Tipe: | Elektrode grafit |
---|---|
Komposisi: | 80% Needle Coke |
Konten Karbon: | High-Carbon (Karbon Tinggi) |
Kelas: | UHP |
Cara membentuk: | Tampilan luas |
Morfologi kristal: | Graphitized |
Pemasok dengan izin usaha terverifikasi
Produksi Paramedik
Elektrode UHP Graphite
Item | Resistansi Listrik spesifik <= µΩ·m | Kekuatan fleksibilitas fleksibilitas > =MPa | MOE<= IPK | CTE( 100-600CELCIUS) <= 10-6/ | ABU<= | DIAMETER DAN PANJANG | Kepadatan massal >=g/cm3 | Konten Koka jarum % |
|
Standar ( YB/T 4089-2015 ) | E | 4.5-6.2 | 10-16 | 10-14 | 1.1-1.5 | 0.2 | 250 mm-700 mm 1800 mm-2700mm |
1.66-1.72 | 45-90% |
N | 3.0-4.2 | 21-30 | 15-20 | 0.9-1.2 | 1.75-1.82 | ||||
Suplai Pabrik | E | <=6.0 | 10-16 | 10-16 | 1.5 | 0.2 | >=1.67 | 50%-100% | |
N | <=4.0 | 21-30 | 14-18 | 1.2 | >=1.78 |
Item | Resistansi Listrik spesifik <= µΩ·m | Kekuatan fleksibilitas fleksibilitas > =MPa | MOE<= IPK | CTE( 100-600CELCIUS) <= 10-6/ | ABU<= | DIAMETER DAN PANJANG | Kepadatan massal >=g/cm3 | Konten Koka jarum % |
|
Standar ( YB/T 4089-2015 ) | E | 5.2-6.5 | 10.5-15 | 9-12 | 1.5-2.2 | 0.2 | 200mm-700mm 1800 mm-2700mm |
1.66-1.72 | 20-35% |
N | 4.0-4.5 | 20-26 | 14-18 | 1.2-1.5 | 1.75-1.82 | ||||
Suplai Pabrik | E | <=6.5 | 10.5-15 | 9-12 | 1.5 | 0.2 | >=1.66 | 25%-40% | |
N | <=4.0 | 20-26 | 14-20 | 1.2 | >=1.78 |
Elektrode Kelas Graphite lainnya , Anda dapat menerima permintaan informasi Anda secara spesifik!
Product Show :
Detail Paket : dalam bentuk kayu atau paket sesuai pesanan pelanggan
Penggunaan: Peningkatan proporsi baja global dibuat menggunakan tungku busur listrik, dan tungku busur listrik sendiri menjadi lebih efisien dan membuat lebih banyak baja per ton elektrode
KITA memiliki pelanggan yang banyak dari pasar internasional.
Pemasok dengan izin usaha terverifikasi