Nama Standar | Komposisi kimia | Sifat Mekanis | ||||||||||||||
JIS | GB | KELUAR | ID | C | Si | MN | P | S | NI | CR | Lainnya | Menghasilkan kekuatan | Tekanan | Naskh (Naskh) | Kekerasan | |
UNS | maks. | maks. | maks. | maks. | maks. | maks. | N/mm2 | N/mm2 | % | HV | HRB | |||||
Baja anti karat austenitic | ||||||||||||||||
SUS201 | 1R17Mn6N5N | 201 | ** | 0.15 | 1 | 5.50-7.50 | 0.06 | 0.03 | 1 | 16.00-18.00 | N0,25 | 245 | 640 | 40 | 253 | 100 |
SUS202 | 1R18Mn8N5N | 202 | ** | 0.15 | 1 | 7.50-10.00 | 0.06 | 0.03 | 4.00-6.00 | 17.00-19.00 | N0,25 | 245 | 590 | 40 | 218 | 95 |
SUS301 | 1R17Ni7 | 301 | 1.431 | 0.15 | 1 | 2 | 0.045 | 0.03 | 6.00-8.00 | 16.00-18.00 | _ | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 218 | ≤ 95 |
SUS301L | 00Cr17Ni7 | 301L | 1.4318 | 0.03 | 1 | 2 | 0.045 | 0.03 | 6.00-8.00 | 16.00-18.00 | N : 0.20 | ≥ 215 | ≥ 550 | ≥ 45 | ≤ 218 | ≤ 95 |
SUS304 | 0C18Ni9 | 304 | 1.4301 | 0.08 | 1 | 2 | 0.045 | 0.03 | 8.0-10.50 | 18.00-20.00 | _ | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 200 | ≤ 90 |
SUS304L | 00C19Ni10 | 304L | 1.4307 | 0.03 | 1 | 2 | 0.045 | 0.03 | 9.00-13.00 | 18.00-20.00 | _ | ≥ 175 | ≥ 480 | ≥ 40 | ≤ 200 | ≤ 90 |
SUS304CU | 0C18Ni9 | 304 | 1.4301 | 0.08 | 1 | 2 | 0.045 | 0.03 | 8.00-10.50 | 18.00-20.00 | CU : 0.70-1.30 | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 200 | ≤ 90 |
SUS304Ni8,5 | 0C18Ni9 | 304 | 1.4301 | 0.08 | 1 | 2 | 0.045 | 0.03 | 8.50-10.50 | 18.00-20.00 | _ | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 200 | ≤ 90 |
SUS304Ni9 | 0C18Ni9 | 304 | 1.4301 | 0.08 | 1 | 2 | 0.045 | 0.03 | 9.00-10.50 | 18.00-20.00 | _ | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 200 | ≤ 90 |
SUS316 | 0Cr17NiM2 | 316 | 1.4401 | 0.08 | 1 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | MO: 2.00-3.00 | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 200 | ≤ 90 |
SUS316L | 00Cr17Ni14M2 | 316L | 1.4404 | 0.03 | 1 | 2 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 | MO: 2.00-3.00 | ≥ 175 | ≥ 480 | ≥ 40 | ≤ 200 | ≤ 90 |
SUS321 | 0C18Ni10Ti | 321 | 1.4541 | 0.08 | 1 | 2 | 0.045 | 0.03 | 9.00-13.00 | 17.00-19.00 | TI: 5*C% | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 200 | ≤ 90 |
SUS309S | 0C23Ni13 | 309S | 1.4833 | 0.08 | 1 | 2 | 0.045 | 0.03 | 12.00-15.00 | 22.00-24.00 | _ | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 200 | ≤ 90 |
SUS310S | 0C25Ni20 | 310S. | 1.4845 | 0.08 | 1.5 | 2 | 0.045 | 0.03 | 19.00-22.00 | 24.00-26.00 | _ | ≥ 205 | ≥ 520 | ≥ 40 | ≤ 200 | ≤ 90 |
Baja anti karat Ferritic | ||||||||||||||||
SUH409L | 00C12Ti | 409L | 1.4512 | 0.03 | 1 | 1 | 0.04 | 0.03 | _ | 10.50-11.75 | TI : 6*C%-0,75 | ≥ 175 | ≥ 360 | ≥ 25 | ≤ 175 | ≤ 80 |
SUS436L | 00Cr17Mo | ** | ** | 0.025 | 1 | 1 | 0.04 | 0.03 | _ | 16.00-19.00 | MO: 0.75-1.50 \ Ti , NB , ZR : 8* ( C%+N% ) -0,80 | ≥ 245 | ≥ 410 | ≥ 20 | ≤ 230 | ≤ 96 |
** | 410 | 1.4006 | 0.15 | 1 | 1 | 0.04 | 0.03 | _ | 11.50-13.50 | _ | ≥ 205 | ≥ 440 | ≥ 20 | ≤ 210 | ≤ 93 | |
SUS410L | 00Cr12 | ** | 1.4003 | 0.03 | 1 | 1 | 0.04 | 0.03 | _ | 11.00-13.50 | _ | ≥ 195 | ≥ 360 | ≥ 22 | ≤ 200 | ≤ 88 |
SUS439 | 00C17 | ** | 1.451 | 0.03 | 1 | 1 | 0.04 | 0.03 | 0.5 | 17.00-19.00 | TI :(0.20+4* (C+N )-1,10 , Al: 0.15 : N : 0.030 | ≥ 205 | ≥ 415 | ≥ 22 | ≤ 200 | ≤ 89 |
SUS434 | ** | 434 | 1.4113 | 0.12 | 1 | 1 | 0.04 | 0.03 | _ | 16.00-18.00 | _ | ≥ 205 | ≥ 450 | ≥ 22 | ≤ 200 | ≤ 88 |
SUS444 | 00Cr18Mo2 | 444 | 1.4521 | 0.025 | 1 | 1 | 0.04 | 0.03 | _ | 17.00-20.00 | MO: 1.75-2.50 Ti , NB , ZR : 8* ( C%+N% ) -0,80 | ≥ 245 | ≥ 410 | ≥ 20 | ≤ 230 | ≤ 96 |
SUS430 | 1R17 | 430 | 1.4016 | 0.12 | 1 | 1 | 0.04 | 0.03 | _ | 16.00-18.00 | _ | ≥ 205 | ≥ 420 | ≥ 22 | ≤ 200 | ≤ 88 |
Baja anti karat Martensit | ||||||||||||||||
SUS420J1 | 2C13 | 420 | 1.4021 | 0.16-0.25 | 1 | 1 | 0.04 | 0.03 | _ | 12.00-14.00 | _ | ≥ 225 | ≥ 520 | ≥ 18 | ≥ 234 | ≥ 97 |
SUS420J2 | 3C13 | 420JS | 1.4028 | 0.26-0.40 | 1 | 1 | 0.04 | 0.03 | _ | 12.00-14.00 | _ | ≥ 225 | ≥ 540 | ≥ 18 | ≥ 247 | ≥ 99 |