Pendahuluan Umum coil Baja Rol panas:
Spesifikasi coil Karbon Steel:
Produk | Koil Baja Karbon/roll/Baja ringan/coil setrika MS/HRC |
material | A36, SS400, Q345B, Q235B, GRADUASI, Q460,St37-2,SA283Gr, S35JR, S235J0, S2J2 |
Standar | ASTM EN DIN ISO JIS BA ANSI |
Teknologi | hot rolled old rolled (sesuai permintaan khusus) |
Ketebalan | 1.0-50mm (atau sesuai permintaan kustom) |
Lebar | 785-2000MM |
Perlakuan Permukaan | Cat hitam, berlapis PE, galvanisasi, warna berlapis, lapisan anti karat tergulung, diiap dengan karat, kotak cek, dsb |
Metode Pemrosesan | Tekukan, pengelasan, Pengalinan, Pengpotong, Pengpotong, Layanan pembantu atau atas permintaan pelanggan |
Waktu pengiriman | dalam 7-15 hari kerja |
Aplikasi | Digunakan secara luas dalam aplikasi suhu tinggi, perangkat medis, bahan bangunan, kimia, industri makanan, pertanian, komponen kapal. Juga berlaku untuk makanan, kemasan minuman, perlengkapan dapur, kereta api, pesawat, sabuk konveyor, kendaraan, baut, mur, pegas, dan kasa. |
Tipe
|
Kelas
|
Standar
|
Baja Struktual Karbon Umum
|
Q195,Q215A,Q215B,Q235A,Q235B,Q235C,Q235D
|
GB
|
SS330,SS440,SS490
|
JIS
|
|
DC01,DD11,DD12,DD13,DX51,S185,S235,S275,S355,E295
|
ID
|
|
SAE1006,SAE1008,SAE1010,SAE1012,SAE1017,SAE1022
|
ASTM
|
|
Gambar gulungan Kualitas Konstrukional
|
08AI,10,20,30,35,45
|
GB
|
C35,C40,C45,C50,C60
|
ID
|
|
SAE1006,SAE1008,SAE1010,SAE1012,SAE1017,SAE1022
|
ASTM
|
|
Bangunan
Struktur Baja
|
08,15,Q215,Q275A,Q390A.
|
GB
|
SN400A,SN400B,SN490B
|
JIS
|
|
Baja Struktur pengelasan
|
Q235,Q345,Q390,Q420,Q460
|
GB
|
SM400,SM490,SM520,SM570
|
ID
|
|
Pipa Baja
|
Q235,Q245
|
GB
|
SPHT1,SPHT2,SPHT3,SPHT4
|
JIS
|
Merek
|
C(Wt%)
|
Si (Wt%)
|
MN (Wt%)
|
P(Wt%)
|
S(Wt%)
|
CU(Wt%)
|
ALS (Wt%)
|
P195
|
≤0.12
|
≤0.30
|
≤0.50
|
≤0.035
|
≤0.040
|
≤0.30
|
/
|
Q215A
|
≤0.15
|
≤0.35
|
≤0.12
|
≤0.045
|
≤0.050
|
≤0.30
|
/
|
Q215B
|
≤0.15
|
≤0.35
|
≤0.12
|
≤0.045
|
≤0.045
|
≤0.30
|
/
|
Q235A
|
≤0.22
|
≤0.35
|
≤0.14
|
≤0.045
|
≤0.050
|
≤0.30
|
/
|
Q235B
|
≤0.20
|
≤0.35
|
≤0.14
|
≤0.045
|
≤0.045
|
≤0.30
|
/
|
Q235C
|
≤0.17
|
≤0.35
|
≤0.14
|
≤0.040
|
≤0.040
|
≤0.30
|
/
|
Q235D
|
≤0.17
|
≤0.35
|
≤0.14
|
≤0.035
|
≤0.035
|
≤0.30
|
≥0.015
|
SS330
|
/
|
/
|
/
|
≤0.050
|
≤0.050
|
/
|
/
|
SS400
|
/
|
/
|
/
|
≤0.050
|
≤0.050
|
/
|
/
|
S235JR
|
≤0.17
|
/
|
≤0.14
|
≤0.035
|
≤0.035
|
≤0.55
|
≥0.015
|
S235J0
|
≤0.17
|
/
|
≤0.14
|
≤0.030
|
≤0.030
|
≤0.55
|
≥0.015
|
S275JR
|
≤0.21
|
/
|
≤0.15
|
≤0.035
|
≤0.035
|
≤0.55
|
≥0.015
|
S275J0
|
≤0.18
|
/
|
≤0.15
|
≤0.030
|
≤0.030
|
≤0.55
|
≥0.015
|
SPHC
|
≤0.15
|
/
|
≤0.60
|
≤0.050
|
≤0.050
|
/
|
/
|
SPHD
|
≤0.10
|
/
|
≤0.50
|
≤0.040
|
≤0.040
|
/
|
/
|
|
≤0.10
|
/
|
≤0.50
|
≤0.030
|
≤0.035
|
/
|
/
|
DD11
|
≤0.12
|
/
|
≤0.60
|
≤0.045
|
≤0.045
|
/
|
/
|
DD12
|
≤0.10
|
/
|
≤0.45
|
≤0.035
|
≤0.035
|
/
|
/
|
DD13
|
≤0.08
|
/
|
≤0.40
|
≤0.030
|
≤0.030
|
/
|
/
|
HCP
|
≤0.012
|
/
|
≤0.20-0.40
|
≤0.030
|
≤0.002
|
≤0.05
|
≥0.015
|
Merek
|
Kekuatan yield Rel, MPa
|
RM kekuatan tensil, MPa
|
Naskh, %
|
Uji dampak
(Longitudinal)
|
|||
Ketebalan, mm
|
KV2, J
|
||||||
≤16
|
>16-25.4
|
20 DERAJAT CELCIUS
|
0 DERAJAT CELCIUS
|
-20
|
|||
P195
|
≥195
|
≥185
|
315-430
|
≥33
|
|
|
|
Q215A
|
≥215
|
≥205
|
335-450
|
≥31
|
|
|
|
Q215B
|
≥215
|
≥205
|
335-450
|
≥31
|
≥27
|
|
|
Q235A
|
≥235
|
≥225
|
370-500
|
≥26
|
|
|
|
Q235B
|
≥235
|
≥225
|
370-500
|
≥26
|
≥27
|
|
|
Q235C
|
≥235
|
≥225
|
370-500
|
≥26
|
|
≥27
|
|
Q235D
|
≥235
|
≥225
|
370-500
|
≥26
|
|
|
≥27
|
Merek
|
Kekuatan yield Rel, MPa
|
Naskh, %
|
|||||
Ketebalan, mm
|
|||||||
1.2-1.6
|
1.6-2.0
|
2.0-2.5
|
2.5-3.2
|
3.2-4.0
|
≥4.0
|
||
SPHC
|
≥270
|
≥27
|
≥29
|
≥29
|
≥29
|
≥31
|
≥31
|
SPHD
|
≥270
|
≥30
|
≥32
|
≥33
|
≥35
|
≥37
|
≥39
|
|
≥270
|
≥31
|
≥33
|
≥35
|
≥37
|
≥39
|
≥41
|
Merek
|
Kekuatan yield Rel, MPa
|
RM kekuatan tensil, MPa
|
Naskh, %
|
|||
Ketebalan, mm
|
Ketebalan, mm
|
|||||
≤16
|
>16-25.4
|
≤5
|
5-16
|
>16
|
||
SS330
|
≥205
|
≥195
|
330-430
|
≥26
|
≥21
|
≥26
|
SS400
|
≥245
|
≥235
|
400-510
|
≥21
|
≥17
|
≥21
|
Merek
|
Kekuatan yield Rel, MPa
|
RM kekuatan tensil, MPa
|
Naskh, %
|
|||||
Ketebalan, mm
|
Ketebalan, mm
|
A80mm
|
A
|
|||||
≤16
|
>16-25.4
|
<3
|
≥3-25
|
1.5-2
|
2-2.5
|
2.5-3
|
3-25.4
|
|
S235JR
|
≥235
|
≥225
|
360-510
|
360-510
|
≥19
|
≥20
|
≥21
|
≥26
|
S235J0
|
≥235
|
≥225
|
360-510
|
360-510
|
≥17
|
≥18
|
≥19
|
≥24
|
S275JR
|
≥275
|
≥265
|
430-580
|
430-560
|
≥17
|
≥18
|
≥19
|
≥23
|
S275J0
|
≥275
|
≥265
|
430-580
|
430-560
|
≥15
|
≥16
|
≥17
|
≥21
|
Merek
|
Kekuatan yield Rel, MPa
|
RM kekuatan tensil, MPa
|
Naskh, %
|
|||
Ketebalan, mm
|
A80mm
|
A
|
||||
1.5-2
|
2-8
|
1.5-2
|
2-3
|
3-8
|
||
DD11
|
170-360
|
170-340
|
≤440
|
≥23
|
≥24
|
≥28
|
DD12
|
170-340
|
170-320
|
≤420
|
≥25
|
≥26
|
≥30
|
DD13
|
170-330
|
170-310
|
≤400
|
≥28
|
≥29
|
≥33
|
Merek
|
Status koil baja
|
Kekuatan yield Rel, MPa
|
RM kekuatan tensil, MPa
|
Naskh, %
|
HCP
|
Coil asli
|
190-280
|
290-350
|
≥38
|
Coil sampul-pass
|
190-280
|
290-340
|
≥38
|
Proses Baja ringan:
Aplikasi Karbon Baja HRC:
Produk rol panas memiliki sifat luar biasa seperti kekuatan tinggi, kekerasan baik, pemrosesan mudah dan kemampuan las yang baik, sehingga digunakan secara luas di industri manufaktur seperti baja, konstruksi, mesin, boiler, dan kapal tekanan, dll.Paket Karbon Steel HRC&Pengiriman:
Bagaimana saya bisa mengambil contoh sebelum memesan?
J:Ya, tentu saja. Biasanya sampel kami gratis, kami dapat memproduksi gambar atau gambar teknis Anda.Pemasok dengan izin usaha terverifikasi