Jenis Produk: | Strip |
---|---|
Material: | Feni36 |
Konten Karbon: | Low Carbon (Karbon Rendah) |
PCD: | 98mm |
ET: | 0 |
Lubang: | 0 |
Pemasok dengan izin usaha terverifikasi
NI | 35-37.0 | FE | BAL. | Co | - | Si | ≤0.3 |
MO | - | CU | - | CR | - | MN | 0.2-0.6 |
C | ≤0.05 | P | ≤0.02 | S | ≤0.02 |
Kerapatan (g/cm3) | 8.1 |
Resistivitas listrik di 20 (ohm.mm2/m) | 0.78 |
Faktor suhu resistivitas (206) X10-/celcius | 3.7-3.9 |
Konduktivitas termal, λ/W/(m*) | 11 |
TC titik Curie/ | 230 |
Elastis modulus, E/IPK | 144 |
θ/ | α1/10-61- | θ/ | α1/10-61- |
20 | 1.8 | 20-250 | 3.6 |
20 -40 | 1.8 | 20-300 | 5.2 |
20 -20 | 1.6 | 20-350 | 6.5 |
20--0 | 1.6 | 20-400 | 7.8 |
20-50 | 1.1 | 20-450 | 8.9 |
20-100 | 1.4 | 20-500 | 9.7 |
20-150 | 1.9 | 20-550 | 10.4 |
20-200 | 2.5 | 20-600 | 11.0 |
Kekuatan tensil | Naskh (Naskh) |
MPa | % |
641 | 14 |
689 | 9 |
731 | 8 |
Rentang suhu, atau suhu | 20-50 | 20-100 | 20-200 | 20-300 | 20-400 |
Ar/ 103 * | 1.8 | 1.7 | 1.4 | 1.2 | 1.0 |
Proses perlakuan panas | |
Annealing untuk pelepas tegangan | Berpemanas hingga 530 -550 dan tahan 1-2 jam Dingin |
annealing | Untuk menghilangkan pengerasan yang dihasilkan dari proses cold-rolled dan cold dring . Annealing perlu dipanaskan hingga 830 celcius dalam vakum, tahan 30 menit |
Proses stabilisasi |
Di media pelindung dan berpemanas hingga 830, tahan 20 menit. memuaskan
Karena stres yang dihasilkan dengan penggalian, berpemanas hingga 315C,tahan 1 jam.
|
Tindakan pencegahan |
Tidak dapat diperkuat dengan perlakuan panas,
Perlakuan permukaan dapat berupa peledakan, penghalus, atau pencacahan.
Aloi dapat digunakan larutan acchloric Acar 25% di 70 untuk membersihkan permukaan teroksidasi
|