Shape: | Round |
---|---|
Application: | Busbar |
Certification: | ISO9001, GB, EN |
Technique: | Hot Rolled |
Grade: | 6000 Series |
Temper: | T3 - T8 |
Pemasok dengan izin usaha terverifikasi
Aloi | Si | FE | CU | MN | Mg | CR | NI | ZN | TI | GA | V | Lainnya | Aluminium min. |
|
Masing-masing | Total | |||||||||||||
6082 | 0.7-1.3 | 0.5 | 0.1 | 0.4-1.0 | 0.6-1.2 | 0.25 | - | 0.2 | 0.1 | - | - | 0.05 | 0.15 | Sisa |
Melembuntukan* | Ketebalan e** |
Menghasilkan stres Rp0,2 (mpa) |
Kekuatan tensil RM (mpa) |
Naskh (Naskh) A[%] |
Naskh (Naskh) A50mm [%] |
Kekerasan ** HB |
T4 | e<=25 | 110 | 205 | 14 | 12 | 65 |
T5 | e<=5 | 230 | 270 | 8 | 6 | 80 |
T6 | E<=5 | 250 | 290 | 8 | 6 | 95 |
5<e<=25 | 260 | 310 | 10 | 8 | 95 |
Kerapatan [kg/m3] |
Rentang pelelehan [C] |
Kelistrikan Konduktivitas [MS/m] |
Termal Konduktivitas [W/m.K] |
Efisiensi bersama Ekspansi termal 10-6/k |
Modulus elastisitas [IPK] |
2700 | 585-650 | 24-32 | 170-220 | 23.4 | ≈70 |
Parameter | Aluminium | Tembaga |
Standar yang relevan | IEC 60105 ISO 209-1,2 |
IEC 60028 |
Properti Fisik Komposisi kimia Panas Khusus gm.cal/ºC gm/cm2 Titik Lekapan |
0.092 2.91 660 |
99% murni 0.220 8.89 1083 |
Sifat Mekanis Kekuatan tensil tinggi /mm2 Kekuatan pencukuran kgf/mm2 sempurna Elastis modulus /mm2 0.2% kekuatan tensil untuk tensil/ mm2 |
20.5/25 15 6,700 16.5/22 |
22-26 16-19 12000 60-80% dari kekuatan tensil |
Properti Kelistrikan Resistan khusus cm Konduktivitas Volume Konduktivitas % IACS Hemat lebar mm/m/ |
3.133 31.9 57 2.3*10-5 |
1.7241 58 100 1.73*10-5 |