Kaca 40% memperkuat bebas Halogen api 4T dan bebas fosfor merah
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-konduktor nilon
Deskripsi Produk | ||||
Kaca 40% diperkuat, PA4T, api Retardant, bebas Halogen dan bebas dari fosfor merah | ||||
Umum | ||||
Formulir | Pelet resin | |||
Filler | 40% Serat kaca | |||
Fitur | Fosfor Merah bebas | Api Non-Brodicated & Non-Chlorinasi | ||
Kartu Kuning UL E47960-100744460 | ||||
Fisik | Nilai nominal | Metode Pengujian | ||
Kerapatan, kering | 1.55 g/cm³ | ISO 1183 | ||
Kering: Molding Shrincage, menyeberangi Flow | 0.85 % | ISO 294-4 | ||
Kering: Molding Shrincage, Flow | 0.30 % | ISO 294-4 | ||
Kering: Penyerapan Air, Keseimbangan (50% RH;23 SBP) | 1.3 % | ISO 62 | ||
Mekanis | Nilai nominal | Metode Pengujian | ||
Kering: Modulus tensil | 13500 MPa | ISO 527-2 | ||
Kondisi: Modulus ketegangan | 13500 MPa | ISO 527-2 | ||
Kering: Tekanan tensil, Pelepas | 170 MPa | ISO 527-2 | ||
Kondisi: Tekanan tensil, Pemutusan | 170 MPa | ISO 527-2 | ||
Kering: Ketegangan tensil, Pemecahan | 1.9 % | ISO 527-2 | ||
Kondisi: Ketegangan tensil, Pemecahan | 1.9 % | ISO 527-2 | ||
Kering: Fleksibilitas Modal | 14500 MPa | ISO 178 | ||
Kondisi: Fleksibilitas Modululus | 14500 MPa | ISO 178 | ||
Kering: Fleksibilitas | 280 MPa | ISO 178 | ||
Kondisi: Stres fleksibilitas | 260 MPa | ISO 178 | ||
Kering: Charpy Nottakic Impact Strength (23 SBP) | 11 kJ/m² | ISO 179 1eA | ||
Kondisi: Karakter memiliki dampak takuk(23 SBP) | 11 kJ/m² | ISO 179 1eA | ||
Kering: Charpy Impact Strength ( SBP 23 - 1) | 65 kJ/m² | ISO 179 1eU | ||
Kondisi: Charpy Unbertakik menguat(23 SBP) | 65 kJ/m² | ISO 179 1eU | ||
Termal | Nilai nominal | Metode Pengujian | ||
Kering: Suhu Defleksi panas, tak disnetasikan(1.8 MPa) | SBP 305 | ISO 75-2/A | ||
Kering: Suhu Penpelelehan (10 SBP/mnt) | SBP 325 | ISO 11357-3 | ||
Kering: CLTE, Aliran | 3,0E-5 cm/cm/C | ASTM D696 | ||
Kering: CLTE, transversal | 3,5 E-5 cm/cm/ C | ASTM D696 | ||
Kering: RTI Elec(0.35 mm) | SBP 140 | UL 746 | ||
Kering: Klasifikasi Flammatility 0.2 mm 1.5 mm |
V-0 V-0 |
IEC 60695-11-10, - 20 | ||
Kelistrikan | Nilai nominal | Metode Pengujian | ||
Kering: Kepekaan volume | > 1,0E+15 Ohm ·cm | IEC 60093 | ||
Kondisi: Resistivitas volume | > 1,0E+15 Ohm ·cm | IEC 60093 | ||
Kering: Kekuatan Listrik | 33 kV/mm | IEC 60243-1 | ||
Kondisi: Kekuatan Listrik | 33 kV/mm | IEC 60243-1 | ||
Kering: Kepekaan relatif 100 Hz 1,0e+6 Hz |
4.20 3.90 |
IEC 60250 | ||
Kondisi: Kerja relatif 100 Hz 1,0e+6 Hz |
4.20 3.90 |
IEC 60250 | ||
Pengeringan : Indeks pembanding | 600 V. | IEC 60112 |