Kabel pemanas campuran Chromium resistan 6ium/Strip/Pita (ni80cr20/ni70cr30/ni60cr15/ni35cr20/ni20cr25/ni3020)

• Application: Aviation, Electronics, Industrial, Medical
• Standard: JIS, GB, DIN, BS, ASTM, AISI
• Purity: >98%
• Alloy: Alloy
• Type: Nickel Strip
• Powder: Not Powder
• Tidak. Model.: Nickel Chromium Alloy
• warna: putih
• ukuran: 0.01-3mm*0.3-600mm
• contoh: pesanan kecil diterima
• permukaan: cerah
• negara bagian: soft,1/4hard,1/2hard,hard,t-hard
• kepekaan ulang: 1.04-1.18 ohm mm2/m
• Paket Transportasi: Waterproof Paper, Weave Bag, Wooden Case
• Spesifikasi: DIN 17470
• Merek Dagang: TANKII
• Asal: China
• Kode HS: 7506200000
• Kapasitas Produksi: 3000 Tons/Year

Deskripsi Produk

Kabel pemanas campuran Chromium resistan 6ium/Strip/Pita (ni80cr20/ni70cr30/ni60cr15/ni35cr20/ni20cr25/ni3020)

1.jalur kabel FeCrAl termasuk:  
OC13Al4,OC19Al3,OC21Al4,OCr20Al5,OC25Al5,OCr21Al6,OC21Al6Nb,OC27Al7Mo2.
2.Nikel Wire Strip Bar mencakup: Kr25Ni20 ,Cr20Ni35,Cr15Ni60,Cr20Ni80.
3.Strip Kabel Nikel tembaga mencakup:
CuNi1,CuBNi2,Cua5,CuNik8,Cuis10,KiNi14,Cu19,CuNik23,Cuis30,CuBN34,B944.
4.Kabel antan mencakup: 6J40,4J42,4J32.
5.Kabel Manganin:6J8,6J12,6J13.

Kondisi Permukaan yang Keterkiriman:
 
Tempat yang disamai oleh cuaca yang baik
Teroksidasi
Jeruk
Isolasi Enambed / PVC
 

Performa Nomenklatur Campuran		C20Ni80	C30Ni70	Cr15Ni60	Cr20Ni35	C20Ni30
Bahan kimia Utama	NI	Rest	Rest	55.0-61.0	34.0-37.0	30.0-34.0
	CR	20.0-23.0	28.0-31.0	15.0-18.0	18.0-21.0	18.0-21.0
	FE	≤1.0	≤1.0	Rest	Rest	Rest
Suhu layanan kontinu maks. Elemen()		1200	1250	1150	1100	1100
Jenis pemasangan di 20 μΩ (·)		1.09	1.18	1.12	1.0	1.04
Kerapatan(g/cm3)		8.40	8.10	8.20	7.90	7.90
Konduktivitas termal (KJ/·m h·)		60.3	45.2	45.2	43.8	43.8
Koefisien perluasan garis (α 10-6/celcigs)		18.0	17.0	17.0	19.0	19.0
Titik peleburan sekitar ()		1400	1380	1390	1390	1390
Naskh (Nonh) pada penahan(%)		>20	>20	>20	>20	>20
Struktur Mikrografis		austenite	austenite	austenite	austenite	austenite
Sifat magnetik		tidak magnetik	tidak magnetik	Magnet lemah	Magnet lemah	Magnet lemah

Properti utama  
 

Material campuran	Komposisi kimia %
	C	P	S	MN	Si	CR	NI	Al	FE
	max(≤)
1R13Al4	0.12	0.025	0.025	0.7	≤1.00	12.5-15.0	----	3.5-4.5	Rest
0C15Al5	0.12	0.025	0.025	0.7	≤1.00	14.5-15.5	----	4.5-5.3	Rest
0C25Al5	0.06	0.025	0.025	0.7	≤0.60	23.0-26.0	≤0.60	4.5-6.5	Rest
0C23Al5	0.06	0.025	0.025	0.7	≤0.60	20.5-23.5	≤0.60	4.2-5.3	Rest
0C21Al6	0.06	0.025	0.025	0.7	≤1.00	19.0-22.0	≤0.60	5.0-7.0	Rest
0C21Al4	0.06	0.025	0.025	0.7	≤1.00	21.0-23.0	≤0.60	3.0-5.2	Rest
0C21Al6Nb	0.05	0.025	0.025	0.7	≤0.60	21.0-23.0	≤0.60	5.0-7.0	Rest
0Cr27Al7Mo2	0.05	0.025	0.025	0.7	≤0.40	26.5-27.8	≤0.60	6.0-7.0	Rest

 Keuntungan utama dan aplikasinya
  Penggunaannya secara luas di    bidang surtur dan sulfida  serta menghasilkan   elektrik industri  
tungku,   alat listrik rumah tangga , dan    perangkat sinar inframerah jauh.