Product Type: | Tube |
---|---|
Material: | Feni |
Carbon Content: | Low Carbon |
PCD: | 98mm |
ET: | 0 |
Hole: | 0 |
Pemasok dengan izin usaha terverifikasi
NI | 28.5-29.5 | FE | BAL. | Co | 16.8-17.8 | Si | ≤0.3 |
MO | ≤0.2 | CU | ≤0.2 | CR | ≤0.2 | MN | ≤0.5 |
C | ≤0.03 | P | ≤0.02 | S | ≤0.02 |
Kode kondisi | Kondisi | Kawat | Strip |
R | Soft | ≤585 | ≤570 |
1/4I | 1/4 keras | 585-725 | 520630 hingga |
1/2I | 1/2 keras | 655795 | 590-700 |
3/4I | 3/4 keras | 725-8-60 | 600-770 |
SAYA | Keras | ≥850 | ≥700 |
Kerapatan (g/cm3) | 8.2 |
Resistivitas listrik di 20(Om*mm2/m) | 0.48 |
Faktor suhu resistivitas (205)X10-/cel | 3.7-3.9 |
TC titik Curie/ | 430 |
Elastis modulus, E/IPK | 138 |
θ/ | α1/10-61- | θ/ | α1/10-61- |
20-60 | 7.8 | 20-500 | 6.2 |
20-100 | 6.4 | 20-550 | 7.1 |
20-200 | 5.9 | 20-600 | 7.8 |
20-300 | 5.3 | 20-700 | 9.2 |
20-400 | 5.1 | 20-800 | 10.2 |
20-450 | 5.3 | 20-900 | 11.4 |
θ/ | 100 | 200 | 300 | 400 | 500 |
λ/ W/(m*) | 20.6 | 21.5 | 22.7 | 23.7 | 25.4 |
Proses perlakuan panas | |
Annealing untuk pelepas tegangan | Berpemanas hingga 470 derajat 540 dan tahan 1-2 jam Dingin |
annealing | Dalam vakum yang dipanaskan hingga 750, 900 |
Waktu Holding | 14 mnt.1h. |
Laju pendinginan | Tidak lebih dari 10 200/mnt di gunakan |
Nama Lalloys | Tipe | Dimensi | ||
UALLOY-4J29 | Kawat | D= 0.1 mm | ||
UALLOY-4J29 | Strip | W= 5. 250mm | T= 0,1mm | |
UALLOY-4J29 | Foil | W= 10 100mm | T= 0.01-0.1 | |
UALLOY-4J29 | Bar | Dia= 8 100mm | L= 50-1000 |