Type: | Stainless Steel Wire |
---|---|
Standard: | ASTM, AISI, GB, JIS, DIN |
Grade: | A1 |
Certification: | ISO, RoHS |
Shape: | Round |
Technique: | Cold Rolled |
Pemasok dengan izin usaha terverifikasi
Komposisi kimia dan Properti Utama Fe-Cr-Al Campuran tahan | ||||||||
Properti \ Grade |
1R13Al4 |
0C25Al5 |
0C21Al6 |
0C23Al5 |
0C21Al4 |
0C21Al6Nb |
0Cr27Al7Mo2 |
|
Komposisi kimia Utama (%) |
CR |
12.0-15.0 |
23.0-26.0 |
19.0-22.0 |
22.5-24.5 |
18.0-21.0 |
21.0-23.0 |
26.5-27.8 |
Al |
4.0-6.0 |
4.5-6.5 |
5.0-7.0 |
4.2-5.0 |
3.0-4.2 |
5.0-7.0 |
6.0-7.0 |
|
Re |
oportune |
oportune |
oportune |
oportune |
oportune |
oportune |
oportune |
|
FE |
BAL. |
BAL. |
BAL. |
BAL. |
BAL. |
BAL. |
BAL. |
|
Nb0,5 |
Mo1.8-2.2 |
|||||||
Suhu Servis Kontinu Maks(OC) |
950 |
1250 |
1250 |
1250 |
1100 |
1350 |
1400 |
|
Resivitivitasan 20oC (Ωmm2/m) |
1.25 ±0.08 |
1.42 ±0.06 |
1.42 ±0.07 |
1.35 ±0.07 |
1.23 ±0.07 |
1.45 ±0.07 |
1.53 ±0.07 |
|
Kerapatan(g/cm3) |
7.4 |
7.1 |
7.16 |
7.25 |
7.35 |
7.1 |
7.1 |
|
Konduktivitas Termal |
52.7 |
46.1 |
63.2 |
60.2 |
46.9 |
46.1 |
45.2 |
|
(KJ/m@h@OC) |
||||||||
Koefisien Ekspansi Termal (α ASCII 10-6/OC) |
15.4 |
16 |
14.7 |
15 |
13.5 |
16 |
16 |
|
Perkiraan Titik pelelehan( OC) |
1450 |
1500 |
1500 |
1500 |
1500 |
1510 |
1520 |
|
Kekuatan tensil(N/mm2) |
580-680 |
630-780 |
630-780 |
630-780 |
600-700 |
650-800 |
680-830 |
|
Naskh (penghapusan) (%) |
>16 |
>12 |
>12 |
>12 |
>12 |
>12 |
>10 |
|
Variasi bagian |
65-75 |
60-75 |
65-75 |
65-75 |
65-75 |
65-75 |
65-75 |
|
Laju penurunan (%) |
||||||||
Frekuensi Benali (berulang)(F/R) |
>5 |
>5 |
>5 |
>5 |
>5 |
>5 |
>5 |
|
Keras (F.H.) |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
200-260 |
|
Waktu Servis Kontinu |
tidak |
≥80/1300 |
≥80/1300 |
≥80/1300 |
≥80/1250 |
≥50/1350 |
≥50/1350 |
|
Struktur Mikrografis |
Ferit |
Ferit |
Ferit |
Ferit |
Ferit |
Ferit |
Ferit |
|
Sifat Magnet |
Magnetik |
Magnetik |
Magnetik |
Magnetik |
Magnetik |
Magnetik |
Magnetik |
Pemasok dengan izin usaha terverifikasi