Standar: | ANSI, DIN, GB, JIS, GOST |
---|---|
Tipe: | Wafer |
Material: | Baja Antikarat |
Struktur: | Flensa |
Koneksi: | Flensa |
Permukaan perapat: | RF |
Pemasok dengan izin usaha terverifikasi
Bahan ASTM Umum untuk Flank | ||||||||||||||
Kelas dan urutan |
Komponen kimia % | Properti mekanis | ||||||||||||
C(Maks) | Si (Maks) | MN (Maks) | CR(Maks) | NI (Maks) | MO (Maks) | P(Maks) | S | Kekuatan tensil mpa(Min) |
Menghasilkan kekuatan mpa(Min) |
Naskh (Naskh) mpa(Min) |
Kekerasan (Maks) |
ψ % |
||
ASTM A105/A105M |
A105 | 0.35 | 0.10-0.35 | 0.65-1.05 | 0.30 | 0.40 | 0.12 | 0.035 | 0.040 | 485 | 250 | 22 | 187 | 30 |
ASTM A182/A182 2M |
F11CL1 | 0.05-0.15 | 0.50-1.00 | 0.30-0.60 | 1.00-1.50 | ... | 0.44-0.65 | 0.030 | 0.030 | 415 | 205 | 20 | 121-174 | 45 |
F11CL2 | 0.10-0.20 | 0.05-1.00 | 0.30-0.80 | 1.00-1.50 | ... | 0.44-0.65 | 0.040 | 0.040 | 485 | 275 | 20 | 143-207 | 30 | |
F11CL3 | 0.10-0.20 | 0.05-1.00 | 0.30-0.80 | 1.00-1.50 | ... | 0.44-0.65 | 0.040 | 0.040 | 515 | 310 | 20 | 156-207 | 30 | |
F12CL1 | 0.05-0.15 | 0.50 | 0.30-0.60 | 0.80-1.25 | ... | 0.44-0.65 | 0.045 | 0.045 | 415 | 220 | 20 | 121-174 | 45 | |
F12CL2 | 0.10-0.20 | 0.10-0.60 | 0.30-0.80 | 0.80-1.25 | ... | 0.44-0.65 | 0.040 | 0.040 | 485 | 275 | 20 | 143-207 | 30 | |
F304 | 0.08 | 1.00 | 2.00 | 18.0-20.0 | 8.0-11.0 | ... | 0.045 | 0.030 | 515 | 205 | 30 | ... | 50 | |
F304H | 0.04-0.10 | 1.00 | 2.00 | 18.0-20.0 | 8.0-11.0 | ... | 0.045 | 0.030 | 515 | 205 | 30 | ... | 50 | |
F304L | 0.030 | 1.00 | 2.00 | 18.0-20.0 | 8.0-13.0 | ... | 0.045 | 0.030 | 485 | 170 | 30 | ... | 50 | |
F316L | 0.030 | 1.00 | 2.00 | 16.0-18.0 | 10.0-15.0 | ... | 0.045 | 0.030 | 485 | 170 | 30 | ... | 50 | |
F317 | 0.08 | 1.00 | 2.00 | 18.0-20.0 | 11.0-15.0 | ... | 0.045 | 0.030 | 515 | 205 | 30 | ... | 50 | |
F321 | 0.08 | 1.00 | 2.00 | 17.0-19.0 | 9.0-12.0 | ... | 0.045 | 0.030 | 515 | 205 | 30 | ... | 50 | |
F347 | 0.08 | 1.00 | 2.00 | 17.0-19.0 | 9.0-13.0 | ... | 0.045 | 0.030 | 515 | 205 |
Pemasok dengan izin usaha terverifikasi