Technique: | Winding Filament Roving |
---|---|
Yarn Structure: | Bulk Yarn |
Surface Treatment: | with Special Treatment of Water Blocking Coating |
Fiberglass Type: | E-Glass |
Tex: | 600teks/735lapisan/1200tex/2400tex |
pelapisan: | High Performance Polymer Matrix |
Pemasok dengan izin usaha terverifikasi
Karakteristik | Bobot/m | Brancn Keluaran | Kekuatan tensil | Naskh (Naskh) | Modulus elastisitas | LASE 0.3% | LASE 0.5% | LASE 1.0% |
Metode Pengujian | ASTM D 885 | ASTM D 885 | ASTM D 885 | ASTM D 885 | EN/ISO 3341 | EN/ISO 3341 | EN/ISO 3341 | EN/ISO 3341 |
Satuan | g/m | m/kg | N | % | IPK | N | N | N |
600Tex | ||||||||
Umum | 0.610 | 1639 | 410 | 2.1 | 80 | 75 | 115 | 215 |
Min | 0.57 | 1532 | 280 | 1.4 | 70 | 60 | 100 | 200 |
Maks. | 0.65 | 1763 | 2.8 | 90 | 90 | 130 | 230 | |
Toleransi | ±7% | ±7% | ±0.7 | ±10 | ±15 | ±15 | ±15 | |
735Tex | ||||||||
Umum | 0.740 | 1351 | 485 | 2.1 | 80 | 95 | 140 | 260 |
Min | 0.69 | 1263 | 330 | 1.4 | 70 | 80 | 125 | 245 |
Maks. | 0.79 | 1453 | 2.8 | 90 | 110 | 155 | 275 | |
Toleransi | ±7% | ±7% | ±0.7 | ±10 | ±15 | ±15 | ±15 | |
1200Tex | ||||||||
Umum | 1.22 | 820 | 775 | 2.1 | 80 | 150 | 225 | 420 |
Min | 1.13 | 766 | 540 | 1.4 | 70 | 145 | 205 | 380 |
Maks. | 1.31 | 881 | 2.8 | 90 | 165 | 245 | 460 | |
Toleransi | ±7% | ±7% | ±0.7 | ±10 | ±15 | ±20 | ±40 | |
2400Tex | ||||||||
Umum | 2.46 | 407 | 1475 | 2.1 | 80 | 265 | 400 | 765 |
Min | 2.29 | 380 | 1030 | 1.4 | 70 | 235 | 360 | 720 |
Maks. | 2.63 | 437 | 2.8 | 90 | 295 | 440 | 810 | |
Toleransi | ±7% | ±7% | ±0.7 | ±10 | ±30 | ±40 | ±45 |
Pemasok dengan izin usaha terverifikasi