Elektrode pengelasan Baja antikarat (E308I-16)

The weld metal deposited by these electrodes has 0.04 percent maximum carbon content. Therefore, it reduces the possibility of intergranular carbide precipitation and increases the resistance to intergranular corrosion without the use of stabilizers such as niobium or titanium.
Use on types 301, 302, 304, 304L and 305 base metals.

Welding Current Type: Dcep (direct current electrode positive) and AC

Welding Position: All.
Note: Electrode 5.0 mm is not recommended for welding in all positions.

Available Diameters: 2.5 mm, 3.2 mm, 4.0 mm, and 5.0 mm

Typical Chemical Composition: (Weight Percent)
C: 0.022 S: 0.012 Mn: 1.30 Cr: 20.20
Si: 0.61 Ni: 10.40 P: 0.016

Typical Mechanical Properties:
Tensile Strength: 520 ~ 560 MPa (75, 000 ~ 81, 000 psi)
Elongation (%): 38 ~ 44

Recommended Operating Current Ranges:
2.5 mm: 50 ~ 85 Amps
3.2 mm: 80 ~ 110 Amps
4.0 mm: 100 ~ 140 Amps
5.0 mm: 140 ~ 180 Amps