Feature: | Biodegradable |
---|---|
CAS No.: | 24937-78-8 |
Formula: | (C2h4)X.(C4h6o2)Y |
EINECS: | 607-457-0 |
Material: | Ethylene-Vinyl Acetatecopolymers/EVA |
Usage: | General Plastics, Engineering Plastics, Specialty Plastics |
Pemasok dengan izin usaha terverifikasi
PROPERTI | METODE PENGUJIAN | SATUAN | Data |
Konten VA | % | 16.0 | |
Kerapatan | ASTM D1505 | g/cm3 | 0.937 |
Cairkan Indeks | ASTM D1238 | g/10 menit | 1.5 |
Kekuatan tensil (Pemecahan) | ASTM D638 | Kg/cm2 | 170 |
Naskh dalam waktu rehat | ASTM D638 | % | 700 |
Titik lebur | ASTM D-3418 | 89 | |
Kekerasan | ASTM D2240 | Pantai D | 37 |
Properti | Metode pengujian | Nilai |
Konten VA(%) | USI | 18 |
Kerapatan(g/cm3) | ASTM D792 | 0.939 |
Cairkan Indeks (g/10 menit) | ASTM D1238 | 2.5 |
Kekuatan tensil(Molded)(Break)(kg/cm2) | ASTM D638 | 180 |
Ongasi akhir (Molded)(%) | ASTM D638 | 750 |
Brittlewatan suhu Rendah(celcius/F50) | ASTM D746 | <-76 |
Vicat lembek(celcius) | ASTM D1525 | 64 |
Titik leleh (celcius) | ASTM D3418 | 86 |
Kekerasan(Shore D) | ASTM D2240 | 36 |
PROPERTI | METODE PENGUJIAN | SATUAN | Data |
Konten VA | % | 28.0 | |
Kerapatan | ASTM D1505 | g/cm3 | 0.954 |
Cairkan Indeks | ASTM D1238 | g/10 menit | 15 |
Kekuatan tensil (Pemecahan) | ASTM D638 | Kg/cm2 | 80 |
Naskh dalam waktu rehat | ASTM D638 | % | >800 |
Titik lebur | ASTM D-3418 | 69 | |
Kekerasan | ASTM D2240 | Pantai D | 20 |
Pemasok dengan izin usaha terverifikasi