CAS No.: | 26007-43-2 |
---|---|
Formula: | resin coc |
EINECS: | resin coc |
Material: | Coc |
Usage: | Engineering Plastics |
Plastic Properties After Heated: | Thermoplastic Plastics |
Pemasok dengan izin usaha terverifikasi
Item Fungsional |
Kondisi pengujian |
Metode Pengujian |
Numerik/deskripsi |
satukan |
|
Sifat mekanis |
Intensitas kekuatan tensil (sadapan) |
|
ASTM D638/ISO 527 |
32 |
Kg/cm²(MPa)[lb/in2] |
modulus tensil |
|
ASTM D638/ISO 527 |
1770 |
Kg/cm²(MPa)[lb/in2] |
|
Ongasi hasil tensil ( pemongangan) |
|
ASTM D638/ISO 527 |
2 |
% |
|
Kononggrasi di break, elongasi) |
|
ASTM D638/ISO 527 |
- |
Kg/cm²(MPa)[lb/in2] |
|
Modulus tekukan ( tingkat elastisitas tekukan) |
|
ASTM D790/ISO 178 |
2750 |
Kg/cm²(MPa)[lb/in2] |
|
Kekuatan fleksibilitas |
|
ASTM D790/ISO 178 |
65 |
Kg/cm²(MPa)[lb/in2] |
|
Kekuatan benturan bertakik IZOD |
1/4" -30 |
ASTM D256/ISO 179 |
- |
Kg·cm/cm(J/M)ft·lb/in |
|
1/4" 23CELCIUS |
ASTM D256/ISO 179 |
- |
Kg·cm/cm(J/M)ft·lb/in |
||
1/8" 23CELCIUS |
ASTM D256/ISO 179 |
- |
Kg·cm/cm(J/M)ft·lb/in |
||
1/8" -30 |
ASTM D256/ISO 179 |
- |
Kg·cm/cm(J/M)ft·lb/in |
||
Kekuatan dampak karakter |
23celcius (takik) |
ASTM D256/ISO 179 |
10.8 |
Kg·cm/cm(J/M)ft·lb/in |
|
-30 (takik) |
ASTM D256/ISO 179 |
- |
Kg·cm/cm(J/M)ft·lb/in |
||
23celcius (tidak bertakik) |
ASTM D256/ISO 179 |
- |
Kg·cm/cm(J/M)ft·lb/in |
||
-30 (tidak bertakik) |
ASTM D256/ISO 179 |
- |
Kg·cm/cm(J/M)ft·lb/in |
||
Kinerja fisik |
Gravitasi spesifik (kerapatan) |
|
ASTM D792/ISO 1183 |
0.948 |
|
Tarif berpesan 23 celcius / 24 jam |
|
ASTM D570/ISO 62 |
0.01 |
% |
|
Mold Shrinkage |
|
ASTM D955 |
- |
% |
|
Indeks logam cair ( koefisien aliran) |
200 g/5 kg |
ASTM D1238/ISO 1133 |
32 |
g/10 menit |
|
220C/10kg |
ASTM D1238/ISO 1133 |
- |
g/10 menit |
||
Properti Termal |
suhu defleksi panas |
Annealing |
ASTM D648/ISO 75 |
110 |
|
Injeksi kotak |
ASTM D648/ISO 75 |
- |
|||
suhu vital |
|
ASTM D785 |
123 |
||
Dengan Kerentanan ( dengan Combusceptibility) |
|
UL94 |