Product Type: | Electric resistance with |
---|---|
Material: | Nickel chrome |
Carbon Content: | -0.04 |
PCD: | - |
ET: | - |
Hole: | - |
Pemasok dengan izin usaha terverifikasi
Komposisi kimia dan Properti Utama Nichrome |
||||||
Properti \ Grade |
NCr 80/20 |
NCr 70/30 |
NCr 60/15 |
NCr 35/20 |
NCr 30/20 |
|
Komposisi kimia Utama |
NI |
Keseimbangan |
Keseimbangan |
55.0-61.0 |
34.0-37.0 |
30.0-34.0 |
CR |
20.0-23.0 |
28.0-31.0 |
15.0-18.0 |
18.0-21.0 |
18.0-21.0 |
|
FE |
≤1.0 |
≤1.0 |
Keseimbangan |
Keseimbangan |
Keseimbangan |
|
Suhu Servis Kontinu Maks(OC) |
1200 |
1250 |
1150 |
1100 |
1100 |
|
Resivitivitasan 20oC (Ωmm2/m) |
1.09 |
1.18 |
1.12 |
1.04 |
1.04 |
|
Kerapatan (g/cm3) |
8.4 |
8.1 |
8.2 |
7.9 |
7.9 |
|
Konduktivitas termal(KJ/m·h·OC) |
60.3 |
45.2 |
45.2 |
43.8 |
43.8 |
|
Koefisien Ekspansi Termal (α ASCII 10-6/OC) |
18 |
17 |
17 |
19 |
19 |
|
Titik Lekapan |
1400 |
1380 |
1390 |
1390 |
1390 |
|
Naskh (penghapusan) (%) |
>20 |
>20 |
>20 |
>20 |
>20 |
|
Struktur Mikrografis |
austenite |
austenite |
austenite |
austenite |
austenite |
|
Sifat Magnet |
tidak magnetik |
tidak magnetik |
tidak magnetik |
Magnet lemah |
Magnet lemah |
Komposisi kimia dan Properti Utama Fe-Cr-Al Campuran tahan |
||||||||
Properti \ Grade |
1R13Al4 |
0C25Al5 |
0C21Al6 |
0C23Al5 |
0C21Al4 |
0C21Al6Nb |
0Cr27Al7Mo2 |
|
Komposisi kimia Utama (%) |
CR |
12.0-15.0 |
23.0-26.0 |
19.0-22.0 |
22.5-24.5 |
18.0-21.0 |
21.0-23.0 |
26.5-27.8 |
Al |
4.0-6.0 |
4.5-6.5 |
5.0-7.0 |
4.2-5.0 |
3.0-4.2 |
5.0-7.0 |
6.0-7.0 |
|
Re |
oportune |
oportune |
oportune |
oportune |
oportune |
oportune |
oportune |
|
FE |
BAL. |
BAL. |
BAL. |
BAL. |
BAL. |
BAL. |
BAL. |
|
Nb0,5 |
Mo1.8-2.2 |
|||||||
Suhu Servis Kontinu Maks(OC) |
650 |
1250 |
1250 |
1250 |
1100 |
1350 |
1400 |
|
Resivitivitasan 20oC (Ωmm2/m) |
1.25 ±0.08 |
1.42 ±0.06 |
1.42 ±0.07 |
1.35 ±0.07 |
1.23 ±0.07 |
1.45 ±0.07 |
1.53 ±0.07 |
|
Kerapatan(g/cm3) |
7.4 |
7.1 |
7.16 |
7.25 |
7.35 |
7.1 |
7.1 |
|
Konduktivitas Termal |
52.7 |
46.1 |
63.2 |
60.2 |
46.9 |
46.1 |
45.2 |
|
(KJ/m·h·OC) |
||||||||
Koefisien Ekspansi Termal (α ASCII 10-6/OC) |
15.4 |
16 |
14.7 |
15 |
13.5 |
16 |
16 |
|
Perkiraan Titik pelelehan( OC) |
1450 |
1500 |
1500 |
1500 |
1500 |
1510 |
1520 |
|
Kekuatan tensil(N/mm2) |
580-680 |
630-780 |
630-780 |
630-780 |
600-700 |
650-800 |
680-830 |
|
Naskh (penghapusan) (%) |
>16 |
>12 |
>12 |
>12 |
>12 |
>12 |
>10 |
|
Variasi bagian |
65-75 |
60-75 |
65-75 |
65-75 |
65-75 |
65-75 |
65-75 |
|
Laju penurunan (%) |
||||||||
Frekuensi Benali (berulang)(F/R) |
>5 |
>5 |
>5 |
>5 |
>5 |
>5 |
>5 |
|
Keras (F.H.) |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
|
Waktu Servis Kontinu |
tidak |
≥80/1300 |
≥80/1300 |
≥80/1300 |
≥80/1250 |
≥50/1350 |
≥50/1350 |
|
Struktur Mikrografis |
Ferit |
Ferit |
Ferit |
Ferit |
Ferit |
Ferit |
Ferit |
|
Sifat Magnet |
Magnetik |
Magnetik |
Magnetik |
Magnetik |
Magnetik |
Magnetik |
Magnetik |
Pemasok dengan izin usaha terverifikasi