After-sales Service: | 24 Hours on Line |
---|---|
Warranty: | Three Years |
Tipe: | Batang Baja Campuran |
Standar: | AISI, ASTM, GB, JIS, DIN, BS |
Teknik: | Tempa |
Aplikasi: | Batang Baja struktural, Alat Steel Bar, Die Steel Bar |
Pemasok dengan izin usaha terverifikasi
Negara | Jepang | Jerman | Inggris | AS |
Standar | JIS G4103 | EN10250 | ASTM A29 | |
Kelas | 36CronMo4/1.6511 | EN24/817M40 | 4340 |
Kelas | C | Si | MN | P | S | CR | MO | NI |
4340 | 0.38-0.43 | 0.15-0.35 | 0.6-0.8 | 0.035 | 0.04 | 0.7-09 | 0.2-0.3 | 1.65-2.0 |
36CronMo4 | 0.32-0.4 | 0.4 | 0.5-0.8 | 0.035 | 0.035 | 0.9-1.2 | 0.15-0.3 | 0.90-1.20 |
EN24 | 0.36-0.44 | 0.1-0.4 | 0.45-0.7 | 0.035 | 0.04 | 1.0-1.4 | 0.2-0.35 | 1.3-1.7 |
0.36-0.43 | 0.15-0.35 | 0.6-0.9 | 0.03 | 0.03 | 0.6-1.0 | 0.15-0.3 | 1.6-2.0 |
Sifat mekanis terutama mencakup kekuatan tensil, kekuatan yield, pemanjangan, area atau reduksi, kekerasan, Nilai dampak, inklusi tidak logam dll. perlakuan panas berbeda, sifat mekanis akan berbeda, seperti Normalized, diperkeras, QT. Jika Anda ingin mengetahui properti-sifat tersebut, silakan hubungi salesman.
5: pandangan atas baja 4340
Ukuran | Bundar | Dia 6-1200 mm |
Pelat/datar/Blok | Ketebalan 6mm-500mm |
|
Lebar 20 mm-1000mm |
||
Perlakuan panas | Dinormalkan ; Anneap ; mengalami quefed ; Tempered | |
Kondisi permukaan | Hitam; dikupas; dibuat dari mesin; ditentukan oleh: Berputar; dikikis | |
Kondisi pengiriman | Ditempa; rol panas; ditarik dingin | |
Uji | Kekuatan tensil, kekuatan yield, pemanjangan, area reduksi, nilai benturan, Kekerasan, ukuran biji, tes ultrasonik, inspeksi di AS, tes partikel magnetik, dll.. | |
Ketentuan pembayaran | T/T;L/C;/gram uang/ Paypal | |
Ketentuan perdagangan | FOB; CIF; C&F; DLL.. | |
Waktu pengiriman | 30-45 hari | |
Aplikasi | baja campuran 4340 digunakan untuk roda gigi pendaratan pesawat, otomotif, pengeboran minyak dan gas, pembentukan hangat dan dingin, pembangunan alat berat, sistem transfer seperti roda gigi dan poros transmisi daya, industri rekayasa umum, dan penggunaan struktural seperti poros tugas berat, roda-gigi, gandar, spindel, kopling sambungan, pin, chipcks, mols, dan seterusnya. |
6. Perlakuan panas
Pelepasan Tegangan Baja campuran 4340 yang diperkeras dan diperkeras juga dapat diperkeras, memberikan kekerasan permukaan hingga RC 60. Panas hingga 500 o C - 530 o C dan tahan lama (dari 10 sampai 60 jam) untuk mengembangkan kedalaman ruang. NitRiding seharusnya diikuti dengan pendinginan lambat (No pemadaman) yang mengurangi masalah distorsi. Oleh karena itu, material kelas nitried 4340 bisa diproses mesin hingga mendekati ukuran akhir, yang hanya menyisakan alat untuk menggiling kecil. Kekuatan tensil 4340 inti material baja biasanya tidak terpengaruh karena kisaran temperatur nitrat biasanya berada di bawah temperatur tempering awal yang digunakan.
Kekerasan Permukaan yang bisa dicapai adalah 600 hingga 650HV.
GB GB/T 1299 |
JIS JIS G4404 |
DIN (W-NR) DIN EN ISO4957 |
AISI/ASTM ASTM A681 |
BS BS 4659 |
Baja Work Tool dingin | ||||
1.2080/X210C12 | D3 | |||
C5M1V | SKD12 | 1.2363/X100CMoV5 | A2/T30102 | BA2 |
C12MV | 1.2601 | D5 | ||
Cr12M1V1 | SKD11 | 1.2379/X153Crm12 | D2 | |
X210CW12 | SKD2 | 1.2436 | D6 | |
9Crawn | SKS3 | 1.2510/100MnCrW4 | O1 | |
9Mn2V | 1.2842 / 90MnCrV8 | O2 | B02 | |
5Crsen Mo | SKT4 | 1.2713 | L6/T61206 | BH224/5 |
Baja Work Tool panas | ||||
1.2355/50CrMoV13-15 | S7/T41907 | |||
5CrNiMV | 1.2714 | 6F3 | ||
5Crsen Ni4Mo | 1.2767 | 6F7 | ||
SKD7 | 1.2365/32CrMoV12-28 | H10/T20810 | BH10 | |
4Crac5MoV | SKD6 | 1.2343/X37CMoV5-1 | H11/T20811 | BH11 |
4Crac5 MoSiV1 | SKD61 | 1.2344/X40CMoV5-1 | H13 | |
SKD62 | 1.2605/X35CWMoV5 | H12/T20812 | BH12 | |
3Cr2W8V | SKD5 | 1.2581 | H21 | |
Baja mold plastik | ||||
3Cr2Mo | 1.2311 | P20 | ||
NAK80 | 1.2312 | P20+S / P21 | ||
3Cr2MnNiMong | 1.2738 | P20+Ni / 718 | ||
4C13 | SUS420J2 | 1.2083 | 415 | |
3C17+S | SUS420F | 1.2085 | ||
3Cr17Mo | SUS420J | 1.2316 | ||
Baja Teknik | ||||
GB GB/T 699 |
JIS JIS G4051 |
DIN (W-NR) EN 10083-2 |
AISI/ASTM ASTM A20 |
EN / BS |
1018 | EN2C | |||
20 | S20C | C20/1.1151 | 1020 | EN3B /070M20 |
S35C | C35 | 1035 | ||
1040 | EN8/080M40 | |||
45 | S45C | C45/1.1191 | 1045 | EN8D/C45E |
50 | S50C | 1050 | ||
S55C | 1055 | EN9/070M55 | ||
Q345 | S355/ST52-3/1.1170 | EN14/150M19 | ||
GB GB/T 3077 |
JIS JIS G4105/JIS G4103 |
DIN (W-NR) EN 10250 |
AISI/ASTM ASTM A29 |
BS BS 970 |
40Cr | SCr440 | 41CR4(1.7035) | 5140 | |
SCM420 | 18CMo4/1.7243 | 4118 | ||
30CrMo | SCM430 | 25CrMo4/1.7218 | 4130 | 708A25/708M25 |
42CrMo | SCM440 | 42cr4/1.7225 | 4140 | EN19/709M40 |
4145 | ||||
4330 | ||||
40CronNikMA | SNCM 439/SNCM8 | 36CronMo4/1.6511 | 4340 | EN24/817M40 |
40NiMCris10-5/1.6745 | EN26 | |||
34CronMo6 / 1.6582 | 4337 | |||
30Cronmo16-6/1.6747 | EN30B/835M30 | |||
32CrMo12/1.7361 | EN40B/722M24 | |||
SCM415 | 16MnCr5 / 1.7131 | 5115 | ||
15Krtidak 6/1.5919 | 3115 | |||
16NiC4/1.5714 | EN351/635M15 | |||
4615/4617 | EN34/665M17 | |||
14tiada 1.5752 | 3310/3415 | EN36/655M13 | ||
15Kritmo16-5/1.6723 | EN39/835M15 | |||
18Cran787-6 (1.6587) | 4815 | |||
SNCM220 | 1.6523/21NiCMo2 | 8620 | 805M20 | |
20CronNiM5 | EN353 | |||
GCr15 | 52100/1.3505 | EN31/535A99 | ||
Baja Antikarat | ||||
SUS440C | X105CMo17/1.4125 | S44004/440C | ||
Keausan-menolak Baja | ||||
GB | JIS | DIN (W-NR) | AISI/ASTM | SSAB |
HB400 | HARDOX400 | |||
NHOTEL | HB500 | HARDOX400 | ||
Baja pegas | ||||
GB | JIS | DIN (W-NR) | AISI/ASTM | SSAB |
65MN | 1066 | |||
60Si2Mn | SUP6 | 60Si7 | 9260 | |
60Si2MnA | SUP7 | 60Si7 | 9260 | |
55CCraMA | SUP9 | 55C3 | 5155 | |
60CnA | SUP9A | 5160 | ||
50CVA | SUP10 | 51CrV4 | 6150 | |
Baja Kecepatan Tinggi | ||||
GB | JIS JIS G4403 |
DIN (W-NR) DIN EN ISO 4957 |
AISI/ASTM ASTM A600 |
BS BS 4659 |
SKH51 | 1.3343 | M2 | ||
SKH55 | 1.3243/HS6-5-2-5 | M35 | ||
SKH59 | 1.3247/HS2-9-1-8 | M42 | ||
SKH2 | HS18-0-1/1.3355 | T1 | ||
SKH3 | S 18-1-2-5/1.3255 | T4/T12004 | ||
SKH4 | 1.3265/S18-1-2-10 | T5/T12005 | BT5 | |
Semua jenis komponen penempaan sesuai Gambar |
Ukuran | Bundar | Dia 8-1200 mm |
Pelat/datar/Blok | Ketebalan 10 mm-800mm |
|
Lebar 20 mm-2000mm |
||
Perlakuan panas | Dinormalkan ; Anneap ; mengalami quefed ; Tempered | |
Kondisi permukaan | Hitam; dikupas; dibuat dari mesin; ditentukan oleh: Berputar; dikikis | |
Kondisi pengiriman | Ditempa; rol panas; ditarik dingin | |
Uji | Kekuatan tensil, kekuatan yield, pemanjangan, area reduksi, nilai benturan, Kekerasan, ukuran biji, tes ultrasonik, inspeksi di AS, tes partikel magnetik, dll.. | |
Ketentuan pembayaran | T/T;L/C;/gram uang/ Paypal | |
Ketentuan perdagangan | FOB; CIF; C&F; DLL.. | |
Waktu pengiriman | 30-45 hari |