Type: | Steel Plate |
---|---|
Standard: | ASTM, AISI, GB, JIS, DIN, BS |
Certification: | ISO, RoHS, IBR |
Surface Treatment: | Blackface |
Technique: | Hot Rolled |
Application: | Mold & Dies, Ship Plate, Boiler Plate, Container Plate, Flange Plate |
Pemasok dengan izin usaha terverifikasi
C | Si | MN | NI | P | S | CR | MO | V | N | Jml | TI | Al | CU | CEV |
maks. 0.2 | maks. 0.6 | 1 - 1.7 | maks. 0.8 | maks. 0.03 | maks. 0.025 | maks. 0.3 | maks. 0.1 | maks. 0.2 | maks. 0.025 | maks. 0.05 | maks. 0.05 | maks. 0.02 | maks. 0.55 | maks. 0.55 |
C | Si | MN | NI | P | S | CR | MO | V | N | Jml | TI | Al | CU | CEV |
maks. 0.2 | maks. 0.6 | 1 - 1.7 | maks. 0.8 | maks. 0.03 | maks. 0.025 | maks. 0.3 | maks. 0.1 | maks. 0.2 | maks. 0.025 | maks. 0.05 | maks. 0.05 | maks. 0.02 | maks. 0.55 | maks. 0.52 |
C | Si | MN | NI | P | S | CR | MO | V | N | Jml | TI | Al | CU | CEV |
maks. 0.2 | maks. 0.6 | 1 - 1.7 | maks. 0.8 | maks. 0.025 | maks. 0.02 | maks. 0.3 | maks. 0.1 | maks. 0.2 | maks. 0.025 | maks. 0.05 | maks. 0.05 | maks. 0.02 | maks. 0.55 | maks. 0.52 |
C | Si | MN | NI | P | S | CR | MO | V | N | Jml | TI | Al | CU | CEV |
maks. 0.2 | maks. 0.6 | 1 - 1.7 | maks. 0.8 | maks. 0.025 | maks. 0.02 | maks. 0.3 | maks. 0.1 | maks. 0.2 | maks. 0.025 | maks. 0.05 | maks. 0.05 | maks. 0.02 | maks. 0.55 | maks. 0.55 |
Ketebalan nominal (mm): | hingga 100 | 100 - 200 |
RM - kekuatan tensil (MPa) | 540-720 | 530-710 |
Ketebalan nominal (mm): | hingga 16 | 16 - 40 | 40 - 63 | 63 - 80 | 80 - 100 | 100 - 150 | 150 - 200 |
H - kekuatan yield minimum (MPa) | 460 | 440 | 430 | 410 | 400 | 380 | 370 |
KV - energi benturan (J) longd (lebih lama), (+N) | +20 55 |
0 47 |
-37 10 43 |
-37 20 40 |
KV - Energi benturan (J) transversal, (+N) | +20 31 |
0 27 |
-37 10 24 |
-37 20 20 |
Ketebalan nominal (mm): | hingga 16 | 16 - 40 | 40 - 63 | 63 - 80 | 80 - 200 |
A - Min. Pemongangan Rendah = 5,65 √ hingga (%) | 17 | 17 | 17 | 17 | 17 |
Ketebalan nominal (mm): | hingga 100 | 100 - 200 | 200 - 250 |
RM - kekuatan tensil (MPa) | 520-680 | 500-650 | 500-650 |
Ketebalan nominal (mm): | hingga 16 | 16 - 40 | 40 - 63 | 63 - 80 | 80 - 100 | 100 - 150 | 150 - 200 | 200 - 250 |
H - kekuatan yield minimum (MPa) | 420 | 400 | 390 | 370 | 360 | 340 | 330 | 320 |
KV - energi benturan (J) longd (lebih lama), (+N) | +20 55 |
0 47 |
-37 10 43 |
-37 20 40 |
KV - Energi benturan (J) transversal, (+N) | +20 31 |
0 27 |
-37 10 24 |
-37 20 20 |
Ketebalan nominal (mm): | hingga 16 | 16 - 40 | 40 - 63 | 63 - 80 | 80 - 200 | 200 - 250 |
A - Min. Pemongangan Rendah = 5,65 √ hingga (%) | 19 | 19 | 19 | 18 | 18 | 18 |
Ketebalan nominal (mm): | hingga 100 | 100 - 200 | 200 - 250 |
RM - kekuatan tensil (MPa) | 520-680 | 500-650 | 500-650 |
Ketebalan nominal (mm): | hingga 16 | 16 - 40 | 40 - 63 | 63 - 80 | 80 - 100 | 100 - 150 | 150 - 200 | 200 - 250 |
H - kekuatan yield minimum (MPa) | 420 | 400 | 390 | 370 | 360 | 340 | 330 | 320 |
KV - energi benturan (J) longd (lebih lama), (+N) | +20 63 |
0 55 |
-37 10 51 |
-37 20 47 |
-37 30 40 |
-37 40 31 |
-37 50 27 |
KV - Energi benturan (J) transversal, (+N) | +20 40 |
0 34 |
-37 10 30 |
-37 20 27 |
-37 30 23 |
-37 40 20 |
-37 50 16 |
Ketebalan nominal (mm): | hingga 16 | 16 - 40 | 40 - 63 | 63 - 80 | 80 - 200 | 200 - 250 |
A - Min. Pemongangan Rendah = 5,65 √ hingga (%) | 19 | 19 | 19 | 18 | 18 | 18 |
Ketebalan nominal (mm): | hingga 100 | 100 - 200 |
RM - kekuatan tensil (MPa) | 540-720 | 530-710 |
Ketebalan nominal (mm): | hingga 16 | 16 - 40 | 40 - 63 | 63 - 80 | 80 - 100 | 100 - 150 | 150 - 200 |
H - kekuatan yield minimum (MPa) | 460 | 440 | 430 | 410 | 400 | 380 | 370 |
KV - energi benturan (J) longd (lebih lama), (+N) | +20 63 |
0 55 |
-37 10 51 |
-37 20 47 |
-37 30 40 |
-37 40 31 |
-37 50 27 |
KV - Energi benturan (J) transversal, (+N) | +20 40 |
0 34 |
-37 10 30 |
-37 20 27 |
-37 30 23 |
-37 40 20 |
-37 50 16 |
Ketebalan nominal (mm): | hingga 16 | 16 - 40 | 40 - 63 | 63 - 80 | 80 - 200 |
A - Min. Pemongangan Rendah = 5,65 √ hingga (%) | 17 | 17 | 17 | 17 | 17 |