Warranty: | Quality Reliable/Available |
---|---|
Type: | Seamless |
Technique: | Hot Rolled |
Material: | Carbon Steel |
Surface Treatment: | Black |
Usage: | Pipeline Transport, Boiler Pipe, Hydraulic/Automobile Pipe, Oil/Gas Drilling, Food/Beverage/Dairy Products, Machinery Industry, Chemical Industry, Mining, Construction & Decoration, Special Purpose |
Pemasok dengan izin usaha terverifikasi
Tipe | pipa/pipa baja karbon | |
Materi | Api 5L /A53 /A106 KELAS B dan material lain yang diperiksa klien | |
Ukuran | Diameter luar | Lancar:17-914mm 3/8"-36" |
Ketebalan dinding | SCH10 SCH20 SCH30 STD SCH40 XS SCH80 | |
SCH100 SCH120 SCH140 SCH160 XXS | ||
Panjang | Satu-satunya panjang acak/Panjang acak Ganda | |
5m-14m, 5,8 m, 6m, 10m, 12 m, atau sebagai permintaan pelanggan sebenarnya | ||
Berakhir | Penutup polos/BLH,dilindungi oleh tutup plastik di kedua ujung, alur yang beralur, alur dan kopling sambungan, dll. | |
Perlakuan Permukaan | Lapisan tanpa Cat, hitam, vareng,galvanisasi, anti-korosi 3PE PP/EP/FBE | |
Metode teknis | Hot-rolled/cold-Died/hot-expanded | |
Metode pengujian | Tes tekanan,deteksi cacat,Eddy current testing, pengujian Hydro statis atau pemeriksaan ultrasonik dan juga pemeriksaan properti kimia dan fisik | |
Pengemasan | Pipa kecil yang bundel dengan strip baja kuat,bagian besar longgar; ditutup dengan tas anyaman plastik; casing kayu; cocok untuk operasi pengangkatan; dimasukkan dalam kontainer 40 kaki atau 45 ft atau dalam jumlah besar; juga sesuai permintaan pelanggan | |
Asal | Cina | |
Aplikasi | Mengirimkan gas dan air oli | |
Pemeriksaan pihak ketiga | SGS BV MTC | |
Ketentuan Perdagangan | FOB CIF CFR | |
Ketentuan Pembayaran | FOB 30%T/T, 70% sebelum pengiriman | |
CIF 30% pra-pembayaran dan keseimbangan yang harus dibayar sebelumnya membuat pengiriman atau | ||
100% L/C tidak dapat dibatalkan saat dilihat | ||
MOQ | 10 ton | |
Kapasitas Suplai | 5000 T/M. | |
Waktu pengiriman | Biasanya dalam 10-45 hari setelah menerima pembayaran di muka |
Komposisi kimia pipa casing
Standar | Kelas | Komposisi kimia(%) | |||||||||
API SPEC 5CT | J55 | C | Si | MN | P | S | CR | NI | CU | MO | V |
K55 | 0.34-0.39 | 0.20-0.35 | 1.25-1.50 | ≤0.020 | ≤0.015 | ≤0.15 | ≤0.20 | ≤0.20 | / | / | |
N80 | 0.34-0.38 | 0.20-0.35 | 1.45-1.70 | ≤0.020 | ≤0.015 | ≤0.15 | / | / | / | 0.11-0.16 | |
Q125 | ≤0.35 | -------------- | ≤1.35 | ≤0.020 | ≤0.010 | ≤1.50 | ≤0.20 | ≤0.20 | / | / | |
P110 | 0.26-0.395 | 0.17-0.37 | 0.40-0.70 | ≤0.020 | ≤0.010 | 0.80-1.10 | ≤0.20 | ≤0.20 | 0.15-0.25 | ≤0.08 |
Kelas | Tipe | Total pemanjangan dengan muatan (%) |
Menghasilkan kekuatan (Min)Mpa |
Menghasilkan kekuatan (maks)Mpa |
Kekuatan tensil Min Mpa |
Kekerasan Maks (HRC) |
Kekerasan Maks (HBW) |
J55 | - | 0.5 | 379 | 552 | 517 | - | - |
K55 | - | 0.5 | 379 | 552 | 655 | - | - |
N80 | 1 | 0.5 | 552 | 758 | 689 | - | - |
N80 | Q | 0.5 | 552 | 758 | 689 | - | - |
L80 | 1 | 0.5 | 552 | 655 | 655 | 23 | 241 |
L80 | 9Cr | 0.5 | 552 | 655 | 655 | 23 | 241 |
L80 | 13Cr | 0.5 | 552 | 655 | 655 | 23 | 241 |
C90 | - | 0.5 | 621 | 724 | 689 | 25.4 | 255 |
C95 | - | 0.5 | 655 | 758 | 724 | - | - |
T95 | - | 0.5 | 655 | 758 | 724 | 25.4 | 255 |
P110 | - | 0.6 | 758 | 965 | 862 | - | - |
Q125 | Semua | 0.65 | 862 | 1034 | 931 | - | - |
Proses Pembuatan Pipa casing:
Pemanasan baja → memukul dengan tepat waktu penggalian hidraulik → memanaskan ulang ekstensi → → rolling berkala → memanaskan ulang → ukuran → pendinginan → meluruskan → pemotongan pipa → pemeriksaan
1. Diperlukan tungku pemanas yang melingkar untuk pemanasan ingot;
2. Memukul dan memanaskan ulang dengan tekanan hidrolik;
3. Pabrik penutup oli menggunakan alat berat ekstensi pelat pemandu dua roller untuk ekstensi;
4. Gunakan kembali tungku pemanas cakram untuk rolling berkala, dan gunakan tungku tanpa masuk untuk memanaskan ulang, pendinginan, pelurus, pemotongan pipa, dan pemeriksaan.