Tipe: | Elektrode grafit |
---|---|
Komposisi: | 80% Needle Coke |
Konten Karbon: | High-Carbon (Karbon Tinggi) |
Kelas: | UHP |
Cara membentuk: | Tampilan luas |
Morfologi kristal: | Graphitized |
Pemasok dengan izin usaha terverifikasi
DIAMETER (MM) | Panjang (mm) | ||||||
Diameter Nominal | Diameter Aktual | Panjang Nominal | Toleransi yang diizinkan | Toleransi Panjang Pendek | |||
Inci | mm | <= | >= | Bagian kulit hitam<= | / | / | / |
3 | 75 | 78 | 73 | 72 | 1000/1200/1400/1600 | ±100 | -275 |
4 | 100 | 103 | 98 | 97 | 1000/1200/1400/1600 | ||
5 | 130 | 132 | 127 | 126 | 1000/1200/1400/1600 | ||
6 | 150 | 154 | 149 | 146 | 1200/1400/1600/1800 | ||
7 | 175 | 179 | 174 | 171 | 1200/1400/1600/1800 | ||
8 | 200 | 205 | 200 | 197 | 1600/1800 | ||
9 | 225 | 230 | 225 | 222 | 1600/1800 | ||
10 | 250 | 256 | 251 | 248 | 1600/1800/2000 | ||
12 | 300 | 307 | 302 | 299 | 1600/1800/2000/2200 | ||
14 | 350 | 358 | 352 | 349 | 1600/1800/2000/2200 | ||
16 | 400 | 409 | 403 | 400 | 1600/1800/2000/2200 | ||
18 | 450 | 460 | 454 | 451 | 1600/1800/2000/2200 | ||
20 | 500 | 511 | 505 | 502 | 1800/2000/2200/2400 | ||
22 | 550 | 562 | 556 | 553 | 1800/2000/2200/2400 | ||
24 | 600 | 613 | 607 | 604 | 2000/2200/2400/2700 | ||
26 | 650 | 663 | 659 | 656 | 2400/2700 | ||
28 | 700 | 714 | 710 | 707 | 2400/2700 |
Diameter Nominal | Elektrode RP Graphite | Elektrode HP Graphite | Elektrode UHP Graphite | |||
mm | Memungkinkan Kapasitas saat ini /A | Densitas saat ini / (A/cm2 ) |
Memungkinkan Kapasitas saat ini /A | Densitas saat ini / (A/cm2 ) |
Memungkinkan Kapasitas saat ini /A | Densitas saat ini / (A/cm2 ) |
75 | 1000-1400 | 22-31 | ||||
100 | 1500-2400 | 19-30 | ||||
130 | 2200-3400 | 17-26 | ||||
150 | 3000-4500 | 16-25 | ||||
200 | 5000-6900 | 15-21 | 5500-9000 | 18-25 | ||
250 | 7000-10000 | 14-20 | 8000-13000 | 18-25 | 8100-12200 | 20-30 |
300 | 10000-13000 | 14-18 | 13000-17400 | 17-24 | 15000-22000 | 20-30 |
350 | 13500-18000 | 14-18 | 17400-24000 | 17-24 | 20000-30000 | 20-30 |
400 | 18000-23500 | 14-18 | 21000-31000 | 16-24 | 25000-40000 | 19-30 |
450 | 22000-27000 | 13-17 | 25000-40000 | 15-24 | 32000-45000 | 19-30 |
500 | 25000-32000 | 13-16 | 30000-48000 | 15-24 | 38000-55000 | 18-27 |
550 | 28000-34000 | 12-14 | 34000-53000 | 14-22 | 45000-65000 | 18-27 |
600 | 30000-36000 | 11-13 | 38000-58000 | 13-21 | 50000-75000 | 18-26 |
650 | 32000-39000 | 10-12 | 41000-65000 | 12-20 | 60000-85000 | 18-25 |
750 | 34000-42000 | 9-11 | 45000-72000 | 12-19 | 70000-120000 | 18-30 |
Produksi Paramedik
Elektrode UHP Graphite
Item | Resistansi Listrik spesifik <= µΩ·m | Kekuatan fleksibilitas fleksibilitas > =MPa | MOE<= IPK | CTE( 100-600CELCIUS) <= 10-6/ | ABU<= | DIAMETER DAN PANJANG | Kepadatan massal >=g/cm3 | Konten Koka jarum % |
|
Standar ( YB/T 4089-2015 ) | E | 4.5-6.2 | 10-16 | 10-14 | 1.1-1.5 | 0.2 | 250 mm-700 mm 1800 mm-2700mm |
1.66-1.72 | 45-90% |
N | 3.0-4.2 | 21-30 | 15-20 | 0.9-1.2 | 1.75-1.82 | ||||
Suplai Pabrik | E | <=6.0 | 10-16 | 10-16 | 1.5 | 0.2 | >=1.67 | 50%-100% | |
N | <=4.0 | 21-30 | 14-18 | 1.2 | >=1.78 |
Item | Resistansi Listrik spesifik <= µΩ·m | Kekuatan fleksibilitas fleksibilitas > =MPa | MOE<= IPK | CTE( 100-600CELCIUS) <= 10-6/ | ABU<= | DIAMETER DAN PANJANG | Kepadatan massal >=g/cm3 | Konten Koka jarum % |
|
Standar ( YB/T 4089-2015 ) | E | 5.2-6.5 | 10.5-15 | 9-12 | 1.5-2.2 | 0.2 | 200mm-700mm 1800 mm-2700mm |
1.66-1.72 | 20-35% |
N | 4.0-4.5 | 20-26 | 14-18 | 1.2-1.5 | 1.75-1.82 | ||||
Suplai Pabrik | E | <=6.5 | 10.5-15 | 9-12 | 1.5 | 0.2 | >=1.66 | 25%-40% | |
N | <=4.0 | 20-26 | 14-20 | 1.2 | >=1.78 |
Elektrode RP Graphite
Item | Resistansi Listrik spesifik <= µΩ·m | Kekuatan fleksibilitas fleksibilitas > =MPa | MOE<= IPK | CTE( 100-600CELCIUS) <= 10-6/ | ABU<= | DIAMETER DAN PANJANG | Kepadatan massal >=g/cm3 | |
Standar ( YB/T 4089-2015 ) | E | 7.0-8.5 | 7.0-9.5 | 6.0-9.0 | 2.2-2.5 | 0.5 | 100-960mm 1600 mm-2700mm |
1.60-1.65 |
N | 4.0-4.5 | 17-22 | 12-16 | 1.5-2.0 | 1.75-1.82 | |||
Suplai Pabrik | E | 8 | 7.5-9.5 | 6.0-10 | 2.5 | 0.5 | 1.6 | |
N | 4.0 | 17-22 | 12-16 | 2.0 | 1.80 |
Product Show :
Detail Paket : dalam bentuk kayu atau paket sesuai pesanan pelanggan
Penggunaan: Peningkatan proporsi baja global dibuat menggunakan tungku busur listrik, dan tungku busur listrik sendiri menjadi lebih efisien dan membuat lebih banyak baja per ton elektrode