliki Termal yang baik | |||
Menggunakan Konsumen | Kelistrikan | Bangunan dan Konstruksi | |
Fisik | Nilai nominal | Metode Pengujian | |
Kerapatan/Gravitasi tertentu | 1.2 1.2 g/cm³ |
ASTM D792 ISO 1183 |
|
Mold Shrinkage, Flow(3.2 mm) | 0.97 % | Metode | |
Mold Shrinkage, XFlow(3.2 mm) | 0.97 % | Metode | |
Laju Aliran meleleh[MFR] (meleleh Flow Rate[FR]) | ASTM D1238 | ||
SBP 330 C;2.16 kgf | 15 g/10 menit | ||
SBP 300 C;1.2 kgf | 2.5 g/10 menit | ||
Mekanis | Nilai nominal | Metode Pengujian | |
Izod Impact, Unestakuk(23 SBP) | 2140 J/m | ASTM D4812 | |
Izod Impact, bertakik (23 SBP) | 578 J/m | ASTM D256 | |
Pengaruh Dart, Energi di Puncak(23 SBP) | 73 J | ASTM D3763 | |
Pengaruh Dart, Total Energy(23 SBP) | 77 J | ASTM D3763 | |
Tekanan tensil, hasil (50 mm/mnt;Tipe I) | 68 MPa | ASTM D638 | |
Tekanan tensil, liburan (50 mm/mnt;Tipe I) | 70 MPa | ASTM D638 | |
Ketegangan tensil, yield(50 mm/mnt;Tipe I) | 7.5 % | ASTM D638 | |
Ketegangan tensil, Pemisah(50 mm/mnt;Tipe I) | 117 % | ASTM D638 | |
Modulus tensil(50 mm/mnt) | 2170 MPa | ASTM D638 | |
Tegangan fleksibilitas, break(1.3 mm/mnt;50 mm;span) | 105 MPa | ASTM D790 | |
Fleksibilitas selaput tubuh (1.3 mm/mnt;50 mm;span) | 2200 MPa | ASTM D790 | |
Termal | Nilai nominal | Metode Pengujian | |
Temperatur lembut Vicat(Laju B/50) | SBP 164 | ASTM D1525 | |
Suhu Defleksi panas[HDT], tidak disGrup | ASTM D648 | ||
0.45 MPa;3.2 mm | SBP 160 | ||
3.2 mm;1.82 MPa | SBP 147 | ||
Uji Tekanan Bola (125 2 C +/- C) | Lulus | IEC 60695-10-2 | |
Sedang memproses | Nilai nominal | ||
Temperatur pengeringan<injeksi> | SBP 120 | ||
Waktu pengeringan<injeksi> | 3 - 4 jam | ||
Waktu pengeringan, Kumulatif<injeksi> | 48 jam | ||
Kandungan Kelembapan Maksimum<injeksi> | 0.02 % | ||
Temperatur larut<injeksi> | SBP - 370 - 350 | ||
Suhu nozzle<injeksi> | SBP - 365 - 345 | ||
Temperatur Depan, Zona 3<injeksi> | SBP - 370 - 350 | ||
Temperatur Tengah, Zona 2<injeksi> | SBP - 360 - 340 | ||
Temperatur Belakang, Zona 1<injeksi> | SBP - 350 - 325 | ||
Suhu mold<injeksi> | SBP - 115 - 80 | ||
Tekanan Balik<injeksi> | 0.3 - 0.7 MPa | ||
Kecepatan sekrup <injeksi> | 40 - 70 rpm | ||
Bidik ke Ukuran Silinder<injeksi> | 40 - 60 % | ||
Kedalaman Ventilasi <injeksi> | 0.025 - 0.076 mm |