Aplikasi: | Penerbangan, Elektronik, Industri, Medis |
---|---|
Standar: | JIS, GB, DIN, BS, ASTM, AISI |
Kemurnian: | >98% |
Alloy: | Alloy |
Tipe: | Jalur nikel |
Bubuk: | Bukan bubuk |
Pemasok dengan izin usaha terverifikasi
Performa Nomenklatur Campuran | C20Ni80 | C30Ni70 | Cr15Ni60 | Cr20Ni35 | C20Ni30 | |
Bahan kimia Utama | NI | Rest | Rest | 55.0-61.0 | 34.0-37.0 | 30.0-34.0 |
CR | 20.0-23.0 | 28.0-31.0 | 15.0-18.0 | 18.0-21.0 | 18.0-21.0 | |
FE | ≤1.0 | ≤1.0 | Rest | Rest | Rest | |
Suhu layanan kontinu maks. Elemen() | 1200 | 1250 | 1150 | 1100 | 1100 | |
Jenis pemasangan di 20 μΩ (·) | 1.09 | 1.18 | 1.12 | 1.0 | 1.04 | |
Kerapatan(g/cm3) | 8.40 | 8.10 | 8.20 | 7.90 | 7.90 | |
Konduktivitas termal (KJ/·m h·) | 60.3 | 45.2 | 45.2 | 43.8 | 43.8 | |
Koefisien perluasan garis (α 10-6/celcigs) | 18.0 | 17.0 | 17.0 | 19.0 | 19.0 | |
Titik peleburan sekitar () | 1400 | 1380 | 1390 | 1390 | 1390 | |
Naskh (Nonh) pada penahan(%) | >20 | >20 | >20 | >20 | >20 | |
Struktur Mikrografis | austenite | austenite | austenite | austenite | austenite | |
Sifat magnetik | tidak magnetik | tidak magnetik | Magnet lemah | Magnet lemah | Magnet lemah |
Material campuran | Komposisi kimia % | ||||||||
C | P | S | MN | Si | CR | NI | Al | FE | |
max(≤) | |||||||||
1R13Al4 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 12.5-15.0 | ---- | 3.5-4.5 | Rest |
0C15Al5 | 0.12 | 0.025 | 0.025 | 0.7 | ≤1.00 | 14.5-15.5 | ---- | 4.5-5.3 | Rest |
0C25Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 23.0-26.0 | ≤0.60 | 4.5-6.5 | Rest |
0C23Al5 | 0.06 | 0.025 | 0.025 | 0.7 | ≤0.60 | 20.5-23.5 | ≤0.60 | 4.2-5.3 | Rest |
0C21Al6 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 19.0-22.0 | ≤0.60 | 5.0-7.0 | Rest |
0C21Al4 | 0.06 | 0.025 | 0.025 | 0.7 | ≤1.00 | 21.0-23.0 | ≤0.60 | 3.0-5.2 | Rest |
0C21Al6Nb | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.60 | 21.0-23.0 | ≤0.60 | 5.0-7.0 | Rest |
0Cr27Al7Mo2 | 0.05 | 0.025 | 0.025 | 0.7 | ≤0.40 | 26.5-27.8 | ≤0.60 | 6.0-7.0 | Rest |
Pemasok dengan izin usaha terverifikasi