Coating: | Uncoated |
---|---|
Application: | Lathe |
Structure: | Indexable Turning Tool |
Material: | Diamond |
Type: | Lathe Turning Tool |
keuntungan: | High Efficiency, Wear-Resistant |
Pemasok dengan izin usaha terverifikasi
Diamond (PCD) | Cubic Boron Carbide (CBN) |
Heat resistance/° | Heat resistance/° |
700-800 | 1400-1500 |
Compressive strength/MPa | Compressive strength/MPa |
600-1100 | 500-800 |
Fracture toughness/MPa*m*1/2 | Fracture toughness/MPa*m*1/2 |
9.0 | 9.0 |
Hardness | Hardness |
>8000HV | 3500~5000HV |
Thermal conductivity/(W/(m*k)) | Thermal conductivity/(W/(m*k)) |
700 | 200-300 |
Coefficient of thermal expansion | Coefficient of thermal expansion |
0.9~1.18 | 3.5~4.8 |
PCD: aluminum and aluminum alloys, copper and steel alloys, titanium, magnesium, zinc, lead and other non-ferrous metals, glass fiber, carbon fiber reinforced plastics and other non-metals | CBN: for brown metal with extremely stable chemical properties, both hardened steel (45-65HRC) bearing steel (60-60HRC) high-speed steel (>62HRC) tool steel (57-60HRC) chilled cast iron rough turning and finishing, high-temperature alloy thermal spray material containing more than 10% of Co carbide and other difficult-to-machine materials of high-speed cutting processing |
Aluminum and aluminum alloys | Ductile iron |
Cutting speed | Hardness |
200-3000 | HB240-300 |
Feed amount | Cutting speed |
0.05-0.5 | 200-400 |
Cutting depth | Feed amount |
0.05-1.0 | 0.1-0.4 |
Cutting depth | |
0.1-1.5 |
Pemasok dengan izin usaha terverifikasi