Fitur ini: | Oksidatif Dedapat dimutakhirkan |
---|---|
CAS No: | 32131-17-2 |
Rumus: | (C12h22n2o2)N |
EINECS: | 211-024-8 |
Material: | Poliamida(Nilon 6.66)/PA |
Penggunaan: | Plastk umum, Plastik teknik, Plastik khusus |
Pemasok dengan izin usaha terverifikasi
Kaca 30% memperkuat struktur langsung (LDS)bebas Halogen Retarant Flanant Halogen yang dapat dipendekkan
https://forever-plastics.en.made-in-china.com/product/rJwRvlcdZpWD/China-Nylon-PA6-GF33-PA66-Granules-PA6-with-30GF-Polyamide-PA66-30-GF-PA6-Material.html Heat-konduktor nilon
Deskripsi Produk | ||||
Kaca 40% diperkuat, PA4T, untuk aplikasi E&E | ||||
Umum | ||||
Formulir | Resin | Pelet | ||
Filler | 40 % | Serat kaca | ||
Kartu Kuning UL E47960-100961700 | ||||
Penggunaan | Kelistrikan | |||
Fisik | Nilai nominal | Metode Pengujian | ||
Kerapatan, kering | 1.53 g/cm³ | ISO 1183 | ||
Kering: Molding Shrincage, menyeberangi Flow | 1.0 % | ISO 294-4 | ||
Kering: Molding Shrincage, Flow | 0.35 % | ISO 294-4 | ||
Kering: Penyerapan Air, Keseimbangan (50% RH;23 SBP) | 1.8 % | ISO 62 | ||
Mekanis | Nilai nominal | Metode Pengujian | ||
Kering: Modulus tensil | 13500 MPa | ISO 527-2 | ||
Kering: Tekanan tensil, Pelepas | 210 MPa | ISO 527-2 | ||
Kering: Ketegangan tensil, Pemecahan | 2.0 % | ISO 527-2 | ||
Kering: Fleksibilitas Modal | 13500 MPa | ISO 178 | ||
Kering: Fleksibilitas | 330 MPa | ISO 178 | ||
Kering: Charpy Nottakic Impact Strength (23 SBP) | 11 kJ/m² | ISO 179 1eA | ||
Kering: Charpy Impact Strength ( SBP 23 - 1) | 65 kJ/m² | ISO 179 1eU | ||
Termal | Nilai nominal | Metode Pengujian | ||
Kering: Suhu Defleksi panas, tak disnetasikan(1.8 MPa) | SBP 305 | ISO 75-2/A | ||
Kering: Suhu Penpelelehan (10 SBP/mnt) | SBP 325 | ISO 11357-3 | ||
Kering: CLTE, Aliran | 3,0E-5 cm/cm/C | ASTM D696 | ||
Kering: CLTE, transversal | 4,0E-5 cm/cm/C | ASTM D696 | ||
Kering: Klasifikasi Flammatility | IEC 60695-11-10, - 20 | |||
0.8 mm | HB | |||
1.5 mm | HB | |||
Kelistrikan | Nilai nominal | Metode Pengujian | ||
Kering: Kepekaan volume | > 1,0E+15 Ohm ·cm | IEC 60093 | ||
Kondisi: Resistivitas volume | > 1,0E+15 Ohm ·cm | IEC 60093 | ||
Kering: Kekuatan Listrik | 33 kV/mm | IEC 60243-1 | ||
Kondisi: Kekuatan Listrik | 33 kV/mm | IEC 60243-1 | ||
Kering: Kepekaan relatif 100 Hz 1,0e+6 Hz |
5.0 4.50 |
IEC 60250 | ||
Kondisi: Kerja relatif 100 Hz 1,0e+6 Hz |
5.00 4.50 |
IEC 60250 | ||
Pengeringan : Indeks pembanding | 600 V. | IEC 60112 |